Imitation ceramic PET/ABS resin composition and preparation method thereof

A technology of ABS resin and ceramic imitation, which is applied in the field of ceramic imitation PET/ABS resin composition and its preparation, which can solve the problems of fragility, complicated process, difficult recycling, etc., and achieve good impact resistance, good toughness and good weather resistance Effect

Inactive Publication Date: 2018-04-03
SHANGHAI KINGFA SCI & TECH +2
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a ceramic imitation PET / ABS resin composition with impact resistance, high surface gloss, easy molding and high density and its Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitation ceramic PET/ABS resin composition and preparation method thereof
  • Imitation ceramic PET/ABS resin composition and preparation method thereof
  • Imitation ceramic PET/ABS resin composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Mix AB-3000N1, HYFE-300, Z-6040 in a high-speed mixer at room temperature for 5-10 minutes; then add PET BG80, ABS PA757, TINUVIN 327, CHIMASSORB 944, Irganox 1010, Irganox 168 into the high-speed mixer Mixed and then extruded in a twin-screw extruder. The processing conditions are: the temperature of the first zone is 235°C, the temperature of the second zone is 245°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 250°C, the temperature of the sixth zone is 250°C, the temperature of the seventh zone is 255°C, and the temperature of the eighth zone is 255°C ℃, the temperature in the ninth zone is 245 ℃; the speed of the host is 350 rpm.

Embodiment 2

[0041] Mix AB-3000N1, HYFE-300, and Z-6040 in a high-speed mixer at room temperature for 5-10 minutes; then add PET BG80, TINUVIN 327, CHIMASSORB 944, Irganox 1010, and Irganox 168 into the high-speed mixer for mixing, and then extruded in a twin-screw extruder. The processing conditions are: the temperature of the first zone is 240°C, the temperature of the second zone is 245°C, the temperature of the third zone is 245°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 250°C, the temperature of the sixth zone is 250°C, the temperature of the seventh zone is 255°C, and the temperature of the eighth zone is 255°C ℃, the temperature in the ninth zone is 240 ℃; the speed of the host is 300 rpm.

Embodiment 3

[0043]Mix AB-3000N1, HYFE-300, Z-6040 in a high-speed mixer at room temperature for 5-10 minutes; then add PET BG80, ABS PA757, PTW, TINUVIN 327, CHIMASSORB 944, Irganox1010, Irganox 168 into high-speed mixing Machine mixing, followed by extrusion in a twin-screw extruder. The processing conditions are: the temperature of the first zone is 235°C, the temperature of the second zone is 245°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 250°C, the temperature of the sixth zone is 250°C, the temperature of the seventh zone is 255°C, and the temperature of the eighth zone is 255°C °C, the temperature in the ninth zone is 245 °C; the speed of the host is 350 rpm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an imitation ceramic PET / ABS resin composition and a preparation method thereof. The imitation ceramic PET / ABS resin composition is prepared from the following components in parts by weight: 13.3 to 63 parts of PET resin, 2 to 50 parts of ABS resin, 0 to 10 parts of a flexibilizer, 30 to 60 parts of filler, 5 to 15 parts of metal powder, 0.5 part of a coupling agent, 0.6 part of a weather-resisting agent and 0.6 part of an antioxidant. The imitation ceramic PET / ABS resin composition disclosed by the invention has the characteristics of better impact resistance, high surface gloss, relatively-large density and the like, and can be used in certain fields instead of ceramic products.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a ceramic-like PET / ABS resin composition and a preparation method thereof. Background technique [0002] Ceramic products used in daily life are mostly made of clay or a mixture containing clay as mud mixing, shaped by a screw vacuum extruder, cut into mud embryos and then calcined. Ceramic products are deeply loved by people because of their natural, beautiful, durable, and low-cost characteristics, and can be seen everywhere in life. However, ceramics also have shortcomings such as high energy consumption for firing, poor toughness and brittleness, and the production process requires the use of precious soil resources, and consumes a lot of energy, generates a lot of waste, and destroys the natural ecology. [0003] Plastic products have the advantages of light weight, good toughness, convenient molding, and easy recycling. Therefore, how to imitate ceramics with p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L67/02C08L23/08C08K13/02C08K3/30C08K3/08C08K5/3475C08K3/22
CPCC08L55/02C08K3/08C08K3/30C08K5/3475C08K13/02C08K2003/0856C08K2003/2241C08K2003/2296C08K2003/3045C08L67/02C08L2205/03C08L2205/06C08L23/0884C08K3/22
Inventor 夏建盟刘志雄杜赏殷年伟黄河生
Owner SHANGHAI KINGFA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com