PVC (polyvinyl chloride)-used bi-component waterborne coating as well as preparation method and application thereof

A water-based paint, two-component technology, applied in the field of paint, to achieve the effect of simple construction and excellent adhesion

Inactive Publication Date: 2017-05-31
CHENGDU ZHANCHEN PAINT
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with oil-based products at this stage, there are still some deficiencies. As a product applied to PVC, the oil-based system is already a very mature product due to its own advantages. This invention attempts to integrate the requirements of both environmental protection and performance. Develop a water-based product for PVC

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A two-component water-based coating for PVC, consisting of a main agent and a curing agent, the curing agent is a water-based polyurethane curing agent, and the main agent is composed of the following raw materials in terms of mass percentage: 54% water-based hydroxyacrylate, 8 % water-based vinyl resin, 0.3% defoamer 1, 0.4% defoamer 2, 0.5% dispersant, 0.3% lubricant, 0.2% leveling agent, 20% titanium dioxide, 0.5% Rheological additive 1, 0.3% rheological additive 2, 0.2% coalescent additive 1, 4% coalescent additive 2, 2% coalescent additive 3, 0.2% pH regulator, The remainder is water;

[0024] Preparation:

[0025] S1. Add the rheological additive, defoamer, and dispersant to the water in turn, stir for 5 minutes at a speed of 300-500 rpm, and mix well;

[0026] S2. Then add titanium dioxide at a rotating speed of 100-200rpm, stir for 15min at a rotating speed of 800-1200rpm, mix evenly, and then sand mill to a fineness≤20 microns;

[0027] S3. Then add water-ba...

Embodiment 2

[0029] A two-component water-based coating for PVC, consisting of a main agent and a curing agent, the curing agent is a water-based polyurethane curing agent, and the main agent is composed of the following raw materials in terms of mass percentage: 46% water-based hydroxyacrylate, 15% % water-based vinyl resin, 0.3% defoamer 1, 0.4% defoamer 2, 0.5% dispersant, 0.3% lubricant, 0.2% leveling agent, 20% titanium dioxide, 0.5% Rheological additive 1, 0.3% rheological additive 2, 0.2% coalescent additive 1, 4% coalescent additive 2, 2% coalescent additive 3, 0.2% pH regulator, The remainder is water;

Embodiment 3

[0031] A two-component water-based paint for PVC, consisting of a main agent and a curing agent, the curing agent is a water-based polyurethane curing agent, and the main agent is composed of the following raw materials in terms of mass percentage: 40% water-based hydroxyacrylate, 18 % water-based vinyl resin, 0.2% defoamer 1, 0.3% defoamer 2, 0.6% dispersant, 0.2% lubricant, 0.3% leveling agent, 25% titanium dioxide, 1% Rheological additive 1, 0.2% rheological additive 2, 0.1% coalescent additive 1, 5% coalescent additive 2, 2.5% coalescent additive 3, 0.1% pH regulator, The remainder is water;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of coating and particularly relates to PVC (polyvinyl chloride)-used bi-component waterborne coating as well as a preparation method and application thereof. The PVC-used bi-component waterborne coating comprises a main agent and a curing agent, wherein the curing agent is a waterborne polyurethane curing agent; the main agent comprises the following raw materials by mass percentage: 40-60% of waterborne hydroxyl acrylate, 8-18% of waterborne vinyl chloride-vinyl acetate resin, 0.5-1.5% of a defoaming agent, 0.2-2% of a dispersing agent, 0.2-0.5% of a lubricating agent, 0.2-0.5% of a flatting agent, 18-25% of titanium dioxide, 0.4-2% of a rheological agent, 4.1-10.5% of a coalescing agent, 0.1-0.5% of a pH regulator and the balance of water. Compared with the existing oil-based PVC product, the PVC-used bi-component waterborne coating conforms to the environment-friendly requirement, is simple in construction, is directly sprayed on most PVC substrates after raw materials are configured in construction proportion and still has excellent adhesion under a condition of no polishing.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a two-component water-based coating for PVC and its preparation method and application. Background technique [0002] With the continuous development of the furniture industry, more and more non-wood materials are used in furniture, such as styrofoam, PVC materials, etc. On the one hand, considering the cost factor, on the other hand, its plasticity and decoration are relatively low. Wood is better. The characteristics of water-based woodware itself, such as low odor, low VOC emission and environmental protection, will make this kind of products a trend in future development. However, compared with oil-based products at this stage, there are still some deficiencies. As a product applied to PVC, the oil-based system is already a very mature product due to its own advantages. This invention attempts to integrate the requirements of both environmental protection and performance. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D127/06C09D7/12
CPCC09D175/04C08K2201/014C08L2205/035C09D7/63C08L27/06C08K13/02C08K5/103C08K5/06
Inventor 刘智勇陈寿生
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com