Phenolic resin shaft sleeve and manufacturing method thereof

A phenolic resin and bushing technology, applied in the field of phenolic resin bushings and their manufacturing, can solve the problems of complex mold manufacturing, large investment, poor surface wear resistance of phenolic resin bushings, etc., and meet low requirements for personnel and equipment , The effect of good surface wear resistance and good versatility

Inactive Publication Date: 2018-01-12
嘉善金泰工程塑业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] (3) For products with high dimensional accuracy requirements (especially for multi-cavity molds), this process is lacking
[0008] (4) The disadvantage of compression molding is that the mold manufacturing is complicated, the investment is large, and due to the limitation of the press, it is impossible to manufacture larger products
[0009] (5) The surface wear resistance of the phenolic resin bushing is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phenolic resin shaft sleeve and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The mass percent of the component of phenolic resin pipe material is: fiber monofilament 40%, thermosetting phenolic resin 30%, hydroxymethyl cellulose 10%, carbonate 20%; Described carbonate is calcium carbonate and carbonic acid The mixture of magnesium, the mass ratio of calcium carbonate and magnesium carbonate is 3:1.

Embodiment 2

[0045] The mass percent of the component of phenolic resin pipe material is: fiber monofilament 40%, thermosetting phenolic resin 30%, hydroxymethyl cellulose 10%, carbonate 20%; Described carbonate is calcium carbonate and carbonic acid The mixture of magnesium, the mass ratio of calcium carbonate and magnesium carbonate is 2:1.

Embodiment 3

[0047] The mass percent of the component of phenolic resin pipe material is: fiber monofilament 30%, thermosetting phenolic resin 25%, hydroxymethyl cellulose 15%, carbonate 30%; Described carbonate is calcium carbonate and carbonic acid The mixture of magnesium, the mass ratio of calcium carbonate and magnesium carbonate is 2:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a phenolic resin shaft sleeve. The phenolic resin shaft sleeve comprises the following components by mass percent: 30-45% of fiber mono-filaments, 25-40% of thermosetting phenolic resin, 5-15% of hydroxymethyl cellulose and 15-30% of carbonate, wherein carbonate is a calcium carbonate andmagnesium carbonate mixture with the grain size of 400 meshes or above. A manufacturingprocess of the phenolic resin shaft sleeve comprises the following steps: (1) mixing; (2) drying; (3) impregnation; (4) stoving; (5) reeling; (6) curing formation; and (7) processing. The provided phenolic resin shaft sleeve has favorable universality, is suitable for forming of various complicated products, and does not need a mold, and the manufactured phenolic resin shaft sleeve has good surface abrasive resistance and high temperature resistance.

Description

technical field [0001] The invention relates to the field of shaft sleeves, in particular to a phenolic resin shaft sleeve and a manufacturing method thereof. Background technique [0002] Phenolic resin bushings can maintain their structural integrity and dimensional stability even at very high temperatures, so they are widely used in some high-temperature fields, such as refractory materials, friction materials, adhesives and foundry industries . [0003] The patent application document with the application number 201611188868.4 discloses a new type of shaft sleeve and its preparation method. It mainly uses special plastic substrates to bond and compound these carbon fibers with X-Y directions by molding; thus obtaining excellent performance. Specialty composites. [0004] The defective of this kind preparation process is: [0005] (1) It is not suitable for compression molding of complex products with depressions, side slopes or small holes. [0006] (2) In the manufa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/06C08L77/06C08L1/28C08K3/26B29C53/60
Inventor 陆晓明
Owner 嘉善金泰工程塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com