Burst-resistant brown paper and making method thereof

A kind of kraft paper and burst-resistant technology, which is applied in papermaking, pulp bleaching, textiles and papermaking, etc. It can solve the problems of packaged items falling out, poor burst resistance, paper rupture, etc., and achieves extended service life, good water absorption, and improved The effect of burst resistance

Inactive Publication Date: 2017-03-22
广州市极合技术咨询有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing kraft paper has poor burst resistance, and the paper often breaks when used for packaging, causing the packaged items to fall out

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Burst-resistant brown paper and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of preparation method of break-resistant kraft paper comprises the following steps:

[0022] (1) 70 parts of coniferous bark, 60 parts of broad-leaved bark, 50 parts of waste paper, 20 parts of cotton fiber, 30 parts of sandalwood bark, 15 parts of bamboo, 26 parts of bagasse, 15 parts of wool and 30 parts of grass are mixed and pulverized, Mixture A is obtained after pulverization;

[0023] (2) Pour mixture A into a digester for cooking, the cooking temperature is 150 degrees Celsius, and the cooking time is 50 minutes;

[0024] (3) Pour the cooked mixture A into the bleaching tank, add 5 parts of aluminum sulfate to the bleaching tank, stir and mix evenly, and the soaking time of the mixture A is 90 minutes.

[0025] (4) Pour the mixed slurry obtained in step 3 into a high-concentration deslagging machine, and sieve the fibers and particles in the mixed slurry;

[0026] (5) Pour the slurry sieved in step 4, 5 parts of talcum powder, 8 parts of calcium carbona...

Embodiment 2

[0030] A kind of preparation method of break-resistant kraft paper comprises the following steps:

[0031] (1) 60 parts of coniferous bark, 50 parts of broad-leaved bark, 40 parts of waste paper, 15 parts of cotton fiber, 22.5 parts of sandalwood bark, 12.5 parts of bamboo, 22 parts of bagasse, 11.5 parts of wool and 25 parts of grass are mixed and pulverized, Mixture A is obtained after pulverization;

[0032] (2) Pour mixture A into a cooker for cooking, the cooking temperature is 125 degrees Celsius, and the cooking time is 45 minutes;

[0033] (3) Pour the cooked mixture A into the bleaching tank, add 7.5 parts of aluminum sulfate to the bleaching tank, stir and mix evenly, and the soaking time of the mixture A is 75 minutes.

[0034] (4) Pour the mixed slurry obtained in step 3 into a high-concentration deslagging machine, and sieve the fibers and particles in the mixed slurry;

[0035] (5) Pour the slurry sieved in step 4, 7.5 parts of talcum powder, 11.5 parts of calc...

Embodiment 3

[0039] A kind of preparation method of break-resistant kraft paper comprises the following steps:

[0040] (1) 50 parts of coniferous bark, 40 parts of broad-leaved bark, 30 parts of waste paper, 10 parts of cotton fiber, 15 parts of sandalwood bark, 10 parts of bamboo, 18 parts of bagasse, 8 parts of wool and 20 parts of grass are mixed and pulverized,

[0041] Mixture A is obtained after pulverization;

[0042] (2) Pour mixture A into a cooker for cooking, the cooking temperature is 100 degrees Celsius, and the cooking time is 40 minutes;

[0043] (3) Pour the cooked mixture A into the bleaching tank, add 10 parts of aluminum sulfate into the bleaching tank, stir and mix evenly, and the soaking time of the mixture A is 60 minutes.

[0044] (4) Pour the mixed slurry obtained in step 3 into a high-concentration deslagging machine, and sieve the fibers and particles in the mixed slurry;

[0045] (5) Pour the slurry screened in step 4, 10 parts of talcum powder, 15 parts of ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a burst-resistant brown paper and a making method thereof. The burst-resistant brown paper is produced from, by weight, 50-70 parts of coniferous bark, 40-60 parts of broadleaf tree bark, 30-50 parts of waste paper, 10-20 parts of cotton fibers, 15-30 parts of wingceltis bark, 10-15 parts of bamboo, 18-26 parts of bagasse, 8-15 parts of wool, 20-30 parts of grass, 5-10 parts of talcum powder, 8-15 parts of calcium carbonate, 3-5 parts of titanium dioxide, 4-10 parts of diatomite, 5-8 parts of clay, 1-5 parts of zinc borate and 5-10 parts of aluminum sulfate. The t brown paper produced in the invention has good burst resistance.

Description

technical field [0001] The invention relates to a burst-resistant kraft paper and a preparation method thereof. Background technique [0002] Kraft paper (kraftpaper), used as packaging material. The intensity is high. Usually yellowish brown. Semi-bleached or fully bleached kraft pulp is light brown, cream or white. Quantitative 80 ~ 120g / m2. The fracture length is generally above 6000m. Tear strength, work of rupture and dynamic strength are high. Mostly roll paper, but also flat paper. Using kraft softwood pulp as raw material, after beating, it is made on fourdrinier paper machine. It can be used as cement bag paper, envelope paper, glue-sealing paper, asphalt paper, cable protection paper, insulating paper, etc. [0003] Kraft paper (kraftpaper), used as packaging material. The intensity is high. Usually yellowish brown. Semi-bleached or fully bleached kraft pulp is light brown, cream or white. Quantitative 80 ~ 120g / m2. The fracture length is generally abo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H15/10D21H11/12D21C3/00D21C9/10D21D5/00D21H17/68
CPCD21H15/10D21C3/00D21C9/10D21D5/00D21H11/12D21H17/68
Inventor 吕玲
Owner 广州市极合技术咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap