Silicone rubber composition and preparation method thereof
A technology of silicone rubber composition and methyl vinyl silicone raw rubber, which is applied in the field of silicone rubber composition and its preparation, can solve the problems of not being resistant to ozone, difficult to protect materials, low toughness, etc., and achieve good weather resistance, good The effect of the shielding effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1
[0027] The silicone rubber composition of the present invention includes the following components by weight: 100 parts of methyl vinyl silicone rubber; 25-60 parts of reinforcing filler; 100-400 parts of X-ray absorber; 2-20 parts of treatment agent; 0.2 to 3 parts of crosslinking agent. In this embodiment, the silicone rubber composition uses 100 parts of methyl vinyl silicone rubber, 60 parts of reinforcing filler, 100 parts of X-ray absorber, 2 parts of treatment agent and 3 parts of crosslinking agent. composition.
[0028] Wherein, the molecular weight of the methyl vinyl silicone rubber is 200,000 to 800,000, and the vinyl content is 0.03% to 5%, and the methyl vinyl silicone rubber is used as the base material of the silicone rubber composition. In this embodiment, the molecular weight of the methyl vinyl silicone rubber is 400,000, and the vinyl content is 1.5%.
[0029] The reinforcing filler is one or more of silica powder, precipitation method white c...
Example Embodiment
[0034] Example 2
[0035] This embodiment is basically the same as embodiment 1, but the difference is that the silicone rubber composition uses 100 parts of methyl vinyl silicone rubber, 50 parts of reinforcing filler, 180 parts of X-ray absorber, 8 parts of The treatment agent and 2.3 parts of crosslinking agent. Wherein, the molecular weight of the methyl vinyl silicone rubber is 200,000, and the vinyl content is 3%. The reinforcing filler is a composition composed of fine silicon powder, aluminum hydroxide, calcium carbonate and diatomaceous earth, and the X-ray absorber is a composition composed of zinc oxide, neodymium oxide, praseodymium oxide, and barium sulfate, The treatment agent is realized by dimethyldiethoxy silane, and the crosslinking agent is realized by benzoyl peroxide and 2,4-dichlorobenzoyl peroxide.
[0036] When preparing the silicone rubber composition of the present invention, in the process of kneading, the kneading is performed at room temperature for 1...
Example Embodiment
[0037] Example 3
[0038] This example is basically the same as Example 1, but the difference is that the silicone rubber composition uses 100 parts of methyl vinyl silicone rubber, 40 parts of reinforcing filler, 260 parts of X-ray absorber, 12 parts of The treatment agent and 1.5 parts of crosslinking agent. Wherein, the molecular weight of the methyl vinyl silicone rubber is 500,000, and the vinyl content is 0.5%. The reinforcing filler is kaolin, the X-ray absorber is molybdenum disulfide, and the treatment agent is composed of hexamethyldisilazane, diphenylsiliconediol and dimethyldimethoxysilane In the composition, the crosslinking agent is a composition composed of tert-butyl peroxybenzoate, di-tert-butyl peroxide and dicumyl peroxide.
[0039] When preparing the silicone rubber composition of the present invention, during the kneading process, the kneading is first at room temperature for 2 hours, and then heated to 190°C and kneaded for 1 hour.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap