Preparation method of compound adsorbent mixture, adsorbent particle and compound adsorbent for purifying VOCs

A composite adsorption and adsorbent technology, which is applied in the direction of chemical instruments and methods, separation methods, and other chemical processes, can solve the problems of demanding industrial equipment, cumbersome method procedures, and high cost of adsorbents, so as to improve the adsorption effect and reduce costs. , is beneficial to the effect of removal

Inactive Publication Date: 2017-09-15
钱立新
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the disadvantages of the prior art that the cost of VOCs adsorbent is relatively high, and the adsorption efficiency is poor, the method of generation is cumbersome, and the requirements for industrial equipment are relatively harsh, and a composite adsorbent mixing The preparation method of composite adsorbent for purifying material, adsorbent particles and VOCs, the composite adsorbent mixed material of the present invention has strong adsorption capacity to VOCs in the air, simple operation, low cost, thereby realizing VOCs high efficiency, low Cost reduction; further, the composite adsorbent mixed material can be granulated to obtain adsorbent particles, and further, the adsorbent particles are further heated to obtain a composite adsorbent for purifying VOCs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of compound adsorbent mixture, adsorbent particle and compound adsorbent for purifying VOCs
  • Preparation method of compound adsorbent mixture, adsorbent particle and compound adsorbent for purifying VOCs

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation method of a composite adsorbent mix material, adsorbent particles and a composite adsorbent for purifying VOCs of the present embodiment, each component of the adsorbent is composed of the following parts by mass: 30 kg of activated alumina, 40 kg of activated carbon, 15kg of iron ore powder, 10kg of pellet ore sieve, 8kg of biomass material, 2kg of magnesia laterite nickel ore, 5kg of kaolin, and 15kg of additives. The creative component distribution ratio, as well as the special particle size composition of activated alumina and activated carbon, make the adsorbent have high porosity and specific surface area. When VOCs are in contact with the adsorbent, the adsorbent can fully contact with VOCs, which is beneficial to The removal of VOCs further improves the adsorption capacity of the adsorbent while increasing the specific surface area.

[0037] It is worth noting that: the particle size of the activated alumina is composed of the following mass percen...

Embodiment 2

[0059] A preparation method of a composite adsorbent mix material, adsorbent particles and a composite adsorbent for purifying VOCs of the present embodiment, each component of the adsorbent is composed of the following parts by mass: 35 kg of activated alumina, 55 kg of activated carbon, 18kg of iron ore powder, 15kg of pellet ore sieve, 12kg of biomass material, 3kg of magnesia laterite nickel ore, 8kg of kaolin, and 20kg of additives. The creative component distribution ratio, as well as the special particle size composition of activated alumina and activated carbon, make the adsorbent have high porosity and specific surface area. When VOCs are in contact with the adsorbent, the adsorbent can fully contact with VOCs, which is beneficial to The removal of VOCs further improves the adsorption capacity of the adsorbent while increasing the specific surface area.

[0060] The preparation method of a kind of composite adsorbent particles of the present embodiment

[0061] Step ...

Embodiment 3

[0077]A preparation method of a composite adsorbent mix material, adsorbent particles and a composite adsorbent for purifying VOCs in this embodiment, each component of the adsorbent is composed of the following parts by mass: 50 kg of activated alumina, 60 kg of activated carbon, 20kg of iron ore powder, 20kg of pellets under sieve, 15kg of biomass material, 4kg of magnesia laterite nickel ore, 10kg of kaolin, and 25kg of additives. The creative component distribution ratio, as well as the special particle size composition of activated alumina and activated carbon, make the adsorbent have high porosity and specific surface area. When VOCs are in contact with the adsorbent, the adsorbent can fully contact with VOCs, which is beneficial to The removal of VOCs further improves the adsorption capacity of the adsorbent while increasing the specific surface area.

[0078] The preparation method of a kind of composite adsorbent particles of the present embodiment

[0079] Step 1: M...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a compound adsorbent mixture, an adsorbent particle and a compound adsorbent for purifying VOCs and belongs to the field of atmospheric VOCs treatment. The method comprises the steps of adding a mixture A and a mixture B to a mixer, adding water to mix and mixing evenly; and adding an additive to the mixer and mixing evenly to prepare the adsorbent mixture, wherein the mixture A comprises activated aluminum oxide, activated carbon and iron ore powder; and the mixture B comprises a pellet sieve residue, a biomass material, magnesium laterite-nickel ore and kaolin. The adsorbent has relatively high porosity and specific surface area; and when the VOCs are in contact with the adsorbent, the adsorbent can be in full contact with the VOCs, and the adsorption efficiency of the adsorbent is improved, thereby achieving high-efficiency and low-cost emission reduction of the VOCs.

Description

[0001] The patent application of the present invention is a divisional application with the application number: 2015102044174. The filing date of the original application is: 2015-04-24. The name of the invention is: a composite adsorbent for purifying VOCs in the air. technical field [0002] The invention relates to the field of VOCs treatment in the atmosphere, and more specifically, relates to a preparation method of a composite adsorbent mixing material, adsorbent particles and a composite adsorbent for purifying VOCs. Background technique [0003] VOCs usually refer to volatile organic chemicals with high vapor pressure at normal temperature and pressure, mainly including alkanes, olefins and aromatic hydrocarbons, as well as various oxygen-containing hydrocarbons, halogenated hydrocarbons, nitrogen hydrocarbons, sulfur hydrocarbons, low boiling point and more Aromatic hydrocarbons, etc., are a class of organic pollutants that are ubiquitous in the air and have a comple...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/30B01D53/04
CPCB01D53/04B01D2253/10B01D2253/102B01D2253/104B01D2253/108B01D2253/11B01D2253/112B01D2253/1122B01D2253/20B01D2257/708B01J20/02B01J20/0229B01J20/08B01J20/12B01J20/165B01J20/20B01J20/22Y02A50/20
Inventor 钱立新相冬文
Owner 钱立新
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap