Industrial crossover vehicle

A straddle vehicle, industrial technology, applied in the direction of metal material coating process, etc., can solve the problems that need to be improved, the surface finish is not ideal, etc., and achieve the effect of excellent abrasion resistance and good surface finish

Inactive Publication Date: 2017-01-25
常熟市常宝电动过跨平车厂
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing industry has used straddle vehicles, including metal spindles, but the wear resistance, rust resistance, corrosion resistance, oxidation resistance, heat resistance, cold resistance, and weather resistance of metal spindles need to be improved, and the surface finish is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The straddle vehicle for industrial use includes a metal main shaft, and the metal main shaft is passivated, and the passivation treatment includes the following steps:

[0026] 1) Put 1 to 2 parts by weight of glycerol monostearate, 1.8 parts by weight of sodium alkylsulfonate, 3.6 parts by weight of hexyldecanol, 4.2 parts by weight of phosphotungstic heteropolyacid, and 0.5 parts by weight of silicon dioxide into 30 parts by weight in sequence part deionized water, stir evenly;

[0027] 2) Add 5.6 parts by weight of aminotriacetic acid, 1.5 parts by weight of 1-hydroxybenzotriazole, 1.5 parts by weight of sodium dodecylbenzenesulfonate, 1.6 parts by weight of tetrasodium ethylenediaminetetraacetic acid, and 0.8 parts by weight of phosphoric acid Sodium hydrogen disodium, continue to stir, until fully mixed, make the passivation treatment liquid;

[0028] 3) Put the metal spindle into the passivation treatment solution for passivation treatment, the treatment tempera...

Embodiment 2

[0030] The straddle vehicle for industrial use includes a metal main shaft, and the metal main shaft is passivated, and the passivation treatment includes the following steps:

[0031] 1) 1 weight part of glycerol monostearate, 1.8 weight parts of sodium alkylsulfonate, 3.6 weight parts of hexyldecanol, 4.2 weight parts of phosphotungstic heteropoly acid, and 0.5 weight part of silicon dioxide are dropped into 30 weight parts successively. In ionized water, stir evenly;

[0032] 2) Add 5.6 parts by weight of aminotriacetic acid, 1.5 parts by weight of 1-hydroxybenzotriazole, 1.5 parts by weight of sodium dodecylbenzenesulfonate, 1.6 parts by weight of tetrasodium ethylenediaminetetraacetic acid, and 0.8 parts by weight of phosphoric acid Sodium hydrogen disodium, continue to stir, until fully mixed, make the passivation treatment liquid;

[0033] 3) Put the metal spindle into the passivation treatment solution for passivation treatment, the treatment temperature is 40°C, and ...

Embodiment 3

[0035] The straddle vehicle for industrial use includes a metal main shaft, and the metal main shaft is passivated, and the passivation treatment includes the following steps:

[0036] 1) 2 parts by weight of glycerol monostearate, 1.8 parts by weight of sodium alkyl sulfonate, 3.6 parts by weight of hexyldecanol, 4.2 parts by weight of phosphotungstic heteropolyacid, and 0.5 parts by weight of silicon dioxide are dropped into 30 parts by weight successively. In ionized water, stir evenly;

[0037] 2) Add 5.6 parts by weight of aminotriacetic acid, 1.5 parts by weight of 1-hydroxybenzotriazole, 1.5 parts by weight of sodium dodecylbenzenesulfonate, 1.6 parts by weight of tetrasodium ethylenediaminetetraacetic acid, and 0.8 parts by weight of phosphoric acid Sodium hydrogen disodium, continue to stir, until fully mixed, make the passivation treatment liquid;

[0038] 3) Put the metal spindle into the passivation treatment solution for passivation treatment, the treatment tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an industrial crossover vehicle. A metal main shaft of the crossover vehicle is subjected to passivation treatment including the following steps: 1), sequentially dropping 1-2 parts by weight of glycerol monostearate, 1.8 parts by weight of alkyl sodium sulfonate, 3.6 parts by weight of hexyldecanol, 4.2 parts by weight of phosphotungstic acid, and 0.5 part by weight of silicon oxide into 30 parts by weight of deionized water and evenly stirring; 2) sequentially dropping 5.6 parts by weight of nitrilotriacetic acid, 1.5 parts by weight of 1-hydroxybenzotriazole, 1.5 parts by weight of sodium dodecylbenzenesulfonate, 1.6 parts by weight of ethylenediamine tetraacetic acid disodium and 0.8 part by weight of disodium hydrogen phosphate again, continuously stirring until the components are fully and evenly mixed to prepare a passivation treatment solution; 3) putting the metal main shaft into the passivation treatment solution to carry out passivation treatment for 40 seconds at the treatment temperature of 50 DEG C, taking out, cleaning with pure water and drying again. The industrial crossover vehicle, of which the metal main shaft is subjected to passivation treatment, has good performance and is good in surface finish.

Description

technical field [0001] The present invention relates to industrial straddle vehicles. Background technique [0002] The existing industry has used straddle vehicles, including metal spindles, but the wear resistance, rust resistance, corrosion resistance, oxidation resistance, heat resistance, cold resistance, and weather resistance of metal spindles need to be improved, and the surface finish is not ideal. Contents of the invention [0003] The object of the present invention is to provide an industrial straddle vehicle, the metal main shaft of which is passivated to form a uniform passivation protective film on the metal surface, which has excellent abrasion resistance, rust resistance, corrosion resistance, oxidation resistance, and corrosion resistance. Heat, cold resistance, weather resistance, and good surface finish. [0004] In order to achieve the above object, the technical solution of the present invention is to design an industrial straddle vehicle, which incl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More