Preparing technology of organic coating of high purity industrial product zinc sulfide powder

A preparation process, zinc sulfide technology, applied in dyeing high-molecular organic compound treatment, dyeing low-molecular organic compound treatment, inorganic pigment treatment, etc., can solve problems such as uneven filling of zinc sulfide powder, affecting luminous effect and appearance, etc., to achieve Good for long-term storage, low equipment requirements, and good compatibility

Inactive Publication Date: 2017-01-18
潍坊大耀新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the material is brittle and broken, the zinc sulfide luminescent powder particles escape to form cavities, indicating that the non-organic-coated high-purity industrial zinc sulfide powder is not filled uniformly in the matrix, which affects its luminous effect and appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing technology of organic coating of high purity industrial product zinc sulfide powder
  • Preparing technology of organic coating of high purity industrial product zinc sulfide powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1, a preparation process of organic coating of high-purity industrial zinc sulfide powder, the preparation method comprises the following steps:

[0034] (1) Put 100kg of low-molecular-weight, high-density polyethylene powder into an electric oil heating reactor, and at the same time add 10kg of metallocene catalyst, 0.5kg of polymerization inhibitor, 0.5kg of surfactant, etc. and stir.

[0035] (2) Rotate electric oil to heat the reactor to stir the mixture of polyethylene powder and additives, and pass in purified air or O 3 And gradually raise the temperature, the heating rate is 1.5°C / min, when the temperature rises to 110°C, keep warm for 72-96 hours, during which air or O 3 And keep rotating the reactor.

[0036] (3) After the heat preservation is completed, cool down to room temperature to obtain oxidized polyethylene wax powder.

[0037] (4) Put the oxidized polyethylene wax powder obtained in step (3) into a high-temperature reaction kettle, and at...

Embodiment 3

[0059] Embodiment 3, a preparation process of organic coating of high-purity industrial zinc sulfide powder, the preparation method comprises the following steps:

[0060] (1) Put 100kg of low-molecular-weight, high-density polyethylene powder into an electric oil heating reactor, and at the same time add 12kg of metallocene catalyst, 0.8kg of polymerization inhibitor, 0.8kg of surfactant, etc. and stir.

[0061] (2) Rotate electric oil to heat the reactor to stir the mixture of polyethylene powder and additives, and pass in purified air or O 3 And gradually heat up, the heating rate is 1.5 ℃ / min, when the temperature rises to 115 ℃, keep warm for 72-96 hours, during which air or O 3 And keep rotating the reactor.

[0062] (3) After the heat preservation is completed, cool down to room temperature to obtain oxidized polyethylene wax powder.

[0063] (4) Put the oxidized polyethylene wax powder obtained in step (3) into a high-temperature reaction kettle, and at the same ti...

Embodiment 4

[0072] Embodiment 4, a preparation process of organic coating of high-purity industrial product zinc sulfide powder, the preparation method comprises the following steps:

[0073] (1) Put 100kg of low-molecular-weight, high-density polyethylene powder into an electric oil heating reactor, and at the same time add 13kg of metallocene catalyst, 1.2kg of polymerization inhibitor, 1.2kg of surfactant and stir.

[0074] (2) Rotate electric oil to heat the reactor to stir the mixture of polyethylene powder and additives, and pass in purified air or O 3 And gradually raise the temperature, the heating rate is 1.5°C / min, when the temperature rises to 125°C, it is kept for 72-96 hours, and air or O is continuously introduced during this period. 3 And keep rotating the reactor.

[0075] (3) After the heat preservation is completed, cool down to room temperature to obtain oxidized polyethylene wax powder.

[0076] (4) Put the oxidized polyethylene wax powder obtained in step (3) into a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing technology of organic coating of high purity industrial product zinc sulfide powder. Firstly, polyethylene powdery material with small molecular weight and high density as well as catalyst are heat in the reaction kettle to increase temperature, afterwards oxidizing agent (hot air, O2 or H2O2) is introduced to prepare oxidized polyethlene wax, the prepared oxidized polyethlene wax is added into emulsifier, polymerization inhibitor, co-emulsifier and the like, emulsification is conducted under status of heating and stirring to obtain oxidized polyethlene wax emulsion, then the oxidized polyethlene wax emulsion is atomized to conduct spraying of the high purity industrial product zinc sulfide powder, so that organic coating of the high purity industrial product zinc sulfide powder is achieved.

Description

technical field [0001] The invention relates to a preparation process for organic coating of high-purity industrial zinc sulfide powder, in particular to a high-molecular coating that can be used for injection molding, long glass fiber, home appliance electronic injection molding, anti-algae coating, brake pad material, resin, etc. The invention relates to a preparation process of high-purity industrial product zinc sulfide powder whose surface is organically coated, and belongs to the technical field of chemical industry. Background technique [0002] High-purity industrial zinc sulfide powder has the characteristics of wear resistance, high strength, excellent penetration of far-infrared beams, and high temperature resistance. It is a non-toxic, harmless, safe and environmentally friendly green product, and is widely used in injection molding, coatings, and automobile brakes. It is a complexing agent, passivating agent, and marine oil stain remover for adsorbing heavy meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/04C09C3/06C09C3/08C09C3/10C08K9/10C08K3/30C08L27/06
CPCC09C1/04C08K3/30C08K9/10C08K2003/3036C09C3/06C09C3/08C09C3/10C08L27/06
Inventor 王强
Owner 潍坊大耀新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap