Composite petroleum coke-based activated carbon and preparation method thereof and supercapacitor

An activated carbon and composite technology, applied in hybrid capacitor electrodes, chemical instruments and methods, carbon compounds, etc., can solve the problems of high internal resistance, far difference in energy density, low specific capacity, etc.

Active Publication Date: 2016-11-09
SHANDONG OBO NEW MATERIAL CO LTD
View PDF4 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the current commercial supercapacitor carbon is still dominated by micropores, and the content of mesopores is low; the internal resistance is high, and the preparation of supercapacitor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite petroleum coke-based activated carbon and preparation method thereof and supercapacitor
  • Composite petroleum coke-based activated carbon and preparation method thereof and supercapacitor
  • Composite petroleum coke-based activated carbon and preparation method thereof and supercapacitor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] The invention provides a kind of preparation method of composite petroleum coke-based activated carbon, comprising the following steps:

[0045] A) After coking the petroleum coke particles treated with the oxidative medium under the condition of the first gas, an activated carbon precursor is obtained;

[0046] B) after the activated carbon precursor obtained in the above steps is mixed with alkali, preactivation is carried out under the condition of the second gas, and then activated under the condition of the third gas, and then the activated carbon dispersion is obtained after washing;

[0047] C) mixing the activated carbon dispersion obtained in the above steps with the graphene oxide solution, drying, and then heat-treating under protective gas conditions to obtain a composite petroleum coke-based activated carbon.

[0048] In the present invention, firstly, the petroleum coke particles treated with an oxidative medium are coked under the condition of the first gas...

Embodiment 1

[0076] Take 100g of high-quality petroleum coke and crush it into 8-12μm particles, add 500mL of 30% hydrogen peroxide, heat to 50°C and soak for 2h, filter, wash, and dry; heat to 450°C under air for 45min, cool naturally, add 100g of powder of KOH and mix well. Put this mixture into a metal nickel crucible, raise the temperature to 450°C at a rate of 10-20°C / min under nitrogen atmosphere and keep it for 3h; . Dissolve the product in water, wash repeatedly until neutral, then add 6M hydrochloric acid to reflux for 2 hours, filter, wash with deionized water until neutral; add deionized water to make a 5% aqueous dispersion; add solid A monolayer graphene oxide solution (0.5%, 100 mL) with a content of 0.5 g and 0.5 g of melamine was ultrasonically stirred for 1 h and spray-dried. Put the obtained solid powder into a rotary furnace, raise the temperature to 800° C. under 10% hydrogen-nitrogen mixed gas and keep it for 2 hours, cool down, and magnetically separate to obtain su...

Embodiment 2

[0082] Take 100g of high-quality petroleum coke and crush it into 50-100μm particles, add 500mL of 1M nitric acid and reflux for 6h, filter, wash, and dry; heat the material to 350°C under air for 60min, and cool naturally. Add 50g KOH dissolved in ethanol to the material, mix evenly and heat to remove the solvent. Put this mixture into a metal nickel crucible, raise the temperature to 500°C at a rate of 10-20°C / min under nitrogen atmosphere and keep it for 1h; . Dissolve the product in water, wash repeatedly until neutral, then add 6M hydrochloric acid to reflux for 2 hours, filter, wash with deionized water until neutral; add deionized water to make a 5% aqueous dispersion; add solid A monolayer graphene oxide solution (0.5%, 100 mL) with a content of 0.2 g and 2.0 g of melamine was ultrasonically stirred for 1 h, and then spray-dried. Put the obtained solid powder into a rotary furnace, raise the temperature to 850°C under 10% ammonia-argon gas mixture and keep it for 1.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides composite petroleum coke-based activated carbon and a preparation method thereof. Activated active sites can be formed on the surface of petroleum coke through the dipping, coking and pre-activating processes of an oxidizing medium, chemical activation part pore-forming is promoted, the use amount of alkali is reduced, the mesopore rate is increased, and the problem that due to the fact that the surface of the petroleum coke is compact, pore forming is difficult is solved. Graphene oxide is reduced into graphene, a conductive network is formed, the conductivity of the activated carbon is improved, and the internal resistance of the activated carbon is reduced. High-temperature heat treatment is carried out jointly, surface functional groups are reduced, and the stability of super-capacitor carbon is improved. The prepared composite petroleum coke-based activated carbon has the advantages of being reasonable in pore size distribution, large in specific surface area, low in internal resistance, high in capacity, low in impurity and low in oxygen-containing functional group and can serve as the super-capacitor carbon, and the super-capacitor with better performance is obtained.

Description

technical field [0001] The invention belongs to the technical field of activated carbon materials, and in particular relates to a composite petroleum coke-based activated carbon, a preparation method thereof, and a supercapacitor. Background technique [0002] Activated carbon, also known as activated carbon black, is black powder or block, granular, honeycomb amorphous carbon, and there are also regular crystalline carbons. In addition to carbon elements, activated carbon also contains a small amount of hydrogen and oxygen elements. Part of these elements are derived from the incomplete carbonization of the activated carbon precursor and remain in the activated carbon, and the other part is formed by the reaction of activating reagents such as water or sodium hydroxide with the surface of activated carbon. Hydroxyl, carboxyl, carbonyl and other groups. In addition, there is also a part of ash in activated carbon, which is mainly composed of inorganic salts remaining in act...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B31/12C01B31/10H01G11/32H01G11/44
CPCC01B32/342H01G11/34Y02E60/13H01G11/32C01P2004/03C01P2004/61C01P2006/12C01P2006/17C01P2006/40C01P2006/80H01G11/44
Inventor 刘海波张在忠董士光胡兴华
Owner SHANDONG OBO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka