A kind of smc reinforced and toughened material wind power generator

A wind turbine, strengthening and toughening technology, which is applied to wind turbines, wind turbine combinations, and wind turbines that are consistent with the wind direction, etc., can solve the problems of insufficient blade stiffness and toughness, low wind energy conversion rate, and large space occupation. Achieve the effects of long service life, high wind energy conversion rate and simple mechanism

Active Publication Date: 2018-09-21
朱森
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to: aim at the above-mentioned existing problems, provide a kind of strengthened and toughened SMC material wind-driven generator, solve the wind-driven generator equipment occupying a large space in the prior art, the wind energy conversion rate is low, the rigidity and toughness of the blade are insufficient, The problem of short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of smc reinforced and toughened material wind power generator
  • A kind of smc reinforced and toughened material wind power generator

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1-8

[0024] Specific embodiment 1-8: as figure 1 The structural diagram of the wind power generator provided for the embodiment 1-8, the embodiment discloses a kind of SMC reinforced and toughened material wind power generator, including the hub 1, the blade 2, the gearbox 3, the generator 4, the rotating device 5, the tower Rod 6, fixed base 7, power supply system 8, blades 2 are fixed on the hub 1, the blades 2 are three identical blades, between the blades 2 and the hub 1 is a curved surface structure with a thin middle and thick sides , the tail of the hub 1 is provided with a gearbox 3 and a generator 4 connected to the gearbox, the power supply system is located inside the fixed base 7, the generator 4 is connected to the power supply system, the hub 1 and the blades 2 are all It is made of SMC reinforced and toughened material, and the fixed base is made of rubber powder reinforced concrete material.

[0025] The preparation method of described SMC reinforced toughened mate...

specific Embodiment 9-13

[0029] Specific examples 9-13: as figure 1 The structural diagram of the wind power generator provided for the embodiment 9-13, the embodiment discloses a kind of SMC reinforced and toughened material wind power generator, including the hub 1, the blade 2, the gearbox 3, the generator 4, the rotating device 5, the tower Rod 6, fixed base 7, power supply system 8, blades 2 are fixed on the hub 1, the blades 2 are three identical blades, between the blades 2 and the hub 1 is a curved surface structure with a thin middle and thick sides , the rear part of the hub 1 is provided with a gearbox 3 and a generator 4 connected to the gearbox, the power supply system is located inside the fixed base 7, and the hub 1 and blades 2 connected to the generator 4 and the power supply system are all adopted It is made of SMC reinforced and toughened material, and the fixed base is made of rubber powder reinforced concrete material.

[0030] The preparation method of described SMC reinforced t...

specific Embodiment 14-20

[0034] Specific examples 14-20: as figure 1 The structural diagram of the wind power generator provided for Examples 14-20, the embodiment discloses a wind power generator made of SMC reinforced and toughened material, including hub 1, blade 2, gearbox 3, generator 4, rotating device 5, tower Rod 6, fixed base 7, power supply system 8, the blades 2 are three identical blades, between the blades 2 and the hub 1 is a curved surface structure with a thin middle and thick sides, and the power supply system is located in a fixed Inside the base, the hub 1 and the blade 2 are made of SMC reinforced and toughened material, and the fixed base is made of rubber powder reinforced concrete material.

[0035] The preparation method of described SMC reinforced toughened material is as follows:

[0036] Resin paste preparation: Disperse the resin matrix, initiator, inorganic filler, nanoparticles, curing agent, ultraviolet absorber, release agent, hydroquinone, and coupling agent in the di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aerogenerator made of a SMC reinforced and toughened material, belonging to the field of new energy. The aerogenerator provided by the invention mainly overcomes the problems of susceptibility to interference by environments, insufficient vane rigidity and toughness, too great weight and short service life of aerogenerators in the prior art. The aerogenerator provided by the invention comprises a wheel hub, vanes, a gear case, a generator, a rotary device, a pole, a fixed base and a power supply system, wherein the vanes are three completely identical vanes; a place between the vanes and the wheel hub is of a curved-surface structure with a thin middle part and two thick edges; the power supply system is located in the fixed base; the wheel hub and the vanes are prepared from the SMC reinforced and toughened material; and the fixed base is prepared from a rubber powder-enhanced concrete material.

Description

technical field [0001] The invention relates to the field of new energy, in particular to a wind power generator. Background technique [0002] With the development of the economy, the consumption of traditional fossil energy is increasing, which has caused environmental pollution problems such as global temperature rise and air pollution. The development and utilization of new energy is imminent. Among all new energy, wind energy is an environmental impact The advantages of small size, large natural reserves, and small investment have broad application prospects. The existing wind power generators are mainly made of wood, metal, engineering plastics, and carbon fiber materials. Among them, the service life of wood is short, and the weight of metal is too large, which leads to the loss of wind energy. The conversion rate is too low, the strength and toughness of engineering plastics are poor, the service life is short, and the cost of carbon fiber materials is too high to be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L63/00C08L67/06C08L83/04C08K13/04C08K7/06C08K3/08C08K3/26C08K3/22F03D9/25F03D1/06F03D13/20
CPCC08K3/08C08K3/22C08K3/26C08K7/06C08K13/04C08K2003/085C08K2003/0856C08K2003/2241C08K2003/265C08K2201/011C08K2201/014C08L63/00C08L67/02C08L67/06F03D1/06F05B2280/4003C08L83/04Y02E10/72
Inventor 朱森
Owner 朱森