Functionalized cable material having thermal stability enhanced through compounding graphene oxide and polyimide

A technology of polyimide and graphene, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of reducing the modulus of composite materials, environmental pollution, etc., and achieve improved interfacial compatibility and good compatibility , good thermal stability

Inactive Publication Date: 2017-02-08
ANHUI ZHONGRUN CABLE GRP SHARES CO LTD
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the thermoplastic polyurethane elastomer improves the toughness of the polyvinyl chloride material, it also reduces the modulus of the composite material at the same time, and uses dioctyl phthalate as a plasticizer, and the benzene ring structure contained in it is harmful to the human body. Potentially physiologically toxic and cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A cable material with functionalized graphene oxide compounded with polyimide to enhance thermal stability, prepared from the following raw materials in parts by weight (kg): thermoplastic polyurethane elastomer 60, polyvinyl chloride 35, stearic acid 0.1, Calcium benzoate 5, mercaptan methyl tin heat stabilizer 0.8, titanate coupling agent 1310.2, epoxy soybean oil 19, barium stearate 0.4, graphene oxide 6, N, N dimethylacetamide 6, Cyclohexyl isocyanate 2, polyimide powder 3, appropriate amount of absolute ethanol.

[0015] Described a kind of functionalized graphene oxide composite polyimide enhances the cable material of thermal stability performance, is made by following specific steps:

[0016] (1) Put calcium benzoate into a high-speed mixer, heat to 100°C, add stearic acid and titanate coupling agent 131, stir at 1000 rpm for 20 minutes, and discharge for use;

[0017] (2) Add polyvinyl chloride into the high-speed mixer, add mercaptan methyl tin heat stabilize...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

Cable material discloses a functionalized cable material having thermal stability enhanced through compounding graphene oxide and polyimide, wherein the cable material is prepared from the following raw materials in parts by weight: 60-65 parts of a thermoplastic polyurethane elastomer, 35-40 parts of polyvinyl chloride, 0.1-0.12 part of stearic acid, 5-6 parts of calcium benzoate, 0.8-1 part of a mercaptan methyltin heat stabilizer, 0.2-0.3 part of a titanate coupling agent 131, 19-20 parts of epoxy soybean oil, 0.4-0.5 part of barium stearate, 6-7 parts of graphene oxide, 6-7 parts of N,N-dimethylacetamide, 2-3 parts of cyclohexyl isocyanate, 3-4 parts of a polyimide powder, and a proper amount of absolute ethyl alcohol. The composite cable material not only has good toughness and rigidity, but also has good thermal stability and excellent aging resistance; and the service life of the cable material is improved.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a cable material with functionalized graphene oxide compounded with polyimide to enhance thermal stability. Background technique [0002] Polyvinyl chloride (PVC) is characterized by high withstand voltage and insulation resistance, and has properties such as flame retardancy, oil resistance, weather resistance, and chemical resistance, but its dielectric constant and dielectric loss are large, and its cold resistance is poor. Plastic has the characteristics of low price, large usage, and excellent performance in all aspects. It is mainly used in insulation, semi-conductive shielding and sheathing of various wires and cables for wires and cables below 1kV and local communication cables. Thermoplastic polyurethane elastomers have the characteristics of plastic reprocessing and rubber elasticity, and are excellent in cold resistance, abrasion resistance and antibacterial pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L27/06C08L91/00C08L79/08C08K13/06C08K9/04C08K5/098C08K5/58C08K5/09C08K3/04H01B3/30C08J3/22
CPCC08L75/04C08J3/226C08J2375/04C08J2427/06C08K2201/014C08L2201/08C08L2203/202C08L2205/035C08L2207/04H01B3/302C08L27/06C08L91/00C08L79/08C08K13/06C08K9/04C08K5/098C08K5/58C08K5/09C08K3/04
Inventor 陆秀忠洪生华胡桂芝
Owner ANHUI ZHONGRUN CABLE GRP SHARES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap