Novel environment-friendly bricks and production method thereof

An environmentally friendly brick and a new type of technology, applied in the field of building materials, can solve the problem that clay resources can no longer meet the needs of brick making, and achieve the effects of low cost, high compressive strength and broad market prospects.

Inactive Publication Date: 2017-01-11
广西塔锡科技有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making. In addition, my country's continuous strengthening of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The new environmentally friendly brick of this embodiment is made of the following raw materials: 10kg of coal gangue powder, 15kg of quicklime, 10kg of construction waste, 15kg of granite tailings, 10kg of coal slime and 20kg of kaolin tailings powder, wherein the coal gangue powder The particle size of the construction waste is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the granite tailings is 40-60 mesh, and the particle size of the kaolin tailings powder is 40-60 mesh .

[0021] The production method of the above-mentioned novel environmental protection brick comprises the following process steps: take raw materials with the following weight: 10kg of coal gangue powder, 15kg of quicklime, 10kg of construction waste, 15kg of granite tailings, 10kg of coal slime and 20kg of kaolin tailings powder, wherein, the The particle size of coal gangue powder is 80-100 mesh, the particle size of the construction waste is 40-60 m...

Embodiment 2

[0024] The novel environmentally friendly brick of this embodiment is made of raw materials with the following weights: 15kg of coal gangue powder, 10kg of quicklime, 15kg of construction waste, 10kg of granite tailings, 15kg of coal slime and 15kg of kaolin tailings powder, wherein the coal gangue powder The particle size of the construction waste is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the granite tailings is 40-60 mesh, and the particle size of the kaolin tailings powder is 40-60 mesh .

[0025] The production method of the above-mentioned novel environmental protection brick comprises the following process steps: take raw materials of the following weight: 15kg of coal gangue powder, 10kg of quicklime, 15kg of construction waste, 10kg of granite tailings, 15kg of coal slime and 15kg of kaolin tailings powder, wherein, the The particle size of coal gangue powder is 80-100 mesh, the particle size of the construction was...

Embodiment 3

[0028] The new environmental protection brick of the present embodiment is made of the following raw materials: 20kg of coal gangue powder, 5kg of quicklime, 20kg of construction waste, 5kg of granite tailings, 20kg of coal slime and 10kg of kaolin tailings powder, wherein the coal gangue powder The particle size of the construction waste is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the granite tailings is 40-60 mesh, and the particle size of the kaolin tailings powder is 40-60 mesh .

[0029] The production method of the above-mentioned novel environmental protection brick comprises the following process steps: take raw materials of the following weight: 20kg of coal gangue powder, 5kg of quicklime, 20kg of construction waste, 5kg of granite tailings, 20kg of coal slime and 10kg of kaolin tailings powder, wherein, the The particle size of coal gangue powder is 80-100 mesh, the particle size of the construction waste is 40-60 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses novel environment-friendly bricks and a production method thereof and belongs to the technical field of building materials. The novel environment-friendly bricks are prepared from, by weight, 10-20 parts of coal gangue powder, 5-15 parts of quick lime, 10-20 parts of building rubbish, 5-15 parts of granite tailings, 10-20 parts of coal slime and 10-20 parts of kaolin tailing powder. The novel environment-friendly bricks are high in compressive strength, good in breaking resistance and low in cost, resources are effectively saved, and secondary pollution to the environment is avoided.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular, it provides a novel environmentally friendly brick and a production method thereof. Background technique [0002] Traditional fired bricks mainly use clay as raw material. However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making, coupled with the continuous strengthening of environmental protection in our country. Therefore research and develop a kind of new environment-friendly brick that uses other raw materials to replace clay, has higher performance and becomes the problem that needs to be solved urgently. Contents of the invention [0003] One of the purposes of the present invention is to provide a novel environmentally friendly brick. The novel environment-friendly brick of the present invention has high compressive strength...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/00C04B18/12C04B18/16C04B18/04B28B1/00B28C5/00B28B3/00B28B11/24
CPCB28B1/00B28B3/00B28B11/24B28C5/003C04B30/00C04B2201/50C04B18/12C04B22/064C04B18/16C04B18/0481Y02W30/91
Inventor 徐庆富
Owner 广西塔锡科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com