Vehicle chassis armor coating and production method thereof

A technology for automobile chassis and armor, applied in anti-corrosion coatings, fire-resistant coatings, anti-fouling/underwater coatings, etc., can solve the problems of single use, no mildew resistance, rust resistance, flame retardancy, etc., and achieve less time and extrusion Good effect, continuous and uninterrupted production effect

Inactive Publication Date: 2018-04-27
海宁迪万沃浦建材科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the coating disclosed in this patent is non-polluting to the environment, the composition of the coating is too simple, has no anti-mildew, anti-rust, and flame-retardant properties, and is single-use. Therefore, a car chassis armor coating and its production method are designed. is very necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vehicle chassis armor coating and production method thereof
  • Vehicle chassis armor coating and production method thereof
  • Vehicle chassis armor coating and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0054] The following are specific embodiments of the present invention and in conjunction with the accompanying drawings, the technical solutions of the present invention are further described, but the present invention is not limited to these embodiments.

[0055] The automobile chassis armor coating comprises, in parts by weight: 22-30 parts of water-based emulsion, 40-60 parts of functional filler, 3-12 parts of film-forming aid, 0.3-0.8 part of dispersant, 0.4-1 part of anti-corrosion and anti-mold agent, 0.3-0.6 parts of defoamer, 0.2-0.5 parts of rust inhibitor, 3-10 parts of flame retardant, 0.5-1.2 parts of thickener, 2-5 parts of antifreeze and 10-20 parts of water; in this embodiment , 28 parts of water-based emulsion, 42 parts of functional filler, 5 parts of film-forming aid, 0.4 part of dispersant, 0.5 part of anti-corrosion and anti-mold agent, 0.4 part of defoamer, 0.3 part of rust inhibitor, 6 parts of flame retardant, thickener 0.8 parts of agent, 3 parts of a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a vehicle chassis armor coating and a production method thereof. The vehicle chassis armor coating solves the problem that the existing coating has a simple formula, has no anti-mildew, anti-rust and flame retardant performances and has a single purpose. The vehicle chassis armor coating comprises, by weight, 22 to 30 parts of an aqueous emulsion, 40 to 60 parts of a functional filler, 3 to 12 parts of a coalescent, 0.3 to 0.8 parts of a dispersant, 0.4 to 1 part of an antiseptic and anti-mould agent, 0.3 to 0.6 parts of a defoamer, 0.2 to 0.5 parts of a rust inhibitor,3 to 10 parts of a flame retardant, 0.5 to 1.2 parts of a thickener, 2 to 5 parts of an antifreezing agent and 10 to 20 parts of water. The vehicle chassis armor coating has strong practicality.

Description

technical field [0001] The invention relates to an automobile chassis armor paint and a production method thereof. Background technique [0002] Chassis armor can effectively protect the vehicle chassis from being hit by road sand and gravel, prevent slight dragging friction; prevent acid, alkali, and salt from corroding the chassis iron plate; prevent chassis screws from loosening; reduce noise transmission during driving, increase Driving tranquility; preventing the heat conduction of the chassis iron plate, so that the cab is warm in winter and cool in summer. [0003] After searching, for example, Chinese patent literature discloses a damping coating for automobile chassis armor [application number: 201610931337.3]. This damping coating for automobile chassis armor is characterized in that it comprises the following raw materials: 145-155 parts of acrylic waterproof emulsion, 45-55 parts of rust-proof emulsion, 95-105 parts of plasticized acrylic emulsion, 145-155 parts...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/14C09D5/18C09D5/08C09D7/61
CPCC09D201/00C08K3/34C08K3/346C08K2003/265C09D5/08C09D5/14C09D5/18
Inventor 胡小红
Owner 海宁迪万沃浦建材科技有限公司