Environment-friendly compound admixture for architectural decoration engineering and preparation method thereof

A technology for building decoration engineering and composite admixture, which is applied in the field of environment-friendly composite admixture for building decoration engineering and its preparation, can solve the problems affecting the economic benefits of iron and steel enterprises, pollute the environment, accumulation of steel slag, etc., and improve the hydration of steel slag. Reactive activity, increased reactivity, increased ability effect

Active Publication Date: 2017-04-26
SHENZHEN HONGTAO DECORATION
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, steel slag has a low utilization rate due to reasons such as difficulty in grinding and low activity, resulting in a large amount of steel slag accumulation, polluting the environment, and affecting the economic benefits of iron and steel enterprises.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly compound admixture for architectural decoration engineering and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An environment-friendly composite admixture for building decoration engineering, which is composed of the following substances in weight percentage: 20wt% of steel slag, 1wt% of hydrotalcite, 0.05wt% of material layer stabilizing substance, 0.1wt% of magnesium fluorosilicate, and 0.1wt% of reinforcing substance %, fiber 0.1wt%, nano-alumina 1wt%, and the balance being slag.

[0032] The material layer stabilizing substance refers to calcium sucrose.

[0033] The said enhancing substance refers to sodium nitrate.

[0034] The fiber is coconut palm fiber.

[0035] Preparation method: Weigh the raw materials according to the above weight percentage, crush them through a crusher until the particle size is less than 5mm; mix the raw materials and send them to a vertical mill for grinding until the specific surface area is 420m 2 / kg, obtained the environment-friendly composite admixture for architectural decoration engineering.

Embodiment 2

[0037] An environment-friendly composite admixture for building decoration engineering, which is composed of the following substances in weight percentage: 30wt% of steel slag, 5wt% of hydrotalcite, 0.3wt% of material layer stabilizing substance, 0.2wt% of magnesium fluorosilicate, and 1wt% of reinforcing substance , 0.5 wt% of fiber, 5 wt% of nano-alumina, and the balance is slag.

[0038] The material layer stabilizing material is composed of calcium sucrose, polyacrylamide, polyoxyethylene alcohol and decaglycerol in a weight ratio of 1:1:1:1.

[0039] The reinforcing substance is composed of sodium nitrate, iminodiacetic acid and aluminum sulfate in a weight ratio of 2:1:2.

[0040] The fibers are composed of sisal fibers, ramie fibers and basalt fibers in a weight ratio of 1:1:3.

[0041] Preparation method: Weigh the raw materials according to the above weight percentage, and crush them through a crusher until the particle size is less than 5mm; mix the raw materials an...

Embodiment 3

[0043] An environment-friendly composite admixture for building decoration engineering, which is composed of the following substances in weight percentage: 24wt% of steel slag, 3wt% of hydrotalcite, 0.2wt% of material layer stabilizing substance, 0.12wt% of magnesium fluorosilicate, and 0.6wt% of reinforcing substance %, fiber 0.4wt%, nano-alumina 2wt%, and the balance being slag.

[0044] The material bed stabilizing substance is composed of polyoxyethylene alcohol and pentaglycerol in a weight ratio of 1:1.

[0045] The reinforcing substance is iminodiacetic acid.

[0046] The fiber is composed of coconut palm fiber and basalt fiber in a weight ratio of 2:1, and the fiber length is 1mm-3mm.

[0047] Preparation method: Weigh the raw materials according to the above weight percentage, and crush them through a crusher until the particle size is less than 5mm; mix the raw materials and send them to a vertical mill for grinding until the specific surface area is 450m 2 / kg, ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of architectural decoration engineering, specifically to an environment-friendly compound admixture for architectural decoration engineering and a preparation method thereof, and the compound admixture comprises the following substances by weight: 20wt%-30wt% of steel slag, 1wt%-5wt% of hydrotalcite, 0.05wt%-0.3wt% of a material layer stabilizing agent, 0.1wt%-0.2wt% of magnesium fluorosilicate, 0.1wt%-1wt% of an enhancing material, 0.1wt%-0.5wt% of fiber, 1wt%-5wt% of nano-alumina and the balance slag. The environment-friendly compound admixture for architectural decoration engineering provided by the invention is good in use effects, and can comprehensively improve the concrete performance, and is also beneficial to the recycling economic construction of iron and steel enterprises, and protects the environment.

Description

technical field [0001] The invention belongs to the technical field of architectural decoration engineering, and in particular relates to an environment-friendly composite admixture for architectural decoration engineering and a preparation method thereof. [0002] technical background [0003] While the rapid development of my country's iron and steel industry has significantly improved people's material living standards, a large amount of steel slag and slag produced in the production process have also brought great troubles to people's lives. Their stockpiles not only occupy valuable land and pollute the surrounding environment, but are also a huge waste of resources. Steel slag and slag contain a large amount of gelling minerals or glassy substances similar to cement clinker, and have better gelling activity under appropriate conditions after grinding. It has always been the main object of research on the resource utilization of industrial waste slag in cement-based mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/10C04B24/32
CPCC04B40/0039C04B2111/00017C04B18/142C04B22/06C04B24/10C04B22/126C04B22/085C04B18/248C04B14/303C04B18/141C04B24/12C04B22/148C04B24/2652C04B24/32C04B24/026C04B14/46C04B24/126C04B24/02
Inventor 董美达
Owner SHENZHEN HONGTAO DECORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap