Degradable UV gravure embossed sand-feeling ink for gold and silver cardboard

A gold and silver card, sandy feeling technology, applied in the field of ink, can solve the problems of insufficient pattern effect and insufficient adhesion of UV gravure printing ink, so as to ensure the UV crosslinking process, improve scratch resistance and hand feeling, and reduce viscosity Effect

Active Publication Date: 2017-04-19
HUIZHOU PERFECT CHEM IND CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this UV gravure ink still has the disadvantages of insufficient adhesion and insufficient pattern effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] S1. First add 15 kg of 1,6-hexanediol diacrylate into the mixing tank, slowly add 13 kg of acrylate resin and 15 kg of epoxy soybean oil acrylate at a stirring speed of 800 rpm, add After finishing, increase the rotating speed to 1800 rpm, stir for 10 minutes until the dissolution is complete, and obtain the semi-finished product 1# for later use;

[0045] S2. Add 5 kg of sand flour, 8 kg of wax powder, 1.5 kg of silicone leveling agent, 1.5 kg of silicone defoamer to semi-finished product 1#, stir and mix evenly while adding, the stirring speed is 1600 rpm, stir 25 minutes;

[0046] S3. Then add 20 kg of isobornyl acrylate, 12 kg of active amine, 4 kg of 184 photoinitiator, and 5 kg of TPO photoinitiator, then reduce the stirring to 800 rpm, and stir for 20 minutes until the stirring is uniform and the initiator dissolves Completely, filter the package with an 80-mesh filter.

Embodiment 2

[0048]S1. First add 25 kg of 1,6-hexanediol diacrylate into the mixing tank, slowly add 10 kg of acrylate resin and 22 kg of epoxy soybean oil acrylate at a stirring speed of 900 rpm, add After finishing, increase the rotating speed to 1700 rpm, stir for 20 minutes until the dissolution is complete, and obtain the semi-finished product 1# for later use;

[0049] S2. Add 3 kg of sand flour, 5 kg of wax powder, 1 kg of silicone leveling agent, 1 kg of silicone defoamer to the semi-finished product 1#, stir and mix evenly while adding, the stirring speed is 1700 rpm, stir 20 minutes;

[0050] S3. Then add 17 kg of isobornyl acrylate, 11 kg of active amine, 2 kg of 184 photoinitiator, and 3 kg of TPO photoinitiator, then reduce the stirring to 900 rpm, and stir for 15 minutes until the stirring is uniform and the initiator dissolves Completely, filter the package with an 80-mesh filter.

Embodiment 3

[0052] S1. First add 19 kg of 1,6-hexanediol diacrylate into the mixing tank, slowly add 15 kg of acrylate resin and 25 kg of epoxy soybean oil acrylate at a stirring speed of 1000 rpm, add After finishing, increase the rotating speed to 1600 rpm, stir for 30 minutes until the dissolution is complete, and obtain the semi-finished product 1# for later use;

[0053] S2. Add 4 kg of sand flour, 7 kg of wax powder, 0.5 kg of silicone leveling agent, 0.5 kg of silicone defoamer to the semi-finished product 1#, stir and mix evenly while adding, the stirring speed is 1800 rpm, stir 15 minutes;

[0054] S3. Then add 10 kg of isobornyl acrylate, 10 kg of active amine, 3 kg of 184 photoinitiator, and 6 kg of TPO photoinitiator, then reduce the stirring to 1000 rpm, and stir for 10 minutes until the stirring is uniform and the initiator dissolves Completely, filter the package with an 80-mesh filter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ink, and in particular, relates to a degradable UV gravure embossed sand-feeling ink for a gold and silver cardboard material. The ink comprises the following components by the weight percentage: 15%-25% of epoxidized soybean oil acrylate, 10%-15% of acrylate, 15%-25% of 1,6-hexanediol diacrylate, 10%-20% of isobornyl acrylate, 2%-4% of a 184 photoinitiator, 3%-6% of a TPO photoinitiator, 8%-12% of an amine initiator, 3%-5% of sand finish powder, 5%-8% of wax powder, and 1%-3% of an auxiliary agent. The degradable UV gravure embossed sand-feeling ink for a gold and silver cardboard has no solvent and no toxic gas emissions when in use, is environmentally friendly, and has no pollution; the ink after curing has the advantages of strong pattern three-dimensional sense, good adhesion force and good fluidity, can meet the requirements of decorative inks, can be biodegraded after being discarded, meets new concepts of environmental protection, reduces environment pollution, and achieves the purpose of sustainable development.

Description

technical field [0001] The invention relates to the technical field of inks, in particular, the invention relates to a degradable UV gravure embossed letter sandy ink used on gold and silver cardboard materials. Background technique [0002] The gravure printing inks on the market are mainly solvent-based, and their components contain a large amount of organic solvents. During construction, a large amount of organic solvents will be volatilized and released into the air, causing pollution to the environment and not conducive to environmental protection, especially benzene Solvents are detrimental to the health of operators. Patents have reported UV gravure inks, and patent CN101486857 discloses a UV curing gravure ink, which uses alkali-soluble acrylate resins and modified epoxy acrylate resins as the main resin, and photoinitiators, pigments, wax powder, Prepared with diluent and auxiliary agent, the prepared UV gravure printing ink has short drying cycle, stable inking pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/101C09D11/107C09D11/03
CPCC09D11/03C09D11/101C09D11/107
Inventor 何建军柏跃松
Owner HUIZHOU PERFECT CHEM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap