Lightweight high-hardness flexible ceramic decorative material and preparation method thereof

A decorative material with high hardness technology, applied in the field of architectural decorative materials, can solve the problems of bulky decorative materials, reduce quality, and have potential safety hazards, and achieve the effects of high bonding performance, long service life, and high wear resistance

Inactive Publication Date: 2018-01-09
万卓(江苏)新材料有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There have been many studies on soft ceramics in the prior art, but there are few reports on the multifunctional and excellent mechanical properties of soft ceramic materials
In real life, many decorative materials are very heavy, such as ceramic tiles and marble. These decorative materials are processed manually, and the requirements for labor are very high when the walls are pasted, and they are easy to be damaged during processing. In the middle, it is easy to fall off the wall due to its own gravity, which poses a safety hazard
[0004] In the existing published literature, there are many studies on lightweight building materials, but there are relatively few studies on lightweight and high hardness in the field of soft porcelain. This is mainly because soft porcelain materials are relatively As far as the material is concerned, there is a characteristic of light texture, which is mainly due to the fact that the raw materials of soft porcelain contain a large amount of organic matter, which can significantly reduce the weight. Therefore, few people pay attention to the research on the light weight of soft porcelain materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight high-hardness flexible ceramic decorative material and preparation method thereof
  • Lightweight high-hardness flexible ceramic decorative material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for preparing a lightweight high-hardness soft porcelain decorative material, characterized in that it comprises the following steps:

[0025] Step (1) Preparation of surface layer powder: Take 20 parts of floating beads, 10 parts of cement, 8 parts of coupling agent, and 1 part of inorganic pigment, add them into a kneader and mix evenly to obtain a surface layer powder. The density of floating beads is 450kg / m 3 .

[0026] Step (2) Preparation of bottom layer powder: Take 10 parts of cement, 10 parts of quartz sand, 20 parts of fly ash, and 2 parts of coupling agent into a kneader and mix evenly to obtain the bottom layer powder.

[0027] Step (3) Prepare the mixed material: add the surface layer powder obtained in step (1) to 20 parts of silicon acrylic emulsion, add 10 parts of water, and stir to obtain the surface layer mixed material; the second mixed powder obtained in step (2) Add the material to 20 parts of silicon-acrylic emulsion, add 10 parts of w...

Embodiment 2

[0031] A method for preparing a lightweight high-hardness soft porcelain decorative material, characterized in that it comprises the following steps:

[0032] Step (1) Preparation of surface layer powder: Take 20 parts of floating beads, 10 parts of cement, 8 parts of coupling agent, and 1 part of inorganic pigment, add them into a kneader and mix evenly to obtain a surface layer powder.

[0033] Step (2) Preparation of bottom layer powder: Take 10 parts of cement, 10 parts of quartz sand, 20 parts of fly ash, and 2 parts of coupling agent into a kneader and mix evenly to obtain the bottom layer powder.

[0034] Step (3) Prepare the mixed material: add the surface layer powder obtained in step (1) to 20 parts of silicon acrylic emulsion, add 10 parts of water, and stir to obtain the surface layer mixed material; the second mixed powder obtained in step (2) Add the material to 20 parts of silicon-acrylic emulsion, add 10 parts of water, and stir to obtain the second bottom laye...

Embodiment 3

[0038] A method for preparing a lightweight high-hardness soft porcelain decorative material, characterized in that it comprises the following steps:

[0039] Step (1) Preparation of surface layer powder: Take 20 parts of floating beads, 5 parts of cement, 8 parts of coupling agent, and 1 part of inorganic pigment, add them into a kneader and mix them evenly to obtain a surface layer powder. The density of floating beads is 450kg / m 3 .

[0040] Step (2) Prepare bottom layer powder: Take 10 parts of cement, 10 parts of quartz sand, 10 parts of fly ash, and 2 parts of coupling agent into a kneader and mix evenly to obtain the bottom layer powder.

[0041] Step (3) Prepare the mixed material: add the surface layer powder obtained in step (1) to 20 parts of silicon acrylic emulsion, add 10 parts of water, and stir to obtain the surface layer mixed material; the second mixed powder obtained in step (2) Add the material to 20 parts of silicone acrylic emulsion, add 10 parts of wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a lightweight high-hardness flexible ceramic decorative material. The lightweight high-hardness flexible ceramic decorative material is composed of two layers, namely a surfacelayer and a bottom layer, wherein the surface layer is composed of floating beads, a coupling agent, silicone acrylic emulsion, cement and inorganic pigments; the bottom layer is composed of cement,quartz sand, silicone acrylic emulsion and fly ash. Compared with an ordinary flexible ceramic material, the flexible ceramic material prepared by the invention has the performances of lightweight andhigh hardness, wherein the mass can be reduced by about 20%, and the hardness is improved by a grade. In addition, the wear resistance and breaking strength of the flexible ceramic material preparedin the invention are similar to those of flexible ceramic materials in the prior art, so that good using time can be ensured.

Description

technical field [0001] The invention belongs to the field of building decoration materials, and relates to a preparation method of a lightweight and high-hardness soft porcelain decoration material. Background technique [0002] Soft porcelain is a new type of flexible surface decoration material, which is obtained by forming and processing water-based polymer emulsion and inorganic substances such as cement, soil, quartz sand or mineral powder. It is an ecological and environmentally friendly building material. The appearance of soft porcelain is similar to ceramics, but it lacks the cold, heavy and fragile texture of traditional ceramic materials. Low cost and convenient construction, it is suitable for architectural decoration such as exterior walls, interior walls and floors, which greatly enriches and beautifies people's living and working environments. [0003] With the development of technology, people have successively developed various and colorful soft porcelains ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/28C04B111/40
Inventor 徐实现
Owner 万卓(江苏)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com