A kind of nickel-brass tape and preparation method thereof

A technology of nickel brass and copper strip, applied in the field of nickel brass strip and its preparation, can solve the problems of development requirements, nickel brass alloy corrosion resistance and wear resistance, etc., to improve internal quality and cold working performance Effects that are easy to implement and inexpensive to produce

Active Publication Date: 2017-07-28
中色正锐(山东)铜业有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous expansion of the application range of copper alloy products, higher and higher performance requirements are put forward for the performance of copper alloy strips. The corrosion resistance and wear resistance of the general-purpose nickel-brass alloys are increasingly unable to meet the material applications. development requirements, and most of them are produced by horizontal continuous casting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The present invention also provides a method for preparing the nickel-brass strip described in any one of the above, comprising the following steps:

[0024] 1) Melting and casting: medium frequency induction furnace is used for semi-continuous casting, phosphor copper alloy is used for deoxidation and degassing, casting is covered with dry borax, the melting temperature is 1200℃~1250℃, and the casting temperature is 1100℃~1130℃;

[0025] A slab is obtained, and the slab includes the following components in weight percentage: 67% to 73% of Cu, 2% to 4.5% of Ni, 0.003% to 0.015% of P, Pb≤0.01, Fe≤0.012%, and the remainder The amount is Zn and unavoidable impurities;

[0026] 2) Hot rolling: heat the slab obtained in step 1) at 800°C to 890°C, the holding time is 1h to 5h, hot rolling is water cooled, the final rolling temperature is 350°C to 550°C, and the total deformation is 80% to 96%, get 14mm ~ 20mm slab;

[0027] 3) Face milling: the slab obtained after step 2) i...

Embodiment 1

[0036] Nickel brass specification: 2.0×205mm thickness tolerance ±0.02mm as an example, including the following steps:

[0037] 1) Melting and casting: medium-frequency induction furnace is used for semi-continuous casting, copper and nickel are added to melt, then zinc is added, and phosphor-copper intermediate alloy is added after covering and slag removal, and the composition is fine-tuned; phosphor-copper alloy is used for deoxidation and degassing, and casting is covered with dry borax , the melting temperature is 1200°C, and the casting temperature is 1130°C; the slab specification is 210×400×6000mm; the slab is obtained, and the slab includes the following components by weight percentage: 67% Cu, 4.5% Ni , 0.003% P, Pb≤0.01, Fe≤0.012%, the balance is Zn and unavoidable impurities;

[0038] 2) Hot rolling: Heating the slab obtained in step 1) to 890°C in a walking furnace, holding time for 1h, hot rolling passes 210mm-180mm-145mm-102mm-70mm-48mm-35mm-26mm-20mm -16mm, ho...

Embodiment 2

[0045] Nickel brass specification: 0.4×205mm thickness tolerance ±0.01mm as an example, including the following steps:

[0046] 1) Melting and casting: medium-frequency induction furnace is used for semi-continuous casting, copper and nickel are added to melt, then zinc is added, and phosphor-copper intermediate alloy is added after covering and slag removal, and the composition is fine-tuned; phosphor-copper alloy is used for deoxidation and degassing, and casting is covered with dry borax , the melting temperature is 1230°C, and the casting temperature is 1120°C;

[0047] In the semi-continuous casting process, after forming the slab shell, the slab is led out of the crystallizer with the liquid melt contained in the slab, and then the slab containing the liquid melt is squeezed and deformed by rolling , the plate thickness deformation is 30mm;

[0048] The size of the slab is 180×400×6000mm;

[0049] A slab is obtained, the slab includes the following components in weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nickel brass strip. The nickel brass strip comprises, by weight percentage, 67%-73% of Cu, 2%-4.5% of Ni, 0.003%-0.015% of P, not larger than 0.01% of Pb, not larger than 0.012% of Fe and the balance Zn and inevitable impurities. According to the nickel brass strip, by optimizing the components and the content of the nickel brass strip, the corrosion resistance and wear resistance of the nickel brass strip are improved remarkably. The invention further provides a manufacturing of the nickel brass strip.

Description

technical field [0001] The invention relates to the technical field of copper material processing, in particular to a nickel brass strip and a preparation method thereof. Background technique [0002] With the continuous expansion of the application range of copper alloy products, higher and higher performance requirements are put forward for the performance of copper alloy strips. The corrosion resistance and wear resistance of the general-purpose nickel-brass alloys are increasingly unable to meet the material applications. At the same time, most of them are produced by horizontal continuous casting. [0003] Therefore, how to provide a nickel brass with high corrosion resistance and wear resistance is a technical problem that those skilled in the art need to solve urgently. Contents of the invention [0004] In view of this, the purpose of the present invention is to provide a kind of nickel brass strip, the corrosion resistance and wear resistance of this nickel brass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/04C22C1/03C22F1/08B23P15/00
CPCB23P15/00C22C1/03C22C9/04C22F1/08
Inventor 刘晨亮姜业欣赵强王晓腾周晶许丙军吕文波胡海军
Owner 中色正锐(山东)铜业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com