Insecticidal lamp plastic lampshade and production method thereof
An insecticidal lamp and lampshade technology, applied in the field of lampshades, can solve the problems of lack of insecticidal effect, unsatisfactory lampshade material of insecticidal lamps, etc., and achieve the effects of good light guiding effect, less light loss loss and good high temperature resistance performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] This embodiment provides a plastic lampshade for an insecticidal lamp, which is made of the following components: 30kg polyacrylonitrile, 30kg polytetrafluoroethylene, 5kg polycarbonate, 5kg dibutyltin dilaurate, N, N '-diphenylbenzidinediamine 5kg, polytrimethylene terephthalate 5kg, antioxidant 1kg, filler 4kg, lubricant 5kg; antioxidant is equal amount of methylphenol, cyclohexanone, bisphenol phosphite A ester; the filler is the same amount of modified silica, modified alumina, nano-aluminum carbide, and modified calcium carbonate; the lubricant is the same amount of glycerin, polyfatty acid resin calcium zinc, rice bran wax, zinc stearate .
[0014] At the same time, the present invention provides a method for preparing the plastic lampshade of insecticidal lamps. After weighing each component according to the above-mentioned mass percentage ratio, mix all the components, heat, melt and stir evenly, and then pour it into the mold Press molding to obtain the plasti...
Embodiment 2
[0016] This embodiment provides a plastic lampshade for an insecticidal lamp, which is made of the following components: 50kg polyacrylonitrile, 50kg polytetrafluoroethylene, 10kg polycarbonate, 10kg dibutyltin dilaurate, N, N '-diphenylbenzidinediamine 10kg, polytrimethylene terephthalate 10kg, antioxidant 3kg, filler 8kg, lubricant 8kg; antioxidant is equal amount of methylphenol, cyclohexanone, bisphenol phosphite A ester; the filler is the same amount of modified silica, modified alumina, nano-aluminum carbide, and modified calcium carbonate; the lubricant is the same amount of glycerin, polyfatty acid resin calcium zinc, rice bran wax, zinc stearate .
[0017] At the same time, the present invention provides a method for preparing the plastic lampshade of insecticidal lamps. After weighing each component according to the above-mentioned mass percentage ratio, mix all the components, heat, melt and stir evenly, and then pour it into the mold Press molding to obtain the pl...
Embodiment 3
[0019] This embodiment provides a plastic lampshade for an insecticidal lamp, which is made of the following components: 40kg polyacrylonitrile, 40kg polytetrafluoroethylene, 8kg polycarbonate, 8kg dibutyltin dilaurate, N, N '-diphenylbenzidinediamine 8kg, polytrimethylene terephthalate 8kg, antioxidant 2kg, filler 6kg, lubricant 7kg; antioxidant is equal amount of methylphenol, cyclohexanone, bisphenol phosphite A ester; the filler is the same amount of modified silica, modified alumina, nano-aluminum carbide, and modified calcium carbonate; the lubricant is the same amount of glycerin, polyfatty acid resin calcium zinc, rice bran wax, zinc stearate .
[0020] At the same time, the present invention provides a method for preparing the plastic lampshade of insecticidal lamps. After weighing each component according to the above-mentioned mass percentage ratio, mix all the components, heat, melt and stir evenly, and then pour it into the mold Press molding to obtain the plasti...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com