Thermoplastic elastomer composition as well as preparation method and application thereof

A thermoplastic elastomer and composition technology, applied in the field of polymer modified materials and its production and processing, can solve the problem of wet skid resistance, wear resistance, poor weather resistance, single material floor can not meet the impact absorption performance and ball rebound performance at the same time and other problems, to achieve excellent weather resistance, improve comfort and safety, and simple preparation methods

Active Publication Date: 2018-05-01
河北英利奥体育用品有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the embodiments of the present invention is to provide a thermoplastic elastomer composition, aiming to solve the defects that the existing single-material floor cannot satisfy the impact absorption performance and the ball rebound performance at the same time, and has poor wet skid resistance, abrasion resistance and weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic elastomer composition as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The thermoplastic elastomer composition is composed of the following components by weight: 75 parts of SEEPS, 65 parts of ethylene-octene block copolymerized olefins, 87 parts of paraffin oil, 102 parts of maleic anhydride grafted butadiene, 132 parts of maleic anhydride Anhydride grafted polypropylene, 60 parts of high styrene rubber powder, 64 parts of nitrile rubber powder, 54 parts of silicone powder, 33 parts of calcium carbonate, 50 parts of PP granules, and weighed 33 parts of DCP masterbatch and 25 parts of TMPTMA.

[0038] The preparation method is as follows: under the condition of 80°C, fully stir 75 parts by weight of SEEPS until it is fluffy without agglomeration, add 87 parts of paraffin oil and stir to make oil-extended rubber; Parts of ethylene-octene block copolymerized olefin, 102 parts of maleic anhydride grafted butadiene, 132 parts of maleic anhydride grafted polypropylene, 60 parts of high benzene rubber powder, 64 parts of nitrile rubber powder, 54...

Embodiment 2

[0042] The thermoplastic elastomer composition is composed of the following components by weight: mainly composed of the following components by weight: 85 parts of SEPS, 90 parts of ethylene-octene block copolymerized olefin, 105 parts of paraffin oil, 100 parts of maleic anhydride Grafted butadiene, 78 parts of maleic anhydride grafted polypropylene, 85 parts of high styrene rubber powder, 90 parts of nitrile rubber powder, 65 parts of silicone powder, 34 parts of calcium carbonate, 50 parts of PP particles, and weighed 28 parts Parts of DCP masterbatch, 20 parts of TMPTMA.

[0043] Its preparation method is as follows: under the condition of 80°C, fully stir 85 parts by weight of SEPS until it is fluffy without agglomeration, add 105 parts of paraffin oil and stir to make oil-extended rubber; Parts of ethylene-octene block copolymerized olefin, 100 parts of maleic anhydride grafted butadiene, 78 parts of maleic anhydride grafted polypropylene, 85 parts of high benzene rubbe...

Embodiment 3

[0047] The thermoplastic elastomer composition is composed of the following components by weight: mainly composed of the following components by weight: 120 parts of SEEPS, 85 parts of ethylene-octene block copolymerized olefins, 150 parts of paraffin oil, 100 parts of maleic anhydride Grafted butadiene, 100 parts of maleic anhydride grafted polypropylene, 60 parts of high styrene rubber powder, 60 parts of nitrile rubber powder, 56 parts of silicone powder, 58 parts of calcium carbonate, 50 parts of PP particles, and weighed 38 parts Parts of DCP masterbatch, 20 parts of TMPTMA.

[0048] The preparation method is as follows: under the condition of 80°C, fully stir 120 parts by weight of SEEPS until it is fluffy and non-caking, add 150 parts of paraffin oil and stir to make an oil-extended rubber compound, and then mix with 85 parts by weight of SEEPS Parts of ethylene-octene block copolymerized olefin, 100 parts of maleic anhydride grafted butadiene, 100 parts of maleic anhydri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a thermoplastic elastomer composition as well as a preparation method and application thereof. The composition is prepared from the following raw materials in parts by weight:20-150 parts of a mixture of SEPS, SEEPS or SEPS and SEEPS, 20-150 parts of an ethylene-octene block copolyalkenamer, 20-200 parts of paraffinic oil, 20-160 parts of maleic anhydride grafted butadiene, 20-150 parts of maleic anhydride grafted polypropylene, 10-200 parts of rubber powder, 10-100 parts of silicone powder, 10-50 parts of an inorganic filler, 1.9-10 percent of DCP master batches, 1.9-10 percent of TMPTMA and 30-50 parts of PP particles. The preparation method comprises the following step of blending a thermoplastic elastomer material and the rubber powder with a two-step method toform a new thermoplastic elastomer blending system. A floor prepared by adopting the thermoplastic elastomer is high in wet traction, wear resistance and weather resistance.

Description

technical field [0001] The invention belongs to the field of polymer modified materials and their production and processing, and in particular relates to a thermoplastic elastomer composition and its preparation method and application. Background technique [0002] Floors for sports venues are required to have the following properties at the same time: good impact absorption performance and good ball rebound performance, and require wet slip resistance and wear resistance. The impact absorption performance can reduce the damage to the leg joints. The solution is usually to use low-density foam materials. However, due to the relatively high compression rate of low-density foam materials, it is easy to cause uneven floor thickness and dents after long-term trampling. , which in turn affects the use of the product, and the rebound performance of the ball cannot meet the design requirements. [0003] For this reason, a hard bottom structure is often used in the prior art, and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/06C08L51/04C08L53/02C08L53/00C08L91/06C08L9/06C08L9/02C08L23/12C08L83/04C08K3/26C08K5/14B29C47/92B29C48/92
CPCB29C48/92B29C2948/9258B29C2948/92704C08K2003/265C08L51/06C08L91/06C08L2205/035C08L2207/04C08L51/04C08L53/025C08L53/00C08L9/06C08L9/02C08L23/12C08L83/04C08K3/26C08K5/14
Inventor 李郁陈东
Owner 河北英利奥体育用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap