High-strength anti-swing bar
An anti-roll bar, high-strength technology, applied in the field of alloy materials, can solve the problems of insufficient function, easy loss of control of vehicles, rolling of vehicles, etc., and achieves the effects of light weight, reduced impurity content, and reduced hot cracking tendency.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1
[0024] The aluminum alloy material for preparing the high-strength anti-roll bar is smelted, wherein the composition of the aluminum alloy material is: Si: 11.2%, Mg: 1.0%, Cr: 0.1%, Cu: 0.25%, Mn: 0.15%, Zr: 0.1%, the balance is Al and inevitable impurity elements; while smelting, a covering agent with a mass of 2% by mass of the aluminum alloy material is added. The covering agent includes the following components by mass percentage: 40% KCl, 40% NaCl, 20% Cryolite; use C 2 Cl 6 After slagging and degassing, let stand for 20 minutes, add 0.5% K / Na modifier of aluminum alloy material, and then cool down to cast high-strength anti-roll bar castings; heat-treat the high-strength anti-roll bar castings and rare earth modified anodes After oxidation treatment and sealing treatment, a high-strength anti-roll bar product is obtained. Among them, the heat treatment includes the following steps: the temperature of the short-term uniform treatment is 450℃, and the time...
Example Embodiment
[0025] Example 2
[0026] The aluminum alloy material for preparing the high-strength anti-roll bar is smelted. The composition of the aluminum alloy material is: Si: 11.4%, Mg: 1.2%, Cr: 0.13%, Cu: 0.26%, Mn: 0.18%, Zr: 0.15%, the balance is Al and unavoidable impurity elements; while smelting, a covering agent with a mass of 2.8% by mass of the aluminum alloy material is added, and the covering agent includes the following mass percentage components: 43% KCl, 41% NaCl, 16% Cryolite; use C 2 Cl 6 After slagging and degassing, let it stand for 23 minutes, add K / Na modifier with a mass of 0.65% of aluminum alloy material, and then cool down to cast high-strength anti-roll bar castings; heat-treat the high-strength anti-roll bar castings with rare earth modified anodes After oxidation treatment and sealing treatment, a high-strength anti-roll bar is obtained. The heat treatment includes the following steps: the temperature of short-term uniform treatment is 458℃, the time is 1.06h;...
Example Embodiment
[0027] Example 3
[0028] The aluminum alloy material for preparing the high-strength anti-roll bar is smelted. The composition of the aluminum alloy material is: Si: 11.5%, Mg: 1.25%, Cr: 0.15%, Cu: 0.28%, Mn: 0.2%, Zr: 0.2%, the balance is Al and inevitable impurity elements; while smelting, a covering agent with a mass of 3.5% by weight of the aluminum alloy material is added. The covering agent includes the following components by mass percentage: 45% KCl, 40% NaCl, 15% Cryolite; use C 2 Cl 6 After slagging and degassing, let it stand for 25 minutes, add K / Na modifier with a mass of 0.75% of aluminum alloy material, and then cool down to cast high-strength anti-roll bar castings; heat-treat the high-strength anti-roll bar castings with rare earth modified anodes After oxidation treatment and sealing treatment, the finished product of high-strength anti-roll bar is obtained. The heat treatment includes the following steps: the temperature of short-time uniform treatment is 465...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap