Synthetic ester for rolling oil, silicon steel rolling oil comprising synthetic ester and application

A technology for rolling oil and synthesizing ester, applied in the field of silicon steel rolling oil, can solve the problems of poor concentration response, dirty rolling mill, bad plate shape, etc., and achieve the effect of prolonging service life, good concentration response and improving permeability

Active Publication Date: 2017-08-11
QUAKER CHEM CHINA
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing lubricating oils generally have poor high temperature resistance, on-site aging and slick oil, poor concentration response, and severe smoke during warm rolling; at the same time, insufficient lubricity, prone to strip breakage and poor shape, and dirty rolling mills are also common problems in silicon steel rolling. main problems faced by the system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic ester for rolling oil, silicon steel rolling oil comprising synthetic ester and application
  • Synthetic ester for rolling oil, silicon steel rolling oil comprising synthetic ester and application
  • Synthetic ester for rolling oil, silicon steel rolling oil comprising synthetic ester and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～16

[0092] A rolling oil, comprising the following components by weight:

[0093] Base oil 93

[0094] Antioxidant BHT 0.5

[0095] Benzotriazole rust inhibitor 3

[0096] Ammonium phosphate extreme pressure agent 1.5

[0097] Emulsifier 1

[0098] Diethanolamine 1;

[0099] Wherein, the emulsifier is the compound mixture of C14 fatty alcohol polyoxyethylene ether and EO / PO block high molecular polymer; the base oil is the base oil preparation examples 1-16.

[0100] Comparative Example 1

[0101] The only difference from the base oil preparation example is that the base oil is the base oil provided in the base oil preparation comparative example 1.

Embodiment 17

[0151] A rolling oil, comprising the following components by weight:

[0152] Base oil 90

[0153] Antioxidant BHT 1

[0154] Benzotriazole rust inhibitor 3

[0155] Ammonium phosphate extreme pressure agent 3

[0156] Emulsifier 1

[0157] Diethanolamine 2;

[0158] The emulsifier is the compound mixture of C16 fatty alcohol polyoxyethylene ether and EO / PO block high molecular polymer; the base oil is the base oil preparation example 4.

[0159]The rolling oil of Example 17 was tested by the method of performance test. The four-ball PB value was 3089N, the RCP friction coefficient was 0.0621, the Soda friction coefficient was 0.0582; the cleanliness grade was 1; the stability test result was no oil slick; The initial volatilization temperature of the property test is 390°C; the rust resistance test shows that there is no rust on the surface; there is a slight smell and smoke; the test results are better than those of Comparative Examples 1 and 2.

Embodiment 18

[0161] A rolling oil, comprising the following components by weight:

[0162] Base oil 95

[0163] Antioxidant BHT 1

[0164] Benzotriazole rust inhibitor 2.5

[0165] Ammonium phosphate extreme pressure agent 1

[0166] Emulsifier 0.5

[0167] Diethanolamine 2;

[0168] The emulsifier is the compound mixture of C16 fatty alcohol polyoxyethylene ether and EO / PO block high molecular polymer; the base oil is the base oil preparation example 4.

[0169] The rolling oil of Example 18 was tested by the method of performance test. The four-ball PB value was 3089N, the RCP friction coefficient was 0.0611, the Soda friction coefficient was 0.0585; the cleanliness grade was 1; the stability test result was no oil slick; The initial volatilization temperature of the property test is 395°C; the rust resistance test shows that there is no rust on the surface; there is a slight smell and smoke; the test results are better than those of Comparative Examples 1 and 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention relates to synthetic ester for rolling oil. The synthetic ester comprises tetrahydric acid ester which has a structure as shown in the formula (I), in the formula (I), A is substituted or unsubstitutedalkyl, and at least one of B1, B2, B3 and B4 is a group containing a polyether structure. The polyether structure is introduced in the synthetic ester for the rolling oil, the tetrahydric acid ester has properties of a nonionic emulsifier, and the synthetic ester has good permeability, self-emulsifying performance and dispersing performance. When the synthetic ester is used for the rolling oil, cleaning of a rolling machine and a plate surface is facilitated by the permeability and the dispersing performance; in a high-temperature rolling process, stability of emulsion of the rolling oil can be maintained by the self-emulsifying performance, concentration response is good, oil slick of emulsion is less, the service life of the emulsion is prolonged, oil consumption is low, and therefore, the synthetic ester is easy to manage. The synthetic ester is the tetrahydric acid ester, has high-temperature stability, cannot be decomposed easily, cannot produce a large amount of smoke, and is environmentally friendly.

Description

technical field [0001] The invention belongs to the field of rolling oil, and particularly relates to a synthetic ester for rolling oil, silicon steel rolling oil containing the same, and use thereof. Background technique [0002] Silicon steel is a ferrosilicon soft magnetic alloy with extremely low carbon content, generally containing 0.5 to 4.5% of silicon. Adding silicon can improve the resistivity and maximum magnetic permeability of iron, reduce the coercivity, core loss (iron loss) and magnetic aging, mainly used to make the iron core of various transformers, motors and generators, is the electronic, power It is an indispensable important soft magnetic alloy material in the military industry. With the increase of silicon content, the yield strength and tensile strength of silicon steel increase significantly, the elongation decreases significantly, and the hardness increases rapidly. High-grade silicon steel has high silicon content, high deformation resistance, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M145/38C10M169/04C10N40/24C10N30/04C10N30/06C10N30/08C10N30/12
CPCC10M145/38C10M169/048C10M2203/1006C10M2207/026C10M2207/2835C10M2207/401C10M2209/103C10M2209/104C10M2209/105C10M2209/108C10M2209/1095C10M2215/042C10M2215/223C10M2223/043C10N2030/04C10N2030/06C10N2030/08C10N2030/12C10N2030/24C10N2030/50C10N2030/54C10N2030/64C10N2030/72C10N2040/24C10N2040/244
Inventor 沈业文
Owner QUAKER CHEM CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap