Paint additive and preparation method thereof

An additive and coating technology, applied in the field of coatings, can solve the problems that architectural coatings are not ideal, affect people's health, and are not environmentally friendly, and achieve the effects of saving the emulsification production process, absorbing toxic volatile components, and reducing raw material consumption and raw material costs.

Inactive Publication Date: 2017-06-30
合肥天沃能源科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In people's living environment, the use of coatings is essential, and the performance of coatings plays a vital role in the living environment. Therefore, people's requirements for coatings are getting higher and higher, especially in the hope of obtaining functions with multiple properties. Sexual coatings, the existing coatings, the function is relatively single
Indoor air is usually purified in daily life. Common purification methods usually use purifiers, humidifiers and other equipment, or plant indoor plants, or use coatings with specific functions. Most of them are chemical components, which are highly toxic and affect people’s health. Easy to pollute the environment
[0004] At present, there are many kinds of architectural coatings sold in the current market in our country, but with the continuous development of science and technology, people have put forward higher requirements for building materials. In the fields of energy saving, environmental protection, fire prevention, heat preservation, etc., it is impossible to fully meet various needs.
Most of the interior and exterior wall architectural coatings generally do not have environmental protection and other functions. Therefore, architectural coatings and their additives with environmental protection functions are one of the technical issues that are urgently needed to be improved in the construction industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of paint additive and preparation method of the preferred embodiment of the present invention;

[0028] The paint additive is prepared from the following raw materials in parts by weight:

[0029] Paste attapulgite clay 26 kg;

[0030] Nano titanium dioxide 8 kg;

[0031] Nano calcium carbonate 12 kg;

[0032] 8 kg of white carbon black;

[0033] Shale diatomite 12 kg;

[0034] 10 kg cloves;

[0035] mint 15 kg;

[0036] 8 kg rosemary;

[0037] Artemisia argyi 11 kg;

[0038] hibiscus 6 kg;

[0039] licorice 5 kg;

[0040] Grapefruit peel 10 kg.

[0041] The paste-like attapulgite clay is a mixture obtained by mixing natural attapulgite clay with water after purification and modification.

[0042] The present invention also relates to a method for preparing paint additives, comprising the steps of:

[0043] (1) Weigh the natural attapulgite clay, crush it to a particle size of 100-200 mesh, then add it to a container, add water 16 times the weight of ...

Embodiment 2

[0050] A kind of paint additive and preparation method of the preferred embodiment of the present invention;

[0051] The paint additive is prepared from the following raw materials in kilograms by weight:

[0052] Paste attapulgite clay 20 kg;

[0053] Nano titanium dioxide 5 kg;

[0054] Nano calcium carbonate 10 kg;

[0055] White carbon black 5 kg;

[0056] Shale diatomaceous earth 5 kg;

[0057] Cloves 8 kg;

[0058] mint 10 kg;

[0059] 3 kg rosemary;

[0060] Artemisia argyi 5 kg;

[0061] Hibiscus 3 kg;

[0062] licorice 1 kg;

[0063] Grapefruit peel 5 kg.

[0064] The paste-like attapulgite clay is a mixture obtained by mixing natural attapulgite clay with water after purification and modification.

[0065] The present invention also relates to a method for preparing paint additives, comprising the steps of:

[0066] (1) Weigh the natural attapulgite clay, crush it to a particle size of 100-200 mesh, then add it to a container, add water 10 times the weight...

Embodiment 3

[0073] A kind of paint additive and preparation method of the preferred embodiment of the present invention;

[0074] The paint additive is prepared from the following raw materials in kilograms by weight:

[0075] Paste attapulgite clay 30 kg;

[0076] Nano titanium dioxide 10 kg;

[0077] Nano calcium carbonate 20 kg;

[0078] White carbon black 10 kg;

[0079] Shale diatomite 15 kg;

[0080] 15 kg cloves;

[0081] mint 20 kg;

[0082] 12 kg rosemary;

[0083] Artemisia argyi 15 kg;

[0084] Hibiscus 8 kg;

[0085] licorice 6 kg;

[0086] Grapefruit peel 12 kg.

[0087] The paste-like attapulgite clay is a mixture obtained by mixing natural attapulgite clay with water after purification and modification.

[0088] The present invention also relates to a method for preparing paint additives, comprising the steps of:

[0089] (1) Weigh the natural attapulgite clay, crush it to a particle size of 100-200 mesh, then add it to a container, add water 20 times the weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating additive and a preparation method thereof. The coating additive comprises the following components: paste-like attapulgite clay, nano-titanium dioxide, nano-calcium carbonate, white carbon black, shale diatomite, clove, mint, mint Rosemary, mugwort, hibiscus, licorice, grapefruit peel. The preparation method comprises: firstly preparing paste-like attapulgite clay; weighing Chinese herbal medicine components, pulverizing and mixing to obtain mixture a1; weighing paste-like attapulgite clay and placing it in a reaction vessel, adding mixture a1, stirring and reacting for 1-2 hours, and ultrasonically To obtain mixture a2; weigh nano-titanium dioxide, nano-calcium carbonate, white carbon black, and shale diatomaceous earth, grind them in a ball mill for 0.5-1.5 hours, add mixture a2 and continue grinding for 0.5-1 hour, and then dry. The additive in the invention can make the coating have good waterproof performance, adsorption performance, anti-mildew and bactericidal performance and other multi-functionality, and also has uniform coating and good mechanical strength, and has good application value.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a coating additive and a preparation method. Background technique [0002] At present, coatings have been involved in various fields and are closely related to people's lives. Coating refers to a type of film material that is applied on the surface of an object to form protection, decoration and other special functions. It mainly includes film-forming base materials, pigments, fillers, solvents, and additives. Coatings can be divided into water-based coatings and organic solvent-based coatings according to the solvent, and coatings can be divided into organic coatings and inorganic coatings according to the film-forming base material. [0003] With the development of society and the improvement of living standards, the global environment is deteriorating day by day, and people's awareness of environmental protection and health is gradually increasing, and the requirements for t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D7/12
CPCC09D5/14C08K3/346C08K3/36C08K5/0058C08K13/06C08K2003/2241C08K2003/265C08K2201/011C09D7/61C09D7/62C09D7/63
Inventor 魏芳芳
Owner 合肥天沃能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products