Wear-resistant alloy spring steel and thermal treatment process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A spring steel and wear-resistant technology, applied in the field of alloy steel, can solve the problems of low hardness and inability to effectively meet the hardness requirements of high-level wear-resistant alloy spring steel, so as to overcome low hardness, high cost performance, and improve wear resistance performance effect
Inactive Publication Date: 2016-10-26
ANHUI HONGQIAO METAL MFG
View PDF5 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, because it does not contain or contain a very small amount of carbide-forming alloying elements such as Cr, Mo, V, etc., the hardness is low, and it cannot effectively meet the hardness requirements of high-grade wear-resistant alloy spring steel.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] A kind of wear-resistant alloy spring steel, in the heat treatment process, the tempering temperature is 610°C, the holding time is 6-8h, air-cooled; the quenching temperature is 800°C, the holding time is 50min-100min, and water-cooling. The composition and ratio of alloy spring steel are: C: 0.3800%, Cu: 0.3200%, Mn: 0.1600%, Si: 3.8000%, Cr: 2.7000%, P: 0.0330%, S: 0.0330%, Ni: 0.3000% , Al: 0.0300%, V: 0.0060, B: 0.0200-1.1000%, and the balance is Fe and unavoidable impurities.
Embodiment 2
[0023] A kind of wear-resistant alloy spring steel, in the heat treatment process, the tempering temperature is 605°C, the holding time is 6-8h, air-cooled; the quenching temperature is 820°C, the holding time is 50min-100min, and water-cooling. The composition and ratio of alloy spring steel are: C: 0.3700%, Cu: 0.2900%, Mn: 0.1600%, Si: 2.8000%, Cr: 2.7000%, P: 0.0050%, S: 0.0430%, Ni: 0.4000% , Al: 0.0220%, V: 0.0060%, B: 0.0800%, Be: 0.0600%, and the balance is Fe and unavoidable impurities.
Embodiment 3
[0025] A kind of wear-resistant alloy spring steel, in the heat treatment process, the tempering temperature is 600°C, the holding time is 6-8h, air-cooled; the quenching temperature is 830°C, the holding time is 50min-100min, and water-cooling. The composition and ratio of alloy spring steel are: C: 0.3900%, Cu: 0.3600%, Mn: 0.1900%, Si: 3.4200%, Cr: 2.7000%, P: 0.0430%, S: 0.0230%, Ni: 0.3000% , Al: 0.0088%, V: 0.0050%, Mo: 0.0050%, Sr: 0.0031%, and the balance is Fe and unavoidable impurities.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses wear-resistant alloy spring steel and a thermal treatment process thereof. The thermal treatment process comprises the following steps: performing air cooling, wherein the tempering temperature is 600+ / -10 DEG C and the insulating time is 6-8h; and performing water cooling, wherein the quenching temperature is 800-830 DEG C and the insulating time is 50-100min. The spring steel comprises the following components in percentages: 0.3600-0.5500% of C, 0.2600-0.4500% of Cu, 0.1500-2.200% of Mn, 0.8000-5.4200% of Si, 0.7000-3.8000% of Cr, 0.030-0.0800% of P, 0.0030-0.0500% of S, 0.3000-0.5000% of Ni, 0.0008-0.0500% of Al, 0.0020-0.0100% of V and the balance of Fe and inevitable impurities. The wear-resistant alloy spring steel disclosed by the invention has an excellent wear-resisting performance, the consumption of materials is reduced, and the production efficiency is enhanced.
Description
technical field [0001] The invention relates to an alloy steel, in particular to a wear-resistant alloy spring steel and its heat treatment process. Background technique [0002] A spring is a mechanical part that uses elasticity to work. Parts made of elastic materials are deformed under the action of external force, and return to their original shape after the external force is removed. Also known as "spring". Spring is an important component of mechanization and automation, and is widely used in aerospace, machinery manufacturing, transportation, instrumentation and other industries, and is generally made of spring steel. [0003] According to the GB / T13304 standard, spring steel is divided into non-alloy spring steel (carbon spring steel) and alloy spring steel according to its chemical composition. Among them, alloy spring steel has a wide application prospect because the addition of alloy elements significantly improves the relaxation resistance, toughness, hardenab...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more