Melamine cross-linked polyvinyl alcohol hydrogel dressing

A technology of cross-linking polyvinyl alcohol and melamine, used in medical science, bandages, etc., can solve problems such as functional limitation repairing wounds, etc., and achieve the effects of repairing wound healing, diluting scars, and good cell growth.

Inactive Publication Date: 2016-11-09
王雅
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the function of existing hydrogel dressings is too limited to repair wounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The melamine cross-linked polyvinyl alcohol hydrogel dressing proposed by the present invention includes the following raw materials in parts by weight: 4 parts of water-retaining film, 6 parts of medical pressure-sensitive adhesive, 6 parts of acetylsalicylic acid, and melamine cross-linked polyvinyl alcohol water 7 parts gel, 5 parts mupirocin, 4 parts wood pulp fiber, 3 parts vitamin A, 5 parts vitamin E, 7 parts protein, 0.5 parts orange essential oil, 0.6 parts lemon essential oil, 0.8 parts peppermint essential oil.

[0018] The preparation method includes the following steps:

[0019] S1, evenly smear the water-retaining film on the medical non-woven fabric to obtain the outer layer of hydrogel A;

[0020] S2. Add melamine to polyvinyl alcohol under alkaline conditions with a pH of 7.2-8.0. After it is fully reacted, add acetylsalicylic acid and mupirocin, and mix with medical pressure-sensitive adhesive to prepare water Gel B;

[0021] S3. Mix vitamin A, vitamin E and ...

Embodiment 2

[0024] The melamine cross-linked polyvinyl alcohol hydrogel dressing proposed by the present invention includes the following raw materials in parts by weight: 3 parts of water-retaining film, 3 parts of medical pressure-sensitive adhesive, 5 parts of acetylsalicylic acid, and melamine cross-linked polyvinyl alcohol water 7 parts gel, 5 parts mupirocin, 5 parts wood pulp fiber, 3 parts vitamin A, 7 parts vitamin E, 8 parts protein, 0.3 parts orange essential oil, 0.5 parts lemon essential oil, 0.2 parts peppermint essential oil.

[0025] The preparation method includes the following steps:

[0026] S1, evenly smear the water-retaining film on the medical non-woven fabric to obtain the outer layer of hydrogel A;

[0027] S2. Add melamine to polyvinyl alcohol under alkaline conditions with a pH of 7.2-8.0. After it is fully reacted, add acetylsalicylic acid and mupirocin, and mix with medical pressure-sensitive adhesive to prepare water Gel B;

[0028] S3. Mix vitamin A, vitamin E and ...

Embodiment 3

[0031] The melamine cross-linked polyvinyl alcohol hydrogel dressing provided by the present invention includes the following raw materials in parts by weight: 5 parts of water-retaining film, 7 parts of medical pressure-sensitive adhesive, 3 parts of acetylsalicylic acid, and melamine cross-linked polyvinyl alcohol water 2 parts gel, 4 parts mupirocin, 6 parts wood pulp fiber, 3 parts vitamin A, 4 parts vitamin E, 7 parts protein, 0.5 parts orange essential oil, 0.6 parts lemon essential oil, 1 part peppermint essential oil.

[0032] The preparation method includes the following steps:

[0033] S1, evenly smear the water-retaining film on the medical non-woven fabric to obtain the outer layer of hydrogel A;

[0034] S2. Add melamine to polyvinyl alcohol under alkaline conditions with a pH of 7.2-8.0. After it is fully reacted, add acetylsalicylic acid and mupirocin, and mix with medical pressure-sensitive adhesive to prepare water Gel B;

[0035] S3. Mix vitamin A, vitamin E and pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses melamine cross-linked polyvinyl alcohol hydrogel dressing which is prepared from, by weight, 3-9 parts of water retention films, 1-8 parts of medical pressure-sensitive adhesive, 2-8 parts of acetylsalicylic acid, 2-12 parts of melamine cross-linked polyvinyl alcohol hydrogel, 1-6 parts of mupirocin, 4-12 parts of wood pulp cellulose, 2-6 parts of vitamin A, 4-12 parts of vitamin E, 4-8 parts of protein, 0.2-1 part of perfume essential oil, 0.2-0.8 part of lemon essence and 0.2-1.2 parts of mint essential oil. The melamine cross-linked polyvinyl alcohol hydrogel dressing has good water solubility and conglutination, and can better promote cell growth, acetylsalicylic acid has an antiinflammation effect, the high-performance hydroscopicity of wood pulp cellulose is far better than that of common gauze, vitamin A, vitamin B and protein accelerate blood circulation, skin ageing is relieved, and the essential oil can fade scars and can also make people pleasure. The dressing can promote cell growth and repair and heal wounds, meanwhile can fade scars and whiten and tender skin, is remarkable in treatment effect, has no side effect and is wide in prospect.

Description

Technical field [0001] The invention relates to the technical field of hydrogel dressings, in particular to a melamine cross-linked polyvinyl alcohol hydrogel dressing. Background technique [0002] With the development of medical technology, more and more dressings are used. Traditional dressings have high permeability, which can easily cause dehydration of the wound, stick to the wound, and cause re-mechanical damage when replaced. Microorganisms in the external environment can easily pass through and cause cross infection. The opportunity is high, the dosage is large, the replacement is frequent, time-consuming, and the patient is painful. Hydrogel dressings have only been developed in recent years. It is a new type of wound dressing composed of high water content water-absorbent polymer gel. It can automatically adjust the moisture of the wound, has the ability to absorb a small amount of exudate, and does not stick to the wound. Easy to remove. However, the functions of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L26/00
CPCA61L26/0014A61L26/0057A61L26/0061A61L26/0066A61L2300/21A61L2300/216A61L2300/252A61L2300/30A61L2300/41A61L2300/428C08L29/04
Inventor 王雅
Owner 王雅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap