RH deep decarbonization and clean steel smelting method
A smelting method and technology for cleaning steel, applied in the field of steelmaking and continuous casting, which can solve the problems of rapid hydrogen diffusion, high safety requirements for injection systems, and easy fire and explosion.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] The present invention is further illustrated by some examples below.
[0016] For example, using this technology to produce ultra-low carbon IF steel, the process is carried out in sequence as follows:
[0017] (1) After the molten steel enters the RH station, the molten steel weight is 255t, the molten steel temperature is 1605°C, the molten steel oxygen content is 0.064%, and the molten steel carbon content is 0.042%. After that, it is evacuated, the lifting gas is argon, and the gas flow is 140Nm 3 / h, blow in oxygen 100m at the 3rd minute of vacuuming 3 .
[0018] (2) Sampling at the 15th minute of RH refining, the carbon content in the molten steel was detected to be 0.0029%. At this time, the moisture content in the argon gas was 0.0015% according to the dew point meter, and an industrial humidifier was used to humidify the lifting gas. After humidification The moisture content in the lifting gas is 50%, the hydrogen content of molten steel is detected to be 0.0021% dur...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap