A fireproof material and mass fraction technology, applied in the field of composite fireproof materials, can solve problems such as weak decoration
Inactive Publication Date: 2017-01-11
魏忠
View PDF0 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
There are two commonly used types: one is high-pressure decorative fire-resistant board, which has the advantages of fireproof, moisture-proof, wear-resistant, oil-resistant, easy to clean, and has many varieties of designs and colors; the other
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0011] Implementation mode one:
[0012] In terms of parts by mass, it includes the following components: 3.6 parts of aluminum oxide, 45 parts of cement, 8 parts of silica, 15 parts of polyester fiber, 5.6 parts of slag powder, 5 parts of sodium hexametaphosphate, 3 parts of magnesium hydroxide , 6 parts of citric acid, 1.5 parts of aluminum silicate fiber, 12 parts of maleimide.
Example Embodiment
[0013] Implementation mode two:
[0014] In terms of parts by mass, it includes the following components: 5.4 parts of aluminum oxide, 60 parts of cement, 15 parts of silica, 20 parts of polyester fiber, 7.2 parts of slag powder, 10 parts of sodium hexametaphosphate, 9 parts of magnesium hydroxide , 14 parts of citric acid, 3.8 parts of aluminum silicate fiber, 18 parts of maleimide.
Example Embodiment
[0015] Implementation mode three:
[0016] In terms of parts by mass, it includes the following components: 4.2 parts of aluminum oxide, 50 parts of cement, 10 parts of silica, 16 parts of polyester fiber, 6.1 parts of slag powder, 6 parts of sodium hexametaphosphate, 5 parts of magnesium hydroxide , 8 parts of citric acid, 2.2 parts of aluminum silicate fiber, 15 parts of maleimide.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of fireproof materials, particularly a composite fireproof material which comprises the following components in parts by mass: 3.6-5.4 parts of aluminum oxide, 45-60 parts of cement, 8-15 parts of silicon dioxide, 15-20 parts of polyester fiber, 5.6-7.2 parts of furnace slag powder, 5-10 parts of sodium hexametaphosphate, 3-9 parts of magnesium hydroxide, 6-14 parts of citric acid, 1.5-3.8 parts of aluminum silicate fiber and 12-18 parts of maleimide. By adopting the formula, the fireproof material has the advantages of high fire-resistant temperature, low manufacturing cost and simple preparation method. Besides, the composite fireproof material has the characteristics of simple and accessible components, long fire-resistant time, low production cost and stable quality, and is easy to produce.
Description
technical field [0001] The invention relates to the technical field of fireproof materials, in particular to a composite fireproof material. Background technique [0002] Fireproof materials are mostly used in buildings, and various forms play an absolute role in modern fire prevention. Commonly used fireproof materials include fireproof boards, fireproof doors, fireproof glass, and fireproof coatings. Fireproof board is the most commonly used material on the market at present. There are two commonly used types: one is high-pressure decorative fire-resistant board, which has the advantages of fireproof, moisture-proof, wear-resistant, oil-resistant, easy to clean, and has many varieties of designs and colors; the other is glass magnesium fire-resistant board, the outer layer is decorative material, and the inner layer is The first layer is mineral glass magnesium fireproof material, which can resist high temperature of 1500 degrees, but the decoration is not strong. The in...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more