High-strength and anti-wear sheet metal part and production process thereof

A production process and wear-resistant technology, applied in the field of sheet metal parts processing, can solve the problems of increased scrap rate, low wear resistance, high damage rate, etc.

Inactive Publication Date: 2018-05-15
博维恩冷冻科技(苏州)有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The sheet metal materials in the prior art have low wear resistance and high damage rate. The damage of the sheet metal often leads to the damage of the whole product, which greatly increases the scrap rate and causes great environmental pollution. In order to improve the utilization rate of sheet metal parts, reduce the scrap rate, save time and effort, the present invention proposes a high-strength wear-resistant sheet metal part and its production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] This embodiment provides a high-strength wear-resistant sheet metal part, including a sheet metal part, the outer surface of the sheet metal part is coated with a high-strength wear-resistant layer, and the high-strength wear-resistant layer consists of a high-strength layer and a wear-resistant layer. The damaged layer is compounded according to the ratio of high-strength layer: wear-resistant layer = 2:3, and the high-strength layer and wear-resistant layer contain the following components in parts by mass:

[0058] The high-strength layer includes the following components in parts by mass: methyl acetate: 15 parts, trichlorethylene: 8 parts, styrene: 9 parts, 2-butanone cyclohexanone: 12 parts, silicone modified ring Oxygen resin: 14 parts, ATO powder: 13 parts, E-20 epoxy resin: 7 parts, alcohol-soluble acrylate resin: 11 parts, carbon fiber powder: 20 parts, film-forming aid: 12 parts;

[0059] The wear-resistant layer includes the following components in parts by ...

Embodiment 2

[0087] This embodiment provides a high-strength wear-resistant sheet metal part, including a sheet metal part, the outer surface of the sheet metal part is coated with a high-strength wear-resistant layer, and the high-strength wear-resistant layer consists of a high-strength layer and a wear-resistant layer. The damaged layer is compounded according to the ratio of high-strength layer: wear-resistant layer = 2:3, and the high-strength layer and wear-resistant layer contain the following components in parts by mass:

[0088] The high-strength layer includes the following components in parts by mass: methyl acetate: 19 parts, trichloroethylene: 11 parts, styrene: 16 parts, 2-butanonecyclohexanone: 19 parts, silicone modified ring Oxygen resin: 20 parts, ATO powder: 17 parts, E-20 epoxy resin: 9 parts, alcohol-soluble acrylate resin: 15 parts, carbon fiber powder: 22 parts, film-forming aid: 17 parts;

[0089] The wear-resistant layer includes the following components in parts by ...

Embodiment 3

[0118] This embodiment provides a high-strength wear-resistant sheet metal part, including a sheet metal part, the outer surface of the sheet metal part is coated with a high-strength wear-resistant layer, and the high-strength wear-resistant layer consists of a high-strength layer and a wear-resistant layer. The damaged layer is compounded according to the ratio of high-strength layer: wear-resistant layer = 2:3, and the high-strength layer and wear-resistant layer contain the following components in parts by mass:

[0119] The high-strength layer includes the following components in parts by mass: methyl acetate: 16 parts, trichlorethylene: 10 parts, styrene: 13 parts, 2-butanonecyclohexanone: 15 parts, silicone modified ring Oxygen resin: 16 parts, ATO powder: 14 parts, E-20 epoxy resin: 8 parts, alcohol-soluble acrylate resin: 13 parts, carbon fiber powder: 21 parts, film-forming aid: 15 parts;

[0120] The wear-resistant layer includes the following components in parts by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength and anti-wear sheet metal part. The high-strength and anti-wear sheet metal part comprises a sheet metal part body, wherein the outer surface of the sheet metalbody is coated with a high-strength and anti-wear layer; the high-strength and anti-wear layer is prepared by compounding a high-strength layer and an anti-wear layer according to a ratio of the high-strength layer to the anti-wear layer of 2: 3; the high-strength layer is prepared from 15 to 19 parts of methyl acetate, 8 to 11 parts of trichloro ethylene, 9 to 16 parts of styrene, 12 to 19 partsof 2-butanone cyclohexanone, 14 to 20 parts of silicone modified epoxy resin, 13 to 17 parts of ATO powder, 7 to 9 parts of E-20 epoxy resin, 11 to 15 parts of alcohol soluble acrylate resin, 20 to 22 parts of carbon fiber powder and 12 to 17 parts of a film forming adjuvant; the anti-wear resistance is prepared from 14 to 19 parts of butadiene styrene rubber, 3 to 8 parts of methylbenzene, 9 to11 parts of water glass, 10 to 13 parts of sodium tetraborate, 22 to 28 parts of mixed phosphate, 18 to 22 parts of cyclohexanone, 11 to 18 parts of aromatic polyamide staple fiber, 19 to 23 parts ofa plasticizer, 32 to 39 parts of an auxiliary material, 13 to 19 parts of a solidifying agent and 29 to 32 parts of a defoaming agent.

Description

technical field [0001] The invention relates to the technical field of sheet metal parts processing, in particular to a high-strength wear-resistant sheet metal part and a production process thereof. Background technique [0002] The sheet metal materials in the prior art have low wear resistance and high damage rate. The damage of the sheet metal often leads to the damage of the whole product, which greatly increases the scrap rate and causes great environmental pollution. In order to improve the utilization rate of sheet metal parts, reduce the scrap rate, save time and effort, the present invention proposes a high-strength wear-resistant sheet metal part and its production process. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a high-strength wear-resistant sheet metal and its production process in view of the shortcomings of the above prior art, which not only improves the work efficiency, but also reduces ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D7/61C23C2/06C23C2/40
CPCC09D4/06C23C2/06C23C2/40
Inventor 唐建明唐荣
Owner 博维恩冷冻科技(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap