Organosilicone impregnating compound for quartz glass fibers and preparation method for organosilicone impregnating compound

A technology of quartz glass fiber and silicone, which is applied in the field of silicone-type sizing for quartz glass fiber and its preparation, can solve the problems of reducing the electrical insulation performance of quartz glass fiber, and achieve high tensile strength at break and low hairiness Effect

Active Publication Date: 2016-12-07
武汉鑫友泰光电科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the epoxy sizing agent is a water-soluble solution, which reduces the electrical insulation performance of the quartz glass fiber to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The embodiment of the present invention also provides a preparation method of the above-mentioned silicone-type sizing agent for quartz glass fibers, comprising the following steps:

[0025] In terms of parts by mass, take 40-50 parts of diluent, stir, add 0.1-2.0 parts of viscosity modifier, continue stirring, add 4-10 parts of silicone resin, and stir evenly to obtain a silicone resin mixture; Dilute 0.1-2.0 parts of antistatic agent with 5-10 parts of diluent to obtain a mixed solution of antistatic agent; add the mixed solution of silicone resin, mixed solution of antistatic agent, and 4-10 parts of silicone oil into the mixing container in sequence, and stir uniform, and then add the remaining diluent, so that the total amount of diluent added is 78 to 90 parts, that is, the silicone-type sizing agent for quartz glass fiber is obtained.

[0026] Preferably, the wetting agent includes 5-8 parts of silicone resin, 5-8 parts of silicone oil, 0.5-1.0 part of antistatic...

Embodiment 1

[0031] This embodiment provides a silicone-type sizing for quartz glass fibers. In parts by mass, the sizing includes 4 parts of epoxy resin-modified silicone resin, 4 parts of polydimethylsiloxane, 0.1 Parts of fatty amine polyoxyethylene quaternary ammonium salt, 0.1 part of polyethylene glycol, 90 parts of butyl acetate.

[0032] This embodiment provides a method for preparing the above-mentioned silicone-type sizing agent for quartz glass fibers, comprising the following steps:

[0033] In terms of parts by mass, take 40 parts of butyl acetate, stir, add 0.1 parts of polyethylene glycol, continue stirring, add 4 parts of epoxy resin modified silicone resin, and stir evenly to obtain a silicone resin mixture; Dilute 0.1 part of aliphatic amine polyoxyethylene quaternary ammonium salt with 10 parts of butyl acetate to obtain an antistatic agent mixture; mix silicone resin mixture, antistatic agent mixture, and 4 parts of polydimethylsiloxane Sequentially added to the mixing...

Embodiment 2

[0035] This embodiment provides a silicone-type sizing for quartz glass fibers. In parts by mass, the sizing includes 5 parts of polyester resin-modified silicone resin, 5 parts of polydiethylsiloxane, 0.5 Parts of imidazoline-based quaternary ammonium salt, 0.5 parts of polyethylene glycol, 82 parts of ethyl acetate.

[0036] This embodiment provides a method for preparing the above-mentioned silicone-type sizing agent for quartz glass fibers, comprising the following steps:

[0037] In terms of parts by mass, take 40 parts of ethyl acetate, stir, add 0.5 parts of polyethylene glycol, continue stirring, add 5 parts of polyester resin modified silicone resin, and stir evenly to obtain a silicone resin mixture; Dilute 0.5 parts of imidazoline-based quaternary ammonium salt with 5 parts of ethyl acetate to obtain a mixed solution of antistatic agent; add the mixed solution of silicone resin, mixed solution of antistatic agent, and 5 parts of polydiethylsiloxane in sequence In t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organosilicone impregnating compound for quartz glass fibers and a preparation method for the organosilicone impregnating compound and relates to the field of quartz glass fiber impregnating compounds. The impregnating compound contains the ingredients in parts by mass: 4-10 parts of silicone resin, 4-10 parts of silicone oil, 0.1-2.0 parts of antistatic agent, 0.1-2.0 parts of viscosity regulator and 78-90 parts of diluent, wherein the diluent is ethyl acetate or butyl acetate. According to the organosilicone impregnating compound for the quartz glass fibers and the preparation method for the organosilicone impregnating compound, the condition that electrical insulation properties of the quartz glass fibers are not affected can be guaranteed, meanwhile, quartz glass fiber yarn treated by using the organosilicone impregnating compound is low in hair feather volume and relatively high in fracture tensile strength.

Description

technical field [0001] The invention relates to the field of sizing agents for quartz glass fibers, in particular to an organosilicon-type sizing agent for quartz glass fibers and a preparation method thereof. Background technique [0002] Quartz glass fiber has high heat resistance, can be used below 1100°C for a long time, and can withstand high temperature up to 1700°C in an instant. At the same time, due to the excellent electrical insulation of quartz glass fiber, its dielectric constant and dielectric loss coefficient are the highest among all minerals. The best fiber, therefore, quartz glass fiber has a wide range of applications in aviation, aerospace, military industry, semiconductor, high temperature insulation, high temperature filtration. [0003] Quartz glass fiber is generally drawn from a quartz glass rod with a silica content of more than 99.95%. Due to the brittleness of quartz glass, a layer of sizing agent must be coated on the surface of quartz glass fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/40
CPCC03C25/40
Inventor 夏新冯严严谢育钊汤安琪刘正楠
Owner 武汉鑫友泰光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com