Imitation stone permeable brick and manufacturing method thereof

A technology of imitating stone and permeable bricks, which is applied in the direction of side ditch/curb, pavement paved with prefabricated blocks, buildings, etc., which can solve the problems that the pore size cannot be made smaller, easy to block, and the water filtration performance is average. Achieve the effect of material saving, good decoration and good water filtration performance

Inactive Publication Date: 2018-01-12
武汉盛大长青建材有限公司
View PDF7 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The internal pore size of the existing concrete permeable bricks cannot be made finer, and its water filtration performance is average, especially in the application process of urban permeable pavement, which is easy to be blocked;
[0003] Moreover, the existing ones generally only imitate stone textures on the surface to improve viewing. Therefore, it is necessary to develop a stone surface permeable brick with better water permeability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitation stone permeable brick and manufacturing method thereof
  • Imitation stone permeable brick and manufacturing method thereof
  • Imitation stone permeable brick and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment one: if figure 1 as shown,

[0034] Making sesame white permeable bricks:

[0035] Step 1. Prepare the concrete base and imitation stone surface, specifically:

[0036] S1. Prepare the base material, add 2kg cement, 8kg base aggregate and 20g water reducer to an appropriate amount of water, stir evenly, dry the water, and transport it to the bottom material distribution box of the block forming equipment for standby;

[0037] S2. Prepare the surface layer material, and transport the polymer cementitious material and the surface layer fine aggregate of the formula amount to the block forming equipment surface layer distribution box after being evenly stirred;

[0038] Among them, the polymer gelling material is made by mixing 0.05kg acrylic resin, 0.08kg polyurethane resin, 0.45kg epoxy resin and 0.29kg fatty amine crosslinking agent;

[0039] The fine aggregate of the surface layer is made of 13.5kg white quartz stone and 1.0kg black quartz stone with a pa...

Embodiment 2

[0045] Making sesame gray permeable bricks:

[0046] Step 1. Prepare the concrete base and imitation stone surface, specifically:

[0047] S1. Prepare base material, add 2kg cement, 8.5kg base aggregate and 20g water reducer to an appropriate amount of water, stir evenly, dry the water, and transport it to the bottom material distribution box of the block forming equipment for standby;

[0048] S2. Prepare the surface layer material, and transport the polymer cementitious material and the surface layer fine aggregate of the formula amount to the block forming equipment surface layer distribution box after being evenly stirred;

[0049] Among them, the polymer gelling material is made by mixing 0.02kg acrylic resin, 0.06kg polyurethane resin, 0.25kg epoxy resin and 0.1kg fatty amine crosslinking agent;

[0050] The fine aggregate of the surface layer is made of 8.5kg white quartz stone and 6.0kg gray quartz stone with a particle size of 0.15-3mm;

[0051] Step 2. Start the bl...

Embodiment 3

[0056] Making maple leaf red permeable bricks:

[0057] Step 1. Prepare the concrete base and imitation stone surface, specifically:

[0058] S1. Prepare the base material, add 2.2kg cement, 8kg base aggregate and 25g water reducer to an appropriate amount of water, stir evenly, dry the water, and transport it to the bottom material distribution box of the block forming equipment for standby;

[0059] S2. Prepare the surface layer material, and transport the polymer cementitious material and the surface layer fine aggregate of the formula amount to the block forming equipment surface layer distribution box after being evenly stirred;

[0060] Among them, the polymer gelling material is made by mixing 0.1kg acrylic resin, 0.65kg epoxy resin and 0.3kg phenalkamine crosslinking agent;

[0061] The surface layer fine aggregate is made of 11.5kg red quartz stone, 1.0kg gray quartz stone, 1.0kg white quartz stone and 1.0kg black quartz stone with a particle size of 0.15-3mm;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an imitation stone permeable brick and a manufacturing method thereof. The imitation stone permeable brick consists of a concrete base layer and an imitation stone surface layer arranged on the concrete base layer. The imitation stone surface layer is supported by polymer cementitious materials and surface layer aggregate and has good drainability. By using continuous graded fine aggregate granules, the through aperture of the interior of the materials is extremely fine, solid particles of being above 5 [mu]m can be filtered, the problems that city permeable pavement bricks are easily jammed and filtrability does not exist are solved, the decorativeness is good, the color and texture of the imitation stone permeable brick is close to the color and texture of natural stone, materials are saved, the natural stone is cut into plates while waste materials are fully used, mining of natural stone resources is reduced, the society is benefited, and the imitation stonepermeable brick is simple in whole preparation process and low in production cost.

Description

technical field [0001] The invention relates to the technical field of brick production, in particular to a stone imitation permeable brick and a production method thereof. Background technique [0002] The internal pore size of the existing concrete permeable bricks cannot be made finer, and its water filtration performance is average, especially in the application process of urban permeable pavement, which is easy to be blocked; [0003] Moreover, the existing ones generally only imitate stone textures on the surface to improve the ornamental value. Therefore, it is necessary to develop a stone surface permeable brick with better water permeability. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a stone imitation permeable brick and its manufacturing method, which effectively overcomes the defects of the prior art. [0005] The technical scheme that the present invention solves the problems of the technologie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E01C11/22E01C5/22C04B28/00C04B28/04C04B28/06C04B28/34C04B26/16C08L63/00C08L33/00C08L75/04C08K3/00C08K3/34C08J3/075
Inventor 张丽徐智勇兰普添
Owner 武汉盛大长青建材有限公司