A polymer material, thermal insulation technology, applied in the field of preparation of thermal insulation polymer materials, can solve problems such as poor heat resistance, incomplete satisfaction, casualties, etc., to overcome poor durability, reduce processing costs, and service life. long effect

Active Publication Date: 2017-01-04
四川梅塞尔科技有限公司
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the cost of organic foam materials is high, the raw materials are not easy to obtain, the insulation effect is good, and the density is small, but the heat resistance is poor, easy to burn, and produces a large amount of toxic smoke when burning, which will not only accelerate the spread of the fire, but also easily cause casualties
Therefore, there is currently no thermal insulation polymer material that fully meets the requirements of energy saving, heat preservation, fire prevention, pollution-free, low cost, and cheap and easy-to-obtain raw materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] A method for preparing a thermal insulation polymer material, comprising the steps of:

[0032] A, the plant biomass waste is crushed;

[0033] B. Soak the pulverized plant biomass waste with a strong alkali solution, neutralize the alkalinity, and dry to obtain activated plant biomass waste;

[0034] C. Activate plant biomass waste according to the mass ratio: functional monomer: initiator: dispersant = 1000: 10-20: 0-2: 0-100 for reaction, and after the reaction, the surface grafted modified plant biomass can be obtained. material waste powder;

[0035] D. According to the mass ratio surface grafting modified plant biomass waste powder: flow modified monomer: initiator: dispersant = 1000: 10~20: 1~2: 1~10 for mixing and granulation to obtain improved Post-destructive plant biomass waste dry powder;

[0036] E. Plant biomass waste dry powder modified according to the mass ratio: polyvinyl chloride: processing aid: filler = 700-1000: 0-300: 10-30: 0-20 mixed and gran...

Embodiment 1

[0047] A: The wheat straw is recycled, and then the wheat straw is crushed so that the grain size of the wheat straw reaches 80 mesh.

[0048] B: Weigh 1000 g of 80-mesh wheat straw, place it in a reaction kettle, add 6 L of inorganic strong alkali sodium hydroxide solution, and soak for 24 hours. After soaking for 24 hours, the sodium hydroxide was filtered out, and purified water was added to clean the wheat straw powder. Add pure water several times to clean until the pH value of the cleaning solution is about 7. Then carry out drying treatment, and the activated wheat straw can be obtained only when the water content reaches below 0.1%.

[0049] C: At room temperature, mix 1000g of activated wheat straw, 20g of succinic anhydride, 2g of glutaric acid peroxide, and 1g of polyvinyl alcohol, and then put the mixed material into a hot mixer for thermal surface modification. The temperature was controlled at 120° C., and the rotational speed of the mixer was at 8 rpm to obtai...

Embodiment 2

[0061] A: The bagasse is recovered, and then the bagasse is crushed to make the bagasse particle size reach 60 mesh.

[0062] B: Weigh again 1000g of 60-mesh bagasse, place it in a reaction kettle, add 6L of inorganic strong alkali sodium hydroxide solution, and soak for 24 hours. After soaking for 24 hours, the sodium hydroxide was filtered out, and purified water was added to clean the bagasse powder. Adding pure water several times to wash until the pH value of the cleaning solution is about 7, and then performing drying treatment, and the activated bagasse can be obtained when the water content reaches below 0.1%.

[0063] C: Mix 1000g of activated bagasse and 10g of hexanoic anhydride, put the mixed material into a hot mixer for thermal surface modification, control the temperature at 100°C, and the speed of the mixer at 30rpm to obtain a surface contact surface. Modified bagasse powder.

[0064] D: Mix 1000g surface-grafted modified bagasse powder, 10g methyl acrylate,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of preparation and modification of natural high polymer materials, and aims to solve the technical problems of high cost, poor heat resistance, flammability and toxic fume generation in case of combustion in the prior art. The invention provides a preparation method of a heat preservation and insulation high polymer material. The method comprises the following steps: A, pulverizing plant biomass waste; B, activating the plant biomass waste; C, obtaining surface grafting modified plant biomass waste powder; D, granulating to obtain modified plant biomass waste dry powder; and E, uniformly mixing the modified plant biomass waste dry powder, polyvinyl chloride, processing aids and fillers according to a certain mass ratio to obtain the heat preservation and insulation high polymer material. A heat preservation and insulation material product prepared by using the heat preservation and insulation high polymer material as a raw material has the advantages of hard texture, light weight, favorable heat preservation effect, environment friendliness and the like.

Description

technical field [0001] The invention belongs to the field of preparation and modification of natural polymer materials, and in particular relates to a preparation method of thermal insulation polymer materials. Background technique [0002] With the advancement and development of science and technology and the continuous consumption of non-renewable energy, energy saving and consumption reduction of building materials has become an important topic and research direction in today's society. Building materials refer to the general term for materials used in civil engineering and construction engineering. It can be divided into structural materials, decorative materials and some special materials. Structural materials include wood, bamboo, stone, cement, concrete, metal, bricks, ceramics, glass, engineering plastics, composite materials, etc.; decorative materials include various coatings, paints, coatings, veneers, tiles of various colors, and special effects Glass, etc.; sp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/00C08L27/06C08K13/02C08K5/098C08K3/22C08K3/34C08F289/00C08F220/14C08F220/18C08F222/06C08F285/00C08H8/00
CPCC08F285/00C08F289/00C08H8/00C08L51/00C08L2201/02C08L27/06C08K13/02C08K5/098C08K2003/2241C08K3/34C08F220/14C08F220/18C08F220/1802C08F220/1804
Inventor 包黎霞倪玉英倪念英董顺平
Owner 四川梅塞尔科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap