High-crack-resistance damping coating

A damping coating, high anti-cracking technology, applied in the field of damping coatings, can solve problems such as cracking, and achieve good stone impact resistance and salt spray resistance.

Active Publication Date: 2017-02-22
郑州安邦达水性材料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention proposes a high-crack-resistant damping coating, which has good flexibility, strong impact resistance and stone impact resistance, and solves the problem that the 90° transition coating of profiles is prone to cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-crack-resistance damping coating
  • High-crack-resistance damping coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A high anti-crack damping paint, calculated by weight parts, comprising the following raw materials:

[0036] 300 parts of acrylic waterproof emulsion, 100 parts of antirust emulsion, 50 parts of plasticized acrylic emulsion, 15 parts of alcohol ester twelve, 25 parts of preservative, 5 parts of black paste, 100 parts of magnesium hydroxide, 50 parts of floating beads, 50 parts of talcum powder part and 50 parts of nano-montmorillonite / polyaniline composite powder.

[0037] Wherein, the acrylic waterproof emulsion is German BASF waterproof emulsion S 400F.

[0038] The anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd. Its solid content is 41±1%, pH is 7-7.5, glass transition temperature is 20°C, minimum film-forming temperature is 30°C, and viscosity is less than 20cps , with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good weather resistance and good corro...

Embodiment 2

[0048] A high anti-crack damping paint, calculated by weight parts, comprising the following raw materials:

[0049] 290 parts of acrylic waterproof emulsion, 95 parts of antirust emulsion, 55 parts of plasticized acrylic emulsion, 13 parts of alcohol ester twelve, 23 parts of preservative, 4 parts of black paste, 95 parts of aluminum hydroxide, 45 parts of floating beads, 45 parts of talcum powder part and 45 parts of nano-montmorillonite / polypyrrole composite powder.

[0050] Wherein, the acrylic waterproof emulsion is German BASF waterproof emulsion S 400F.

[0051] The anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd. Its solid content is 41±1%, pH is 7-7.5, glass transition temperature is 20°C, minimum film-forming temperature is 30°C, and viscosity is less than 20cps , with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good weather resistance and good corrosio...

Embodiment 3

[0060] A high anti-crack damping paint, calculated by weight parts, comprising the following raw materials:

[0061] 310 parts of acrylic waterproof emulsion, 105 parts of antirust emulsion, 45 parts of plasticized acrylic emulsion, 17 parts of alcohol ester twelve, 27 parts of preservative, 6 parts of black paste, 55 parts of aluminum hydroxide, 40 parts of magnesium hydroxide, floating beads 55 parts, 55 parts of talcum powder and 55 parts of nano-montmorillonite / polyaniline composite powder.

[0062] Wherein, the acrylic waterproof emulsion is German BASF waterproof emulsion S 400F.

[0063] The anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd. Its solid content is 41±1%, pH is 7-7.5, glass transition temperature is 20°C, minimum film-forming temperature is 30°C, and viscosity is less than 20cps , with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good weather re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-crack-resistance damping coating. The high-crack-resistance damping coating comprises the following raw materials in parts by weight: 290 to 310 parts of an acrylic acid waterproof emulsion, 95 t 105 parts of an anti-rust emulsion, 45 to 55 parts of a plasticized acrylic acid emulsion, 13 to 17 parts of a film-forming aid, 90 to 110 parts of functional fillers and 45 to 55 parts of corrosion-resistant fillers. The damping coating has high flexibility, impact resistance and high stone crash resistance, and solves the problem that the profile 90-degree transitional coating is susceptible to cracking.

Description

technical field [0001] The invention belongs to the technical field of damping coatings, and in particular relates to a highly crack-resistant damping coating. Background technique [0002] At present, there are many types of damping coatings at home and abroad, but from the solvent of the coatings, there are mainly two types: solvent-based and water-based. Most of the former contain organic solvents and asphalt, which are highly toxic, highly volatile, pollute the environment, and have poor workability, so they are rarely used now. The latter damping coating uses water as a solvent, has low toxicity, low odor, low cost, easy construction, and environmental protection, and is the first choice for damping coatings for urban rail vehicles. [0003] my country has developed and produced damping coatings since the 1960s, and has formed a relatively mature development and production system so far, among which was authorized on May 13, 1998: Patent No. CN1039342C, the invention n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D133/08C09D5/08C09D7/12C08F220/18C08F212/08C08F220/14C08F220/46C08F220/06C08F4/40
CPCC08F4/40C08F220/18C08F220/1804C08K2201/011C08L2205/025C08L2205/035C09D5/08C09D7/61C09D133/00C08L33/00C08L33/08C08L79/02C08K13/04C08K3/34C08K3/346C08L79/04C08F212/08C08F220/14C08F220/46C08F220/06C08F220/1818
Inventor 孙天宝谢金彪
Owner 郑州安邦达水性材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com