A self-healing environmentally friendly permeable polymer modified cement-based waterproof slurry

A waterproof slurry and permeable technology, applied in the field of polymer modified cement-based waterproof slurry, can solve the problems of micro-cracks that cannot be blocked and low permeability

Active Publication Date: 2018-07-27
TANGSHAN DONGFANG YUHONG WATERPROOF TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the permeability is low, it cannot react to form chelates, and it cannot block microcracks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1. Preparation of component A: first add 60 parts of water to the liquid material mixing tank, turn on the disperser of the mixing tank, and keep the speed at 1000 rpm, then add 600 parts of acrylic emulsion and 3 parts of defoamer to the liquid material Disperse in the material mixing tank for 5 minutes, then reduce the stirring speed to 800 rpm, measure 6 parts of dispersant, 3 parts of defoamer, and 1 part of fungicide into the liquid material mixing tank, stir for 20 minutes, and mix Evenly, the A component is obtained.

[0028] 2. Preparation of component B: Start the gravity-free powder mixer, keep the speed at 50 Hz, then add 350 parts of 42.5 gray cement to the powder mixing tank, and measure 150 parts of 60-120 mesh quartz sand into the mixing tank , then add 5 parts of naphthalene-based water reducer, 1 part of early strength agent, 3 parts of rubber powder, 60 parts of osmotic crystal masterbatch and 15 parts of super absorbent into the gravity-free mixing ta...

Embodiment 2

[0032] 1. Preparation of component A: first add 30 parts of water to the liquid material mixing tank, turn on the disperser of the mixing tank, keep the speed at 1000 rpm, then add 600 parts of acrylic emulsion and 3 parts of defoamer to the liquid material Disperse in the material mixing tank for 5 minutes, then reduce the stirring speed to 800 rpm, measure 8 parts of dispersant, 3 parts of defoamer, and 1 part of fungicide into the liquid material mixing tank, stir for 20 minutes, and mix Evenly, the A component is obtained.

[0033]2. Preparation of component B: Start the gravity-free powder mixer, keep the speed at 50 Hz, then add 400 parts of 42.5 gray cement to the powder mixing tank, and then add 150 parts of 60-120 mesh quartz sand to the mixing tank. In the cylinder, add 3 parts of naphthalene-based water reducer, 1 part of early strength agent, 3 parts of rubber powder, 40 parts of osmotic crystal masterbatch, and 10 parts of super water-absorbing agent into the grav...

Embodiment 3

[0037] 1. Preparation of component A: first add 20 parts of water to the liquid material mixing tank, turn on the disperser of the mixing tank, keep the speed at 1000 rpm, then add 550 parts of acrylic emulsion and 3 parts of defoamer to the liquid material Disperse in the material mixing tank for 5 minutes, then reduce the stirring speed to 800 rpm, measure 5 parts of dispersant, 3 parts of defoamer, and 1 part of fungicide into the liquid material mixing tank, stir for 20 minutes, and mix Evenly, the A component is obtained.

[0038] 2. Preparation of component B: Start the gravity-free powder mixer, keep the speed at 50 Hz, then add 300 parts of 42.5 gray cement to the powder mixing tank, and then add 150 parts of 60-120 mesh quartz sand to the mixing tank. In the tank, add 5 parts of naphthalene-based water reducer, 1 part of early strength agent, 3 parts of rubber powder, 50 parts of osmotic crystal masterbatch, and 20 parts of super water-absorbing agent into the gravity...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
tear strengthaaaaaaaaaa
Login to View More

Abstract

A self-healing environment-friendly penetrating type polymer modified cement-based waterproofing slurry is composed of a liquid material and a powdered material. The liquid material is prepared from, by weight, 550-750 parts of acrylic emulsion, 3-8 parts of defoaming agent, 5-10 parts of dispersing agent, 0.1-3 parts of sterilizing agent and 20-100 parts of deionized water; the powdered material is prepared from, by weight, 200-500 parts of 42.5 grey cement, 100-200 parts of quartz sand of 60 meshes to 120 meshes, 100-300 parts of quartz powder of 200 meshes, 1-5 parts of naphthalene water reducer, 0.5-2 parts of early strength agent, 1-5 parts of rubber powder, 30-70 parts of TC master batches and 8-20 parts of super water absorber. When the waterproofing slurry is used, the liquid material and the powdered material are stirred to be uniform according to the weight ratio of 10:(15-25), and the waterproofing slurry is obtained. According to the self-healing environment-friendly penetrating type polymer modified cement-based waterproofing slurry, the purposes of reaching self healing and environmental friendliness of the waterproofing slurry are achieved mainly by adding the immersing-crystallizing material TC master batches and the super water absorber in the powdered material and introducing the acrylic emulsion with low glass transition temperature into the liquid material; preparation is easy, the cost is low, environmental friendliness and no pollution are achieved, and mass production can be achieved.

Description

technical field [0001] The invention relates to a polymer-modified cement-based waterproof slurry, in particular to a self-healing, environment-friendly and permeable polymer-modified cement-based waterproof slurry. Background technique [0002] The two-component polymer modified cement-based waterproof slurry is a waterproof material with waterproof function formed by the mutual mixing of emulsion, cement and admixture. Its waterproof mechanism is mainly formed through the volatilization of emulsion water and the hydration reaction of cement powder High-strength and tough waterproof coating film, which plays an insulating role between moisture and building structure. Cement-based permeable crystalline waterproof material is a product made of Portland cement or ordinary Portland cement, quartz sand, etc., mixed with active chemical substances. It is a new type of rigid waterproof material. Its mechanism of action is that after it interacts with water, the active chemical su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/27
CPCC04B28/04C04B2111/00017C04B2111/27C04B2201/50C04B24/2641C04B2103/50C04B2103/408C04B2103/69C04B14/06C04B2103/302C04B24/04C04B24/2623C04B2103/0068C04B24/2652
Inventor 黄凯王会元黄江清
Owner TANGSHAN DONGFANG YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More