High-transparency wear-resistant corrosion-resistant microcrystalline glass and preparation method thereof

A glass-ceramic and high-transparency technology, which is applied in glass manufacturing equipment, glass pressing, glass molding, etc., can solve the problem of low wear resistance, glass-ceramic is not suitable for large-scale paving on the ground, and glass-ceramic is easy to be damaged. Scratches and other problems can be achieved to improve the overall performance, increase the luminous intensity, and promote the effect of crystallization

Inactive Publication Date: 2017-06-30
合肥红蔻健康管理有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high gloss on the surface of glass-ceramic, it is easier to show scratches than polished tiles, and the Mohs hardness of glass-ceramic can only reach level 6, so glass-ceramic is easy to be scratched and wear-resistant. Low, this shortcoming limits the application of glass-ceramic to a great extent, for example, ordinary glass-ceramic is not suitable for paving the ground in a large area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A high-transparency wear-resistant and corrosion-resistant glass-ceramics, according to the chemical composition of the final product, its composition is: SiO 2 : 35%, GeO 2 : 25%, FeO: 15%, CaO: 12.09%, MgO: 4%, Al 2 o 3 : 1%, Li 2 O: 2%, BaO: 0.5%, Y 2 o 3 :0.01%, Sb 2 o 3 :0.3%, K 2 O: 1%, NaO: 1%, InF 3 : 0.1%, TFe: 3%.

[0025] The preparation method of the high-transparency wear-resistant and corrosion-resistant glass-ceramics, the specific steps are as follows:

[0026] (1) carry out batching according to above-mentioned percentage by weight;

[0027] (2) Place the raw materials of the prepared high-transparency, wear-resistant and corrosion-resistant glass-ceramics in a high-energy ball mill for ball milling and mixing for 1 hour;

[0028] (3) Put the powder obtained by the ball milling into a corundum jar and wet mix for 1 hour to make a slurry, then dry the slurry with a rotary evaporator to make a mixture;

[0029] (4) Put the mixture into the man...

Embodiment 2

[0035] A high-transparency wear-resistant and corrosion-resistant glass-ceramics, according to the chemical composition of the final product, its composition is: SiO 2 : 35%, GeO 2 : 25%, FeO: 12.78%, CaO: 12%, MgO: 4.5%, Al 2 o 3 : 1.2%, Li 2 O: 2.5%, BaO: 0.6%, Y 2 o 3 :0.02%, Sb 2 o 3 :0.35%, K 2 O: 1.2%, NaO: 1.2%, InF 3 : 0.15%, TFe: 3.5%.

[0036] The preparation method of the high-transparency wear-resistant and corrosion-resistant glass-ceramics, the specific steps are as follows:

[0037] (1) carry out batching according to above-mentioned percentage by weight;

[0038] (2) Place the raw materials of the prepared high-transparency, wear-resistant and corrosion-resistant glass-ceramics in a high-energy ball mill for ball milling and mixing for 1 hour;

[0039] (3) Put the powder obtained by the ball milling into a corundum tank and wet mix for 1.2 hours to make a slurry, then dry the slurry with a rotary evaporator to make a mixture;

[0040] (4) Put the mixt...

Embodiment 3

[0046] A high-transparency wear-resistant and corrosion-resistant glass-ceramics, according to the chemical composition of the final product, its composition is: SiO 2 : 35%, GeO 2 : 20%, FeO: 12%, CaO: 15%, MgO: 5%, Al 2 o 3 : 1.57%, Li 2 O: 3%, BaO: 0.8%, Y 2 o 3 :0.03%, Sb 2 o 3 :0.4%, K 2 O: 1.5%, NaO: 1.5%, InF 3 : 0.2%, TFe: 4%.

[0047] The preparation method of the high-transparency wear-resistant and corrosion-resistant glass-ceramics, the specific steps are as follows:

[0048] (1) carry out batching according to above-mentioned percentage by weight;

[0049] (2) Place the raw materials of the prepared high-transparency, wear-resistant and corrosion-resistant glass-ceramics in a high-energy ball mill for ball milling and mixing for 2 hours;

[0050] (3) Put the powder obtained by the ball milling into a corundum jar and wet mix for 1.5 hours to make a slurry, then dry the slurry with a rotary evaporator to make a mixture;

[0051] (4) Put the mixture into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-transparency wear-resistant corrosion-resistant microcrystalline glass and a preparation method thereof. The high-transparency wear-resistant corrosion-resistant microcrystalline glass comprises the following chemical composition: 25-35% of SiO2, 15-25% of GeO2, 10-15% of FeO, 10-20% of CaO, 4-6% of MgO, 1-2% of Al2O3, 2-4% of Li2O, 0.5-1% of BaO, 0.01-0.05% of Y2O3, 0.3-0.5% of Sb2O3, 1-2% of K2O, 1-2% of NaO, 0.1-0.3% of InF3, and 3-5% of TFe. The microcrystalline glass has the advantages of soft and crystal luster, compactness, and uniform tone, after adding Li2O and InF3, crystallization of the microcrystalline glass is promoted, integral performance of the microcrystalline glass is increased, wear-resistant corrosion-resistant performances are strong, compared with the matrix glass, the luminous intensity is obviously increased, and the microcrystalline glass is suitable for active optical materials in the fields of optical communication, display and storage.

Description

technical field [0001] The invention relates to a glass-ceramic, in particular to a high-transparency wear-resistant and corrosion-resistant glass-ceramic and a preparation method thereof. Background technique [0002] Glass-ceramics refers to the basic glass of specific components, a type of composite material containing a large number of crystalline phases and glass phases, which has glass properties and ceramic properties, and is prepared by controlling crystallization during the heating process. Since its inception, glass-ceramic has been favored by many scientific researchers because of its adjustable composition and designable functions. The distribution of the glass phase and the crystalline phase varies with their ratio: when the proportion of the glass phase is large, the glass phase is a continuous matrix, and the crystal phase is evenly distributed in it; when the glass phase is small, the glass phase is dispersed Between the crystal grids, it is a continuous net...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/14C03B11/00C03B32/02
CPCC03C10/0009C03B11/00C03B32/02
Inventor 不公告发明人
Owner 合肥红蔻健康管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com