Solar panel selective heat absorption material and preparation method thereof

A technology of heat-absorbing materials and solar panels, which is applied in the field of solar heat absorption, can solve the problems of low thermal efficiency of solar collectors, coatings that are not weather-resistant, and premature pulverization, etc., and achieve excellent mechanical properties, high water and temperature resistance, Good defoaming effect

Inactive Publication Date: 2018-03-20
GUANGXI JIKUAN SOLAR ENERGY EQUIP
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, it is generally used in the market to spray black organic coatings on the heat-absorbing plate core of solar collectors, such as black fluorocarbon resin, black epoxy resin, black polyurethane resin, etc., because ordinary resin materials are used as adhesives. 2. Since ordinary carbon black or black pigments are used as the color body, there is no spectrum selectivity
Therefore, its coating has a high emissivity, which results in low thermal efficiency of the solar collector.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solar panel selective heat absorption material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A solar panel selective heat-absorbing material and a preparation method thereof, the material is made of the following raw materials in parts by weight:

[0019] 8 parts of nano-scale spinel pigment, 6 parts of nickel powder, 40 parts of linseed oil-based water-based polyurethane-polyacrylic resin, 10 parts of drying oil alkyd resin, 6 parts of anhydrous acetone, 6 parts of EFKA3570, 8 parts of SN-5027 14 parts, polyether modified silicone oil defoamer.

[0020] The main raw materials for the synthesis of the linseed oil-based water-based polyurethane-polyacrylic acid resin are hydroxylated linseed oil, isophorone diisocyanate, polyether N210 (Mn=1000), 2,2-dimethylol propionic acid, acetal Diethylene glycol, stannous octoate, dibutyltin dilaurate, triethylamine, acetone, methyl methacrylate, butyl acrylate, sodium lauryl sulfate, potassium persulfate, and sodium bicarbonate.

[0021] The nano-scale spinel pigment is obtained by calcining the following raw materials a...

Embodiment 2

[0025] A solar panel selective heat-absorbing material and a preparation method thereof, the material is made of the following raw materials in parts by weight:

[0026] 5 parts of nano-scale spinel pigment, 4 parts of nickel powder, 30 parts of linseed oil-based water-based polyurethane-polyacrylic resin, 8 parts of drying oil alkyd resin, 4 parts of anhydrous acetone, 4 parts of EFKA3570, 4 parts of SN-5027 8 parts, polyether modified silicone oil defoamer.

[0027] The main raw materials for the synthesis of the linseed oil-based water-based polyurethane-polyacrylic acid resin are hydroxylated linseed oil, isophorone diisocyanate, polyether N210 (Mn=1000), 2,2-dimethylol propionic acid, acetal Diethylene glycol, stannous octoate, dibutyltin dilaurate, triethylamine, acetone, methyl methacrylate, butyl acrylate, sodium lauryl sulfate, potassium persulfate, and sodium bicarbonate.

[0028] The nano-scale spinel pigment is obtained by calcining the following raw materials aft...

Embodiment 3

[0032] A solar panel selective heat-absorbing material and a preparation method thereof, the material is made of the following raw materials in parts by weight:

[0033] 10 parts of nano-scale spinel pigment, 8 parts of nickel powder, 50 parts of linseed oil-based water-based polyurethane-polyacrylic resin, 12 parts of drying oil alkyd resin, 8 parts of anhydrous acetone, 8 parts of EFKA3570, 12 parts of SN-5027 part, 20 parts of polyether modified silicone oil defoamer.

[0034] The main raw materials for the synthesis of the linseed oil-based water-based polyurethane-polyacrylic acid resin are hydroxylated linseed oil, isophorone diisocyanate, polyether N210 (Mn=1000), 2,2-dimethylol propionic acid, acetal Diethylene glycol, stannous octoate, dibutyltin dilaurate, triethylamine, acetone, methyl methacrylate, butyl acrylate, sodium lauryl sulfate, potassium persulfate, and sodium bicarbonate.

[0035] The nano-scale spinel pigment is obtained by calcining the following raw m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
emissivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a solar panel selective heat absorption material and a preparation method thereof. The solar panel selective heat absorption material is prepared from the following raw materials in parts by mass: 5-10 parts of a nano-scale spinel type pigment, 4-8 parts of nickel powder, 30-50 parts of linseed oil based waterborne polyurethane-polyacrylic resin, 8-12 parts of drying oil alkyd resin, 4-8 parts of anhydrous acetone, 4-8 parts of EFKA3570, 4-12 parts of SN-5027 and 8-20 parts of a polyether modified silicone oil defoamer. The solar panel selective heat absorption materialprovided by the invention is simple in preparation technology, low in cost and liable in industrial production; and in addition, a coating prepared by using the material is high in heat absorption rate and low in light emitting rate and has good mechanical properties and stronger weatherability.

Description

technical field [0001] The invention relates to the technical field of solar heat absorption, in particular to a selective heat absorption material for a solar panel and a preparation method thereof. Background technique [0002] Energy utilization plays a pivotal role in the development of human society, but the excessive development of resources and inefficient resource utilization make human beings face a severe test. As we all know, solar energy is the most abundant and widely available renewable energy, which plays a major role in solving energy crisis and environmental problems. , making it a hot research topic in various countries. [0003] Solar absorbing coatings are mainly divided into spectrally selective absorbing coatings and high-absorbing absorbing coatings. Spectrum-selective heat-absorbing coatings are special coatings with high absorption of visible-near-infrared light and high reflection of infrared light. , that is, it can effectively absorb solar energ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D167/08C09D183/12C09D7/61C09D7/63
CPCC09D175/14C08K2003/0862C08L67/08C08L83/12C08K3/34C08K3/08C08K5/07
Inventor 丘秋燕李正良陈明贤金秋生郭家红姚小龙
Owner GUANGXI JIKUAN SOLAR ENERGY EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap