Antibacterial and moisture preservation mask with mild touch sense and manufacturing method thereof

A production method and a technology for moisturizing face, which are applied in the directions of skin care preparations, medical preparations containing active ingredients, pharmaceutical formulas, etc., and can solve the problems of unfavorable inflammation, acne repair, itching at the wound site, and unfavorable sleep state of users, etc. problems, to accelerate wound healing, improve stability and viscosity, and ensure uniformity

Active Publication Date: 2018-02-06
GUANGDONG YALGET FINE CHEM
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the one-time independent sealed package is convenient for storage, there is no need to add too much antibacterial and bactericidal substances, but because the non-woven fabric will bring a foreign body sensation, which is not conducive to sleep; This type of mask is usually packed in a box for multiple uses, how to prevent the mask containing a lot of nourishing ingredients from spoiling is a key control factor for the quality of this substrate-free mask
[0006] For this reason, antibacterial and bactericidal substances need to be added in an appropriate amount in the non-substrate mask to prevent the growth of bacteria in the mask, but these ingredients also affect the facial skin to a certain extent, and have certain irritation to the skin. Bactericidal substances are likely to affect the repair of inflammation and acne, making the wound site feel itchy, which is not conducive to the user to go to sleep; adding less mask is easy to breed bacteria, which is not conducive to the repair of inflammation and acne, and even make symptoms worse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and moisture preservation mask with mild touch sense and manufacturing method thereof
  • Antibacterial and moisture preservation mask with mild touch sense and manufacturing method thereof
  • Antibacterial and moisture preservation mask with mild touch sense and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Calculated by weight, equipped with 200g of allantoin, 200g of niacinamide, 1kg of trimethylglycine, 500g of erythritol, 20g of sodium hyaluronate, 2kg of glycerol polyether-26, 1kg of D-panthenol, and 4 benzophenone 30g, Carbomer 300g, Acrylates / Vinyl Isodecanoate Crosspolymer 100g, Simethicone 1kg, Vitamin E 200g, Butylene Glycol 4kg, Menthol 3g, Brilliant Blue 3g, PEG-7 Olive Oil Ester 15g, potassium hydroxide 150g, essence 12g, nano silver ion water 30kg, deionized water 59.267kg;

[0039] The above materials are prepared as follows:

[0040] Step (1): Nano-silver ion water is prepared by adding 0.25g of nano-silver oxide powder, 14.88g of sodium borosilicate, and 14.88g of calcium borosilicate into 29.97g of deionized water at a speed of 10000~12000r / min Form nano-silver ion water with a uniform dispersion system;

[0041] Step (2): Heat 59.267kg of deionized water in the mixing tank to 80~83°C, keep it for 10~15min, and add 200g of allantoin and 200g of nicotina...

Embodiment 2

[0046] Calculated by weight, equipped with 80g of allantoin, 100g of niacinamide, 800g of trimethylglycine, 200g of erythritol, 10g of sodium hyaluronate, 1.5kg of glyceryl polyether-26, 800g of D-panthenol, and 800g of benzophenone- 4 10g, carbomer 250g, acrylate / vinyl isodecanoate crosspolymer 300g, simethicone 1.5kg, vitamin E 350g, butylene glycol 5kg, PEG-7 olive oil ester 30g, potassium hydroxide 125g , Nano silver ion water 32kg, deionized water 56.945kg;

[0047] The above materials are prepared as follows:

[0048] Step (1): Add 0.15g of nano-silver oxide powder and 29.85g of sodium borosilicate to 29.97g of deionized water and prepare nano-silver ion water with a uniform dispersion system at a speed of 10000~12000r / min. silver ion water;

[0049] Step (2): Heat 56.945kg of deionized water in the mixing tank to 82~85°C, keep it for 15~20min, and add 80g of allantoin and 100g of nicotinamide in proportion at a stirring speed of 15~20r / min, Erythritol 200g, D-Panthen...

Embodiment 3

[0054] Calculated by weight, equipped with 450g of allantoin, 350g of nicotinamide, 2kg of trimethylglycine, 750g of erythritol, 35g of polymer sodium hyaluronate, 45g of oligomeric hyaluronate sodium, glycerol-26 2.3kg, D -Panthenol 1.3kg, Benzophenone-4 200g, Carbomer 650g, Acrylate / Vinyl Isodecanoate Crosspolymer 50g, Simethicone 800g, Vitamin E 150g, Butylene Glycol 3.2kg, Peppermint Brain 4.5g, brilliant blue 1.5g, PEG-7 olive oil ester 10g, potassium hydroxide 325g, essence 8g, nano silver ionized water 29kg, deionized water 58.371kg;

[0055] The above materials are prepared as follows:

[0056] Step (1): Nano-silver ion water is prepared by adding 0.25g of nano-silver oxide powder, 14.88g of sodium borosilicate, and 14.88g of calcium borosilicate into 32.97g of deionized water at a speed of 13000~15000r / min Form nano-silver ion water with a uniform dispersion system;

[0057] Step (2): Heat 58.371kg of deionized water in the mixing tank to 80~83°C, keep it for 10~15m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of cosmetics, in particular to an antibacterial and moisture preservation mask with the mild touch sense and a manufacturing method thereof. Glycerol contents are not added in a product; after the face is coated with the mask, the touch sense is mild but not sticky or greasy; under the effects of emulsifying and thickening ingredients such as acrylic ester/vinyl isodecanoate crosslinked polymers, dimethicone, carbomer and butanediol, after the still standing for 4 to 8 h after the coating of the product, the surface layer is in a half solidified state; the influence of the product on bedding, mattress and pillows under unconscious actions during deep sleeping can be reduced. In addition, through the use of nanometer silver with strong antibacterial and bactericidal effects, the complementary effect is achieved with allantoin, and D-panthenol antibacterial and bactericidal ingredients in the formula, so that the antibacterial and bactericidalcapability of the product is improved. The synergistic effect is achieved with moisture preservation ingredients of trimethylglycine trimethylglycocoll, phycite, sodium hyaluronate and the like in the product; the skin fine blood vessels, inflammation or acne are fast restored; meanwhile, watery and glossy states are restored.

Description

technical field [0001] The invention relates to the technical field of cosmetics, in particular to an antibacterial and moisturizing facial mask with mild touch and a manufacturing method thereof. Background technique [0002] A good face is the best way to make a deep first impression. Full of moist texture, the shiny and smooth facial skin makes the beautiful face look more tender and charming. How many beauty lovers have always been cautious and concerned about the maintenance of facial skin. [0003] In daily life, it is inevitable that due to various reasons such as high work pressure, lack of attention to cleaning, uncontrolled diet, irregular work and rest, etc., the facial skin will appear dull, dry, acne, sagging and other skin problems. The use of facial masks can improve the above conditions. Keep the facial skin moisturized, smooth and firm, and delay aging. [0004] Protection during the day and repair at night have become the skin care awareness of many peop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/19A61K8/34A61K8/44A61K8/49A61K8/67A61K8/73A61K8/81A61K8/86A61K8/891A61K8/91A61K8/92A61Q19/00
CPCA61K8/19A61K8/34A61K8/345A61K8/44A61K8/4946A61K8/673A61K8/675A61K8/678A61K8/735A61K8/8147A61K8/86A61K8/891A61K8/91A61K8/922A61K2800/48A61K2800/524A61Q19/00
Inventor 吕英杰翁创金
Owner GUANGDONG YALGET FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap