Film plating liquid for automobile glass and preparation method thereof

A technology for automotive glass and coating solution, applied in coatings, wax coatings, natural resin coatings, etc., can solve the problems of low light transmittance, inability to effectively protect the glass surface, etc., to achieve increased light transmittance, good leveling, Simple preparation method

Inactive Publication Date: 2017-11-24
伊婕
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The coating solution for automotive glass in the prior art cannot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The components of the coating solution include 10 parts by weight of polyether siloxane, 5 parts of hexadecyltrimethoxysilane, 10 parts of polyoxyethylene lauryl ether, 5 parts of jasmine oil, 2 parts of nanoparticles, 3-amino 4 parts of propyltrimethoxysilane, 5 parts of fluorocarbon surfactant, 20 parts of montan wax emulsion, 8 parts of Dama resin, 2 parts of nano titanium dioxide, 1 part of silicon micropowder and 30 parts of deionized water.

[0016] The preparation method of the present embodiment comprises the following steps:

[0017] A. Mix polyether siloxane, cetyltrimethoxysilane, lauryl polyoxyethylene ether, jasmine oil, nanoparticles, and 3-aminopropyltrimethoxysilane into the reaction tank for low-temperature heating reaction , the temperature is 40°C, the time is 20min, and then slowly cooled to room temperature to obtain the mixed solution A;

[0018] B. Add 3-aminopropyltrimethoxysilane, fluorocarbon surfactant, montan wax emulsion, dama resin and dei...

Embodiment 2

[0021] The components of the coating solution include 20 parts by weight of polyether siloxane, 15 parts of hexadecyltrimethoxysilane, 25 parts of polyoxyethylene lauryl ether, 10 parts of jasmine oil, 8 parts of nanoparticles, 3-amino 12 parts of propyltrimethoxysilane, 15 parts of fluorocarbon surfactant, 40 parts of montan wax emulsion, 18 parts of Dama resin, 5 parts of nano titanium dioxide, 6 parts of silicon micropowder and 40 parts of deionized water.

[0022] The preparation method of the present embodiment comprises the following steps:

[0023] A. Mix polyether siloxane, cetyltrimethoxysilane, lauryl polyoxyethylene ether, jasmine oil, nanoparticles, and 3-aminopropyltrimethoxysilane into the reaction tank for low-temperature heating reaction , the temperature is 40°C, the time is 20min, and then slowly cooled to room temperature to obtain the mixed solution A;

[0024] B. Add 3-aminopropyltrimethoxysilane, fluorocarbon surfactant, montan wax emulsion, dama resin a...

Embodiment 3

[0027] The components of the coating solution include 12 parts of polyether siloxane, 6 parts of hexadecyltrimethoxysilane, 12 parts of polyoxyethylene lauryl ether, 6 parts of jasmine oil, 3 parts of nanoparticles, 3-amino 5 parts of propyltrimethoxysilane, 6 parts of fluorocarbon surfactant, 24 parts of montan wax emulsion, 10 parts of Dama resin, 3 parts of nano-titanium dioxide, 2 parts of silicon micropowder and 32 parts of deionized water.

[0028] The preparation method of the present embodiment comprises the following steps:

[0029] A. Mix polyether siloxane, cetyltrimethoxysilane, lauryl polyoxyethylene ether, jasmine oil, nanoparticles, and 3-aminopropyltrimethoxysilane into the reaction tank for low-temperature heating reaction , the temperature is 40°C, the time is 20min, and then slowly cooled to room temperature to obtain the mixed solution A;

[0030] B. Add 3-aminopropyltrimethoxysilane, fluorocarbon surfactant, montan wax emulsion, dama resin and deionized w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses film plating liquid for automobile glass and a preparation method thereof. The film plating liquid is prepared from the following components in parts by weight: 10 to 20 parts of polyether siloxane, 5 to 15 parts of hexadecyltrimethoxysilane, 10 to 25 parts of lauryl alcohol polyoxyethylene, 5 to 10 parts of jasmine oil, 2 to 8 parts of nanoparticles, 4 to 12 parts of 3-aminopropyl trimethoxysilane, 5 to 15 parts of a fluorocarbon surfactant, 20 to 40 parts of montan wax emulsion, 8 to 18 parts of dammar resin, 2 to 5 parts of nano titanium white, 1 to 6 parts of silicon micro-powder and 30 to 40 parts of de-ionized water. The preparation method disclosed by the invention is simple and the prepared film plating liquid can be used for improving the wearing resistance of the surface of the automobile glass; meanwhile, the light transmittance of the glass can be increased and the smooth finish is increased.

Description

technical field [0001] The invention relates to the technical field of coating liquid preparation, in particular to a coating liquid for automobile glass and a preparation method thereof. Background technique [0002] Automobile glass coating solution refers to coating an invisible hydrophobic protective film with a thickness of only a few to a dozen nanometers on the surface of the automobile glass, so that water droplets cannot form an irregular water film that interferes with people's sight. Widely used on the front and rear windshields, side windshields, and rearview mirrors of automobiles to ensure that the glass still maintains a good line of sight in rainy days. After using this product on the front windshield and rear mirror of the car, the driver's line of sight is no longer affected by the rain film, and the clarity of vision is greatly increased, which greatly improves the comfort and safety of driving in rainy conditions. [0003] The coating solution for automo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D191/06C09D171/02C09D183/12C09D193/00C09D7/12C09D7/06C03C17/00
CPCC09D191/06C03C17/009C08K2003/2241C08L2201/10C08L2205/035C08L83/12C08L71/02C08L91/00C08L93/00C08K13/02C08K5/5419C08K5/544C08K3/22C08K3/36
Inventor 伊婕
Owner 伊婕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap