Air entrainment-controllable polycarboxylic water reducer used for purely machine-made sand concrete, and preparation method thereof

A polycarboxylic acid-based and concrete technology, applied in the field of concrete admixtures, can solve the problems of large concrete pumping loss, poor bubble stability, poor water retention, etc. The effect of improving the slump performance

Active Publication Date: 2017-05-31
中建商品混凝土(福建)有限公司 +1
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the deficiencies in the prior art, and aims to provide an air-entraining controllable polycarboxylate water reducer for pure machine-made sand concrete and i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Air entrainment-controllable polycarboxylic water reducer used for purely machine-made sand concrete, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An air-entraining controllable polycarboxylate water reducer for pure machine-made sand concrete is prepared by the following method:

[0033] (1) The octylphenol polyoxyethylene ether monomer (CH 3 (CH 2 ) x C 6 h 4 (OC 2 h 4 ) y OH x=8, y=7) was added into the flask, the temperature was raised to 110-120°C, nitrogen was passed through the liquid, and the acrylic acid monomer (octylphenol polyoxyethylene ether monomer and acrylic acid monomer) was added into the flask The molar ratio is 1:1.1), oleum (accounting for 1% of the total amount of the two monomers), phenothiazine (accounting for 0.02% of the total amount of the two monomers) and hydroquinone (accounting for the total amount of the two monomers 0.02%), the temperature was controlled at 110-120°C, and the reaction was carried out for 4-6 hours. After the temperature was lowered to 80-85°C, sodium hydroxide solution was added while stirring to neutralize to pH=6.5-7, and the unsaturated carboxylic acid- ...

Embodiment 2

[0038] An air-entraining controllable polycarboxylate water reducer for pure machine-made sand concrete is prepared by the following method:

[0039] (1) Nonylphenol polyoxyethylene ether monomer (CH 3 (CH 2 ) x C 6 h 4 (OC 2 h 4 ) y OH x=8, y=11) was added into the flask, the temperature was raised to 110-120°C, nitrogen was passed through the liquid, stirred evenly, and then methacrylic acid monomer (nonylphenol polyoxyethylene ether monomer and methyl The molar ratio of acrylic acid monomer is 1:1.2), oleum (accounting for 2% of the total amount of the two monomers), phenothiazine (accounting for 0.05% of the total amount of monomers) and hydroquinone (accounting for the total amount of monomers 0.05%), the temperature was controlled at 110-120°C, and the reaction was carried out for 4-6 hours. After the temperature was lowered to 80-85°C, sodium hydroxide solution was added while stirring to neutralize to pH=6.5-7 to obtain unsaturated carboxylic acid- Alkylphenol po...

Embodiment 3

[0044] An air-entraining controllable polycarboxylate water reducer for pure machine-made sand concrete is prepared by the following method:

[0045] (1) Nonylphenol polyoxyethylene ether monomer (CH 3 (CH 2 ) x C 6 h 4 (OC 2 h 4 ) y OH x=8, y=9) into the flask, heated up to 110-120°C, passed nitrogen under the liquid, stirred evenly, and then added acrylic acid monomer (the mixture of nonylphenol polyoxyethylene ether monomer and acrylic acid monomer) into the flask The molar ratio is 1:1.15), oleum (accounting for 1.5% of the total amount of the two monomers), phenothiazine (accounting for 0.04% of the total amount of the two monomers) and hydroquinone (accounting for the total amount of the two monomers 0.04%), the temperature was controlled at 110-120°C, and the reaction was carried out for 4-6 hours. After the temperature was lowered to 80-85°C, sodium hydroxide solution was added while stirring to neutralize to pH=6.5-7, and the unsaturated carboxylic acid- Alkyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fineness modulusaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of concrete additives, and concretely relates to an air entrainment-controllable polycarboxylic water reducer used for purely machine-made sand concrete, and a preparation method thereof. The preparation method comprises the following steps: carrying out an esterification reaction on an alkylphenol polyoxyethylene monomer and an unsaturated carboxylic acid to generate an unsaturated carboxylic acid-alkylphenol polyoxyethylene esterification product monomer, carrying out an aqueous solution copolymerization reaction on the unsaturated carboxylic acid-alkylphenol polyoxyethylene esterification product monomer, an unsaturated polyether monomer and an unsaturated sulfonic acid monomer through an oxidation-reduction initiation system, and adding a proper amount of a molecular weight control agent to control the molecular weight in order to obtain the air entrainment-controllable polycarboxylic water reducer. The water reducer prepared in the invention has the advantages of high water reduction rate, good adaptability, small bubble diameters, stable sealing property and controllable air entrainment when applied to the purely machine-made sand concrete, and well solves the problems of difficult air entrainment, poor bubble stability and large concrete pumping loss of the purely machine-made sand concrete.

Description

technical field [0001] The invention belongs to the field of concrete admixtures, in particular to an air-entraining controllable polycarboxylate water reducer for pure machine-made sand concrete and a preparation method thereof. Background technique [0002] Polycarboxylate water reducer is widely used in construction projects due to its strong molecular structure designability, simple production process, high water reducing rate, good slump retention performance, strong adaptability to other materials, and green and pollution-free production process. It has been widely used and replaced the traditional naphthalene-based water reducer to become a type of admixture with the largest amount of engineering use, the highest technical content, and the most significant economic and environmental benefits. As a surfactant, the polycarboxylate water reducer itself has a certain air-entraining performance, but because of the large size and poor stability of the air bubbles it introdu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F283/06C08F220/06C08F228/02C08F212/14C04B24/16C04B103/30
CPCC04B24/165C04B2103/302C08F283/065C08F220/06C08F228/02C08F212/14
Inventor 张恒春吕振华季锡贤纪晓辉唐方宇马路张超关涌
Owner 中建商品混凝土(福建)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap