High-resistance nickel-chromium electrothermal alloy material for electric heating elements

A technology of nickel-chromium alloy and electric heating element, which is applied in the direction of metal material coating process, etc., can solve the problem of unsatisfactory surface finish, and achieve the effect of excellent abrasion resistance and good surface finish

Inactive Publication Date: 2017-01-25
CHANGSHU MEILI ALLOY MATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing electric heating elements use nickel-chromium high-resistance electric heating alloy materials. The wear resistance, oxidation resistance, corrosion resistance, rust resistance, and weather resistance of the nickel-chromium alloy main body need to be improved, and the surface finish is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The electric heating element is made of nickel-chromium high-resistance electric heating alloy material, which includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0026] 1) 1 to 2 parts by weight of sodium hydroxide, 3.3 parts by weight of amino trimethylene phosphonic acid, 2.1 parts by weight of γ-glycidyl ether trimethoxysilane, 1.1 parts by weight of nonylphenol ethoxylate carboxylate Drop into 40 parts by weight of deionized water successively, and stir evenly;

[0027] 2) Add 5.5 parts by weight of diethylene glycol phenyl ether, 2.6 parts by weight of methyl vinyl ketone, 0.5 parts by weight of sodium secondary alkyl sulfate, and 0.7 parts by weight of benzotriazole, and continue stirring until fully mixed Uniformly, the coating treatment solution is prepared;

[0028] 3) Put the nickel-chromium alloy main body into the coating treatment s...

Embodiment 2

[0030] The electric heating element is made of nickel-chromium high-resistance electric heating alloy material, which includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0031] 1) Put 1 part by weight of sodium hydroxide, 3.3 parts by weight of aminotrimethylene phosphonic acid, 2.1 parts by weight of γ-glycidyl ether trimethoxysilane, and 1.1 parts by weight of nonylphenol ethoxylate carboxylate in sequence 40 parts by weight of deionized water, stirred evenly;

[0032] 2) Add 5.5 parts by weight of diethylene glycol phenyl ether, 2.6 parts by weight of methyl vinyl ketone, 0.5 parts by weight of sodium secondary alkyl sulfate, and 0.7 parts by weight of benzotriazole, and continue stirring until fully mixed Uniformly, the coating treatment solution is prepared;

[0033] 3) Put the nickel-chromium alloy main body into the coating treatment solution for...

Embodiment 3

[0035] The electric heating element is made of nickel-chromium high-resistance electric heating alloy material, which includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0036] 1) Put 2 parts by weight of sodium hydroxide, 3.3 parts by weight of aminotrimethylene phosphonic acid, 2.1 parts by weight of γ-glycidyl ether trimethoxysilane, and 1.1 parts by weight of nonylphenol ethoxylate carboxylate in sequence 40 parts by weight of deionized water, stirred evenly;

[0037] 2) Add 5.5 parts by weight of diethylene glycol phenyl ether, 2.6 parts by weight of methyl vinyl ketone, 0.5 parts by weight of sodium secondary alkyl sulfate, and 0.7 parts by weight of benzotriazole, and continue stirring until fully mixed Uniformly, the coating treatment solution is prepared;

[0038] 3) Put the nickel-chromium alloy main body into the coating treatment solution fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-resistance nickel-chromium electrothermal alloy material for electric heating elements. The alloy material comprises a nickel-chromium alloy main body, wherein the nickel-chromium alloy main body is subjected to film coating treatment; the film coating treatment comprises the following steps: (1) sequentially adding 1-2 parts (by weight) of sodium hydroxide, 3.3 parts (by weight) of amino trimethylene phosphonic acid, 2.1 parts (by weight) of gamma-epoxy propyl ether trimethoxysilane and 1.1 parts (by weight) of nonylphenol ethyl oxide carboxylate into 40 parts (by weight) of deionized water, and carrying out uniform stirring; (2) then, sequentially adding 5.5 parts (by weight) of diethylene glycol phenyl ether, 2.6 parts (by weight) of methyl vinyl ketone, 0.5 part (by weight) of secondary sodium alkyl sulfate and 0.7 part (by weight) of benzotriazole e into the solution, and continuing to carry out stirring until thorough and uniform mixing is achieved, so as to prepare a film coating treatment solution; (3) dipping the nickel-chromium alloy main body in the film coating treatment solution, taking out the nickel-chromium alloy main body, and then, baking the nickel-chromium alloy main body. According to the high-resistance nickel-chromium electrothermal alloy material for the electric heating elements, disclosed by the invention, the surface of the nickel-chromium alloy main body is coated with a protective film, so that the performance is good, and the surface smoothness is good.

Description

technical field [0001] The invention relates to a nickel-chromium high-resistance electric heating alloy material for an electric heating element. Background technique [0002] Existing electric heating elements use nickel-chromium high-resistance electric heating alloy materials. The wear resistance, oxidation resistance, corrosion resistance, rust resistance, and weather resistance of the nickel-chromium alloy main body need to be improved, and the surface finish is not ideal. Contents of the invention [0003] The object of the present invention is to provide a nickel-chromium high-resistance electric heating alloy material for electric heating elements. Corrosion, rust resistance, weather resistance, and good surface finish. [0004] In order to achieve the above object, the technical solution of the present invention is to design a nickel-chromium high-resistance electric heating alloy material for electric heating elements, which includes a nickel-chromium alloy mai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/64
CPCC23C22/64C23C2222/20
Inventor 陈俊达
Owner CHANGSHU MEILI ALLOY MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap