A system and method for efficiently chlorinating vanadium from vanadium slag

A vanadium slag, high-efficiency technology, applied in vanadium oxide, improvement of process efficiency, etc., can solve the problems of reduced chlorination selectivity and efficiency, fluctuation of chlorination temperature, difficulty in comprehensive utilization of extracted tailings, etc.

Active Publication Date: 2017-10-03
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF11 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the industry, the extraction of vanadium in vanadium slag is mainly achieved through the preparation of vanadium oxide products through sodium roasting-leaching-precipitation-calcination-decomposition, and there are the following outstanding problems: (1) lengthy process, high energy consumption, and high production costs; (2) ) The vanadium recovery rate is low, and the recovery rate from vanadium slag to vanadium oxide products is less than 80%; (3) Environmental problems are prominent, and the introduction of a large amount of sodium in the sodium roasting process makes the comprehensive utilization of extraction tailings difficult, and the leaching-precipitation process produces a large amount of Ammonia nitrogen wastewater containing a variety of harmful metal ions and sodium sulfate has a serious impact on the ecological environment
[0005] The main outstanding problems in the existing chlorination vanadium extraction technology include: (1) The chlorination and roasting of vanadium slag is a strong exothermic process, and the heat generated by the chlorination reaction needs to be passed through The chlorination temperature can only be stabilized by removing the heat from the furnace wall, so solids and gases usually enter the reactor at near room temperature, and can only participate in the reaction after being preheated by the heat generated by the chlorination reaction, which makes the local reaction efficiency of the chlorination reactor too low (2) Due to the need to remove the heat produced by the chlorination reaction through a large amount of heat dissipation to maintain the operating temperature, the operating conditions and environmental climate changes are likely to cause fluctuations in the chlorination temperature, resulting in a reduction in the selectivity and efficiency of chlorination. Reasonable heat needs to be used Balanced supply and temperature control methods; (3) For the chlorine-containing tailings produced by chlorination and roasting of vanadium slag and the impurity chlorides produced by the separation and removal of chlorides, effective comprehensive treatment methods cannot be provided, which can easily cause environmental pollution; ( 4) The preparation of industrial vanadium products vanadium pentoxide by vanadium chloride (vanadium oxychloride) lacks an efficient and clean technical route. Because vanadium has a high solubility in hydrochloric acid solution, direct hydrolysis will cause the recovery rate of vanadium to be too low. Although the use of ammonium salt precipitation can increase the precipitation rate of vanadium, it will produce a large amount of ammonia nitrogen wastewater, and the environmental problems are prominent; etc.
These problems are all important reasons why the existing vanadium slag chlorination vanadium extraction process cannot be applied on a large scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A system and method for efficiently chlorinating vanadium from vanadium slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0063] In order to make the purpose, technical solutions and advantages of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are the Some, but not all, embodiments of the invention. It should be noted that the examples are only used to illustrate the technical solution of the present invention, not to limit it. figure 1 It is a system and method schematic diagram of a vanadium slag high-efficiency chlorination vanadium extraction system of the present invention.

[0064] combine figure 1 , a kind of vanadium slag high-efficiency chlorination vanadium extracting system used in the present embodiment comprises a chlorination bed feeding device 1, a chlorination fluidized bed 2, a distillation device 3, a hydrolysis fluidized bed 4, an oxidation bed feeding d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

Provided are a system and method for highly effective chlorination and vanadium extraction from vanadium slag. By means of heat exchange between a chlorination gas and a chlorination flue gas, a chlorination gas is preheated and an appropriate amount of air is added, which causes coke powder to partially combust, thus providing a balanced supply of heat during the process of chlorination; also, by means of high-temperature fluidization oxidation of the chlorinated slag, the chlorinated slag is used in a comprehensive manner, and the chlorine gas is recycled; further, by means of vapor-phase hydrolysis of the vanadium oxytrichloride product of chlorination, a powdered divanadium pentoxide product is obtained; the reaction efficiency of chlorination is improved, the consumption of chlorine gas is reduced, the harm of chlorinated slag is eliminated, and the pollution problem caused by conventional ammonium salt precipitation is prevented.

Description

technical field [0001] The invention belongs to the fields of chemical industry and metallurgy, and particularly relates to a system and method for efficiently chlorinating vanadium slag and extracting vanadium. Background technique [0002] Vanadium-titanium magnetite is an important symbiotic resource of vanadium, titanium and iron. Titanium is enriched in smelting slag by reduction smelting, vanadium is reduced to molten iron and then further blown to obtain V-containing 2 o 5 10wt%-28wt% vanadium slag, so that the separation and utilization of vanadium, titanium and iron resources in minerals can be effectively realized. At present, in the industry, the extraction of vanadium in vanadium slag is mainly achieved through the preparation of vanadium oxide products through sodium roasting-leaching-precipitation-calcination-decomposition, and there are the following outstanding problems: (1) lengthy process, high energy consumption, and high production costs; (2) ) The van...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/04C22B34/22
CPCC01G31/02C22B7/04C22B34/22Y02P10/20
Inventor 范川林朱庆山杨海涛
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products