Paint formula suitable for surface layer of microwave oven

A technology for microwave ovens and coatings, applied in powder coatings, epoxy resin coatings, coatings, etc., can solve problems such as inability to meet electrical spraying and surface protection, cannot meet production and living needs, poor physical properties, etc., and achieve good prospects for use , cost reduction, and the effect of wasting human resources

Inactive Publication Date: 2017-04-05
袁传江
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, its powder coating is composed of polyester resin, blocked isophor copper diisocyanate, benzoin and dibutyltin dilaurate. Its disadvantages are poor physical properties, poor covering eff

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Embodiment one:

[0014] A coating formulation suitable for the surface layer of a microwave oven, the coating formulation comprises 20% epoxy resin, 17% curing agent, 3% auxiliary agent, 7% leveling agent, 20% barium sulfate, 2% brightening agent, Titanium dioxide 18%, high-gloss wax 1%, color masterbatch 2%, charge enhancer 5%, antioxidant 4% and silicon carbide 1%, the sum of the quantities of each component is equal to 100%.

Example Embodiment

[0015] Embodiment two:

[0016] A coating formulation suitable for the surface layer of a microwave oven, the coating formulation includes 24.5% epoxy resin, 16% curing agent, 4% auxiliary agent, 7.5% leveling agent, 18% barium sulfate, 2% brightening agent, Titanium dioxide 14.5%, high-gloss wax 1%, color masterbatch 2%, charge enhancer 4%, antioxidant 5.5% and silicon carbide 1%, the sum of the quantities of each component is equal to 100%.

Example Embodiment

[0017] Embodiment three:

[0018] A coating formulation suitable for the surface layer of a microwave oven, the coating formulation comprises 29% epoxy resin, 15% curing agent, 5% auxiliary agent, 8% leveling agent, 16% barium sulfate, 2% brightening agent, Titanium dioxide 11%, high-gloss wax 1%, color masterbatch 2%, charge enhancer 3%, antioxidant 7% and silicon carbide 1%, the sum of the quantities of each component is equal to 100%.

[0019] When preparing the composite paint formula of the present invention, each component batching is prepared according to the formula, put into a mixer, fully mix for 30min at a speed of 600 rpm, then put into a dryer to dry and form a sheet, and then pass The powder coating is obtained by grinding the powder with a pulverizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a paint formula suitable for a surface layer of a microwave oven. The paint formula comprises, by weight, 20-29% of epoxy resin, 15-17% of curing agents, 3-5% of auxiliaries, 7-8% of flatting agents, 16-20% of barium sulfate, 2% of sensitizers, 11-18% of titanium dioxide, 1% of high light wax, 2% of color master, 3-5% of electric power increase agents, 4-7% of antioxidants and 1% of silicon carbide, and the weight sum of the components is equal to 100%. The paint formula has the advantages of good covering performance and low cost.

Description

technical field [0001] The invention relates to the field of powder coatings, in particular to a coating formula suitable for the surface layer of microwave ovens. Background technique [0002] Powder coating is a new type of solvent-free 100% solid powder coating. It has the characteristics of no solvent, no pollution, recyclable, environmental protection, saving energy and resources, reducing labor intensity and high mechanical strength of the coating film. In the prior art, its powder coating is composed of polyester resin, blocked isophor copper diisocyanate, benzoin and dibutyltin dilaurate. Its disadvantages are poor physical properties, poor covering effect, and easy generation of fine bubbles. Unable to meet electrical spraying and surface protection. That is, the existing powder coatings have poor coverage and cannot meet the needs of production and life. Contents of the invention [0003] The technical problem to be solved by the present invention is to overco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D7/12C09D5/03
Inventor 袁传江
Owner 袁传江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap