A drawing powder with good lubricating effect

A kind of wire drawing powder and good technology, applied in the field of wire drawing powder, can solve the problems of temperature increase, decrease of lubricating effect, reduction of wire drawing quality, etc., and achieve the effects of low wear rate, improved wire drawing quality and good fluidity

Active Publication Date: 2020-04-17
当涂县宏宇金属炉料有限责任公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, during the wire drawing process, especially in the rapid drawing process, the temperature of the existing wire drawing powder increases and the lubricating effect decreases, which greatly reduces the quality of the wire drawing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A wire-drawing powder with a good lubricating effect, the wire-drawing powder is made by mixing calcium hydroxide, sodium hydroxide, stearic acid, vegetable oil, paraffin, activated talcum powder, and silicon dioxide-coated nano-attapulgite;

[0016] The mass ratio of the activated talc powder to the silica-coated nano-attapulgite is 8-10:1.

[0017] The preparation method of the activated talc powder is as follows: put the talc powder into a high-speed mixer, heat up and mix, wait until the temperature reaches 125-128° C., keep warm for 8 minutes, then add polyvinyl alcohol with 1.5% calcium carbonate mass, and stir for 15 minutes. Then add citric acid with 0.18% talcum powder mass, continue stirring for 20 minutes, discharge at 100°C, and cool naturally to obtain the product.

[0018] The particle size of the activated talcum powder is 500-600 mesh.

[0019] The preparation method of the silica-coated nano-attapulgite is as follows: soak the nano-attapulgite in a sod...

Embodiment 2

[0023] A wire-drawing powder with a good lubricating effect, the wire-drawing powder is made by mixing calcium hydroxide, sodium hydroxide, stearic acid, vegetable oil, paraffin, activated talcum powder, and silicon dioxide-coated nano-attapulgite;

[0024] The mass ratio of the activated talc powder to the silica-coated nano-attapulgite is 8-10:1.

[0025] The preparation method of the activated talc powder is as follows: put the talc powder into a high-speed mixer, heat up and mix, wait until the temperature reaches 125-128° C., keep warm for 8 minutes, then add polyvinyl alcohol with 1.5% calcium carbonate mass, and stir for 15 minutes. Then add citric acid with 0.18% talcum powder mass, continue stirring for 20 minutes, discharge at 100°C, and cool naturally to obtain the product.

[0026] The particle size of the activated talcum powder is 500-600 mesh.

[0027] The preparation method of the silica-coated nano-attapulgite is as follows: soak the nano-attapulgite in a sod...

Embodiment 3

[0031] A wire-drawing powder with a good lubricating effect, the wire-drawing powder is made by mixing calcium hydroxide, sodium hydroxide, stearic acid, vegetable oil, paraffin, activated talcum powder, and silicon dioxide-coated nano-attapulgite;

[0032] The mass ratio of the activated talc powder to the silica-coated nano-attapulgite is 8-10:1.

[0033] The preparation method of the activated talc powder is as follows: put the talc powder into a high-speed mixer, heat up and mix, wait until the temperature reaches 125-128° C., keep warm for 8 minutes, then add polyvinyl alcohol with 1.5% calcium carbonate mass, and stir for 15 minutes. Then add citric acid with 0.18% talcum powder mass, continue stirring for 20 minutes, discharge at 100°C, and cool naturally to obtain the product.

[0034] The particle size of the activated talcum powder is 500-600 mesh.

[0035] The preparation method of the silica-coated nano-attapulgite is as follows: soak the nano-attapulgite in a sod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses wire-drawing powder with a good lubricating effect. The wire-drawing powder is prepared from calcium hydroxide, sodium hydroxide, stearic acid, vegetable fat, paraffin, activated talcum powder and silicon dioxide cladded nano-attapulgite in a mixing mode. According to the prepared wire-drawing powder with the good lubricating effect, the mobility is good, the weight change is small after an ignition test of 500-600 DEG C, in the use process, the possibility of mutual gnawing soldering type contact between a steel wire and the contact surface of a die can be greatly reduced, thus the friction resistance can be remarkably reduced, and the good lubricating effect can still be kept under high temperature. The wire-drawing powder is low in loss rate and long in service life, and the cost is greatly reduced. Besides, by utilizing the prepared wire-drawing powder for wire-drawing lubrication, the wire-drawing quality is also improved remarkably.

Description

technical field [0001] The invention belongs to the technical field of wire drawing powder, and in particular relates to a wire drawing powder with good lubricating effect. Background technique [0002] Drawing powder, commonly known as dry "drawing lubricant", also known as "drawing lubricant powder", is usually divided into calcium-based drawing powder and Naji drawing powder. In the deformation process of steel wire cold drawing, it can play a lubricating property, greatly reduce the friction coefficient, save energy consumption, prolong the service life of the wire drawing die, and in the high-speed drawing process, the faster the drawing speed, the better the lubricating effect. When drawing low-carbon steel wire, high-carbon steel wire, special alloy steel wire, and stainless steel wire, it can make the steel wire form a lubricating film with the deformation temperature of the steel wire during the high-temperature and high-pressure drawing process to protect the finis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C9/02
CPCB21C9/02
Inventor 芮德发
Owner 当涂县宏宇金属炉料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com