Brine concrete, preparation method and construction method

A production method and concrete technology, which can be applied to coagulating pavements, buildings, roads, etc., which are laid on site, can solve the problems of inability to adapt to the use in salt lake areas, poor corrosion resistance, and low strength, and achieve reduced maintenance costs, high strength, and high strength. The effect of high hardness

Inactive Publication Date: 2017-12-26
ЦИНХАЙ СОЛТ ЛЕЙК ИНДАСТРИ ГРУП КО ЛТД
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of brine concrete to solve the problem that the existing cement concrete has poor corrosion resistance, low strength and cannot be used in the salt lake area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] Step S1 brine stirring:

[0074] The old brine is transported from the salt lake to the configuration site and mixed with fresh water to form brine with a specific gravity of 1.5.

[0075] Step S2 mixing and stirring:

[0076] a. gravel mixing

[0077] The first crushed stone with a specification of 5-10mm and the second crushed stone with a specification of 10-40mm are put into the loader at a mass ratio of 3:7 for mixing.

[0078] b. Material mixing

[0079] Put the brine formed in step S1 into the loader for mixing with lightly burned powder and medium sand according to the mass ratio of brine, lightly burned powder, medium sand and crushed stone at 1.45:1.2:3.25:4.86 to form brine concrete.

[0080] The above-mentioned brine concrete is used to construct the road according to the construction method of brine concrete.

Embodiment 2

[0082] Embodiment 2 is the same as Embodiment 1, except that in step S2b, a setting retarder is added to the loader as an auxiliary agent, and the mass ratio of the added retarder to lightly burned powder is 0.567:1.2.

Embodiment 3

[0084] Step S1 brine stirring:

[0085] The old brine is transported from the salt lake to the configuration site, and is mixed with fresh water to form brine with a specific gravity of 1.0.

[0086] Step S2 mixing and stirring:

[0087] a. Gravel mixing:

[0088] The first crushed stone with a specification of 5-10mm and the second crushed stone with a specification of 10-40mm are put into the loader at a mass ratio of 3:7 for mixing.

[0089] b. Material mixing:

[0090] Put the brine formed in step S1, lightly burned powder, medium sand, and setting retarder at a mass ratio of 1.4:1.2:3.1:0.5:4.5 for brine, lightly burned powder, medium sand, retarder, and gravel Mix in the machine to form brine concrete.

[0091] The above-mentioned brine concrete is used to construct the road according to the construction method of brine concrete.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses brine concrete, a preparation method and a construction method. The brine concrete is prepared from brine, light burning powder, medium sand and macadam, wherein the mass radio of the brine to the light burning powder to the medium sand to the macadam is (1.4 to 1.5) to 1.2 to (3.1 to 3.5) to (4.5 to 5.0). The preparation method of the brine concrete comprises the steps of S1 brine mixing and S2 mixed material mixing. The construction method of the brine concrete comprises the steps of S1 roadbed trimming; S2 filling; and S3 joint construction. The raw material of the brine concrete can be obtained by extracting large amount of waste old brine resources in a salt lake, the cost is low, the initial coagulation is quick, and the temperature in a condensation process is relatively high, so that a road can be open as early as possible. The road constructed by the brine concrete provided by the invention is high in strength, high in rigidity, has no corrosion problem and has low maintenance cost at the later stage. Furthermore, the preparation method of the brine concrete provided by the invention is simple and convenient, and the construction quality of the pavement can be effectively ensured by combining the construction method and the brine concrete.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a brine concrete, a production method and a construction method. Background technique [0002] Concrete generally refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate, mixed with water in a certain proportion, and stirred. At present, when the cement concrete produced in the market is used in the salt lake area, based on the characteristics of Portland cement and the special geographical environment of the salt lake, there are a lot of calcium hydroxide and calcium aluminate hydrate in Portland cement, which is easy to cause soft water. , acid and salt corrosion, so the use of Portland cement in the salt lake area is likely to cause high salt corrosion, which reduces the strength of the concrete. Regular maintenance is required in the later work, which increases the cost, and the Portland cement The initial setting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32E01C7/14
CPCC04B28/32C04B2111/0075E01C7/142C04B14/06C04B14/02
Inventor 李晓辉谢康民张荣祥肖学英李浩放王骏侯军王久林黄龙张志宏杨小波刘发忠张力许涛杨晓东
Owner ЦИНХАЙ СОЛТ ЛЕЙК ИНДАСТРИ ГРУП КО ЛТД
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap