Attapulgite particles for purifying air and preparation method thereof

A technology for attapulgite and air purification, applied in chemical instruments and methods, botanical equipment and methods, chemicals for biological control, etc. Full sex and strong adhesion

Inactive Publication Date: 2017-06-20
MINGGUANG GUOXING ATTAPULGITE CLAY
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the acidic substance itself is corrosive and dangerous, and has no visualization function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An attapulgite particle for air purification, comprising the following raw materials: 130 parts of attapulgite, 60 parts of solid waste fiber slurry, 10 parts of diatomite, 5 parts of nano-bentonite, modified sepiolite 5 parts, 3 parts of sodium carbonate, 3 parts of styrene-butadiene emulsion, 3 parts of camphor bark, 3 parts of ammonium molybdate, 3 parts of mugwort leaf, 3 parts of ammonium chloride, 1 part of amino resin, 1 part of carbomer, methyl citrate 1 part of ester, 1 part of xanthan gum, 1 part of acrylic acid, 1 part of octyl acrylate, 1 part of potassium persulfate, 1 part of tourmaline powder, 3 parts of pore forming agent, 3 parts of auxiliary agent and 180 parts of water;

[0036] The solid waste fiber slurry comprises the following raw materials in parts: 10 parts of organic fiber, 1 part of industrial solid waste, 1 part of 5% aqueous sodium hydroxide solution, 1 part of 8% modified starch aqueous solution and 10 parts of water.

[0037] Wherein, the ...

Embodiment 2

[0059] An attapulgite particle for air purification, comprising the following raw materials: 150 parts of attapulgite, 70 parts of solid waste fiber slurry, 13 parts of diatomite, 10 parts of nano-bentonite, modified sepiolite 10 parts, 5 parts of sodium carbonate, 5 parts of styrene-butadiene emulsion, 5 parts of camphor bark, 5 parts of ammonium molybdate, 5 parts of mugwort leaf, 5 parts of ammonium chloride, 3 parts of amino resin, 3 parts of carbomer, methyl citrate 3 parts of ester, 3 parts of xanthan gum, 3 parts of acrylic acid, 3 parts of octyl acrylate, 3 parts of potassium persulfate, 3 parts of tourmaline powder, 5 parts of pore-forming agent, 5 parts of auxiliary agent and 200 parts of water;

[0060] The solid waste fiber slurry includes the following raw materials: 15 parts of organic fiber, 4 parts of industrial solid waste, 3 parts of 5% aqueous sodium hydroxide solution, 3 parts of 8% modified starch aqueous solution and 20 parts of water.

[0061] Wherein, t...

Embodiment 3

[0083] An attapulgite particle for air purification, comprising the following raw materials: 140 parts of attapulgite, 65 parts of solid waste fiber slurry, 12 parts of diatomite, 7 parts of nano-bentonite, modified sepiolite 7 parts, 4 parts of sodium carbonate, 4 parts of styrene-butadiene emulsion, 4 parts of camphor bark, 4 parts of ammonium molybdate, 4 parts of mugwort leaf, 4 parts of ammonium chloride, 2 parts of amino resin, 2 parts of carbomer, methyl citrate 2 parts of ester, 2 parts of xanthan gum, 2 parts of acrylic acid, 2 parts of octyl acrylate, 2 parts of potassium persulfate, 2 parts of tourmaline powder, 4 parts of pore-forming agent, 4 parts of auxiliary agent and 190 parts of water;

[0084] The solid waste fiber slurry includes the following raw materials: 12 parts of organic fiber, 3 parts of industrial solid waste, 2 parts of 5% aqueous sodium hydroxide solution, 2 parts of 8% modified starch aqueous solution and 15 parts of water.

[0085] Wherein, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses attapulgite particles for purifying air and a preparation method thereof and relates to the technical field of processing of attapulgite. The attapulgite particles are prepared from the following raw materials: 130 to 150 parts of attapulgite, 60 to 70 parts of solid waste fiber pulp, 10 to 13 parts of diatomite, 5 to 10 parts of nano bentonite, 5 to 10 parts of modified sepiolite, 3 to 5 parts of sodium carbonate, 3 to 5 parts of butadiene-styrene emulsion, 3 to 5 parts of camphor tree bark, 3 to 5 parts of ammonium molybdate, 3 to 5 parts of folium artemisiae argyi, 3 to 5 parts of ammonium chloride, 1 to 3 parts of amino resin, 1 to 3 parts of Carbomer, 1 to 3 parts of methyl citrate, 1 to 3 parts of xanthan gum, 1 to 3 parts of acrylic acid, 1 to 3 parts of octyl acrylate, 1 to 3 parts of potassium persulfate, 1 to 3 parts of tourmaline powder, 3 to 5 parts of a pore forming agent, 3 to 5 parts of an auxiliary agent and 180 to 200 parts of water. The attapulgite particles disclosed by the invention are used as an ammonia-removing adsorption material for purifying air and have a good adsorption effect.

Description

technical field [0001] The invention relates to the technical field of attapulgite processing, in particular to attapulgite particles used for air purification and a preparation method thereof. Background technique [0002] Ammonia is a colorless gas with a pungent and pungent odor, and is one of the common pollutants in buildings. It mainly comes from concrete building materials, furniture, decoration viscose materials, etc. As these substances change with the ambient temperature and humidity, ammonia gas is slowly released to pollute the indoor environment. Ammonia is irritating and corrosive to the skin and mucous membranes, and high concentrations can cause serious consequences. The national standard indoor air quality standard GB / T18883-2002 stipulates that the maximum allowable concentration of ammonia in the indoor air is 0.20 mg / m3. [0003] At present, there are mainly two types of ammonia removal products in indoor environmental pollution control products: one is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/12B01J20/30B01D53/02A01N65/24A01N61/00A01N59/06A01N59/00A01N59/16A01N37/36A01N37/06A01P1/00A01P3/00
CPCB01J20/12A01N37/06A01N37/36A01N59/00A01N59/06A01N59/16A01N61/00A01N65/00A01N65/24B01D53/02B01D2257/406B01D2258/06B01J20/14A01N2300/00
Inventor 李振国
Owner MINGGUANG GUOXING ATTAPULGITE CLAY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap