Purifying method of pulp electrolyte containing antimony concentrates

Abstract

The invention discloses a purifying method of pulp electrolyte containing antimony concentrates. The purifying method comprises the following steps: (A) oxidation: part of divalent iron ions are oxidized as trivalent iron ions; (B) extraction: oxide liquid and an organic phase are mixed in a mixing tank for extraction; (C) washing: less antimony in the organic phase is transferred into washing liquid; (D) blank: a washing organic phase flows to clarifying tank component phases on a blank stage by the mixing tank; (E) reverse extraction: such substances as iron, copper and silicon dioxide in the organic phase are transferred into sodium carbonate solution to generate precipitations; and (F) regeneration: the reversely extracted organic phase is mixed with a prepared regeneration agent in the mixing tank for regeneration. The purifying method solves the problem the entrainment problem of antimony in the organic phase, and realizes recycling of the organic phase.

Description

technical field [0001] The invention relates to a method for separating valuable metal antimony from impurity iron ions and harmful organic substances in an antimony electrolyte, in particular to a method for purifying an antimony-containing concentrate slurry electrolyte. Background technique [0002] The modern metallurgical production methods of metal antimony are mainly divided into two categories: fire method and wet method. At present, antimony by fire method is the main method. Antimony smelting by fire method is mainly volatile roasting-reduction smelting method, that is, antimony trioxide is produced first, and then crude antimony is produced by reduction smelting; antimony smelting by wet method mainly includes two methods: alkaline leaching and acid leaching. The process of antimony smelting by pyrometallurgy has the problems of long process, many returning materials, difficult separation of antimony and lead, and accumulation of polysulfides in alkaline wet antim...

AI Technical Summary

Problems solved by technology

When treating complex antimony-gold concentrates with slurry electrolysis process, antimony is selectively leached in the anode area, and metal antimony is deposited and precipitated in the cathode, reaching a balance. However, about 4% of the iron in the raw material is leached into the solution, and the iron continues to accumulate, thus affecting The entire electrolysis process is carried out normally; at the same time, the organic flotation agent added in the early flotation process of the complex antimony-gold concentrate and the oil unloaded during the operation of various equipment reduce the current efficiency of antimony electrolysis and increase the unit power consumption. Therefore, it is necessary to purify, remove iron and reduce oil in the slurry electrolyte, so as to maintain the concentration of iron ions in a reasonable area

[0003] Chen Yongqiang, Liu Yong, Wang Chengyan, etc. mentioned in the "continuous expansion test of electrolysis of high arsenic antimony gold concentrate pulp electrolysis" published in the twelfth issue of nonferrous metals (smelting part) in 2015, and mentioned extraction and removal of iron, and hydrochloric acid back extraction was used in the process; Zhang Yinsheng, Wang Chengyan, Jiang Peihai, etc. published in the second issue of Nonferrous Metals (Smelting Part) in 2003 "P204 Extraction and Separation of Iron Antimony Process Research" mentioned extraction and removal of iron, washing of loaded organic phase, hydrochloric acid back extraction and back extraction The N235 iron extraction process of iron in the liquid is composed of processes such as iron extraction. The deficiencies in these two studies are: ① The iron ion in the anolyte of the slurry electrolysis in the production site exists in the form of Fe 2+ , while Fe 3+ The content is less than 1g/L, P204 mainly extracts Fe 3+ , Fe 2+ The amount of extraction is less; ② due to Fe 3+ The stripping speed in hydrochloric acid is slow, and the organic phase after stripping a

Images