Method for preparing hollow UO2 nanospheres by ammonium uranyl carbonate solution irradiation

A technology of ammonium uranyl tricarbonate and nanospheres, which is applied in the field of preparation of uranium oxide materials

Inactive Publication Date: 2016-10-26
PEKING UNIV
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there has been no report on hollow nanostructures of uranium oxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing hollow UO2 nanospheres by ammonium uranyl carbonate solution irradiation
  • Method for preparing hollow UO2 nanospheres by ammonium uranyl carbonate solution irradiation
  • Method for preparing hollow UO2 nanospheres by ammonium uranyl carbonate solution irradiation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention is further elaborated below by embodiment, but does not limit the scope of the present invention in any way.

[0034] 1. Experimental reagents:

[0035] UO 2 (NO 3 ) 2 ·6H 2 O, GR, Chemapol, Prague Czechoslovakia;

[0036] NH 4 HCO 3 、Na 2 CO 3 , ammonium formate (HCOONH 4 ) are analytically pure, directly used;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing hollow UO2 nanospheres by ammonium uranyl carbonate solution irradiation. The method includes: preparing low-concentration UO2(CO3)3<4-> alkaline solution containing a free radical removing agent; adopting electron beam or gamma-ray irradiation to obtain the hollow UO2 nanospheres, different in diameter, wall thickness and cavity diameter, formed by self assembly of nanoparticles through control of conditions such as absorbed dose and dose rate. A uranium oxide hollow nanostructure which is prepared for the first time is conducive to researches of application of uranium oxide nanoparticles to fields of nuclear fuel, catalysis and the like.

Description

technical field [0001] The invention relates to a preparation technology of uranium oxide materials, in particular to a preparation method of a hollow nanostructure of uranium oxide. Background technique [0002] Uranium oxides, such as UO 2 , U 3 o 8 , UO 3 , is not only an important nuclear fuel, but also a class of effective catalysts. In the past ten years, studies have shown that nanoscale uranium oxide has a very low sintering temperature and good catalytic activity. Therefore, the synthesis of uranium oxide nanomaterials with specific size and morphology has attracted extensive attention. Currently, like quasi-spherical UO 2 Nanoparticles, U 3 o 8 Nanoflower, U 3 o 8 Nanorods, U 3 o 8 Nanotubes / wires and other uranium oxide micro / nanomaterials with complex structures have been prepared by thermochemical and electrochemical methods. In addition, the irradiation method has the characteristics of mild conditions and no introduction of impurities, and has bee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G43/025B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00C01G43/025C01P2002/72C01P2004/04C01P2004/34C01P2004/64
Inventor 陈庆德沈兴海王永明
Owner PEKING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com