A technology of polymer materials and remote control equipment, applied in the field of polymer materials for remote control equipment, can solve the problems of increasing product difficulty and cost, affecting product appearance, etc., and achieve the effects of reducing production difficulty, speeding up assembly and finished product time, and reducing costs

Active Publication Date: 2020-12-04
四川威亿塑胶制品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this case, it will seriously affect the appearance of the product and increase the difficulty and cost of product manufacturing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer material for remote control equipment

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0017] Specific embodiment 1: This embodiment discloses a kind of macromolecular material for remote control equipment, described macromolecular material comprises: 100 parts of PMMA macromolecular matrix, 0.2 part of iron oxide pigment toner, nano-silicon nitride 1 1 part, the particle size is 20-50nm, 1 part of copper telluride, the particle size is 1-5μm.

specific Embodiment 2

[0018] Specific embodiment 2: This embodiment discloses a polymer material for remote control equipment, and the polymer material includes in parts by weight: 100 parts of ABS polymer matrix, 2 parts of chrome yellow powder, 5 parts of nano-titanium nitride, The particle size is 20-50nm, and the particle size of 5 parts of tungsten telluride is 1-5μm.

specific Embodiment 3

[0019] Specific embodiment 3: This embodiment discloses a polymer material for remote control equipment. The polymer material includes in parts by weight: 100 parts of PP polymer matrix, 1 part of molybdenum chrome red powder, and 2 parts of nano-boron nitride , the particle size is 20-50nm, and the particle size of 2 parts of bismuth telluride is 1-5μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high polymer material for remote control equipment, belonging to the field of material modification. The high polymer material contains the following components in parts by weight: 100 parts of a high polymer matrix, 0.2-2 parts of a toner, 1-5 parts of a nano-inorganic material and 1-5 parts of a telluretted metal material.

Description

technical field [0001] The invention relates to the field of material modification, in particular to a polymer material for remote control equipment. Background technique [0002] Infrared remote control is widely used in commonly used household appliances or electronic devices such as TVs, set-top boxes, and infrared 3D glasses. On these remote control devices, in order to receive infrared light, a hole is usually made on the appearance of the product, and the second is to make a hole on the appearance of the product to inlay a transparent product (remote control window). In this case, the appearance of the product is seriously affected and the difficulty and cost of product manufacturing are increased. Contents of the invention [0003] The object of the present invention is to: aim at the above-mentioned existing problems, provide a kind of polymer material for remote control equipment, described polymer material comprises: 100 parts of polymer matrix, 0.2-2 part of to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/12C08K3/22C08K3/34C08K3/30C08L55/02C08K3/28C08L23/12C08K3/38C08L53/02
Inventor 夏飞
Owner 四川威亿塑胶制品有限公司