Hot-wet comfortable polyester fiber DTY silk used in summer and preparation method thereof

A polyester fiber and comfortable technology, which is applied in the field of summer heat-moisture comfort polyester fiber DTY yarn and its preparation, can solve the problems of poor heat-moisture comfort performance and the like

Active Publication Date: 2018-05-15
JIANGSU HENGLI CHEM FIBER
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problem of poor heat and humidity comfort performance of knitted fabrics prepared from fibers in the prior art, and provide a kind of summer heat and humidity comfortable polyester fiber DTY yarn with good heat and humidity comfort performance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-wet comfortable polyester fiber DTY silk used in summer and preparation method thereof
  • Hot-wet comfortable polyester fiber DTY silk used in summer and preparation method thereof
  • Hot-wet comfortable polyester fiber DTY silk used in summer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] A kind of preparation method of hot and humid comfortable polyester fiber DTY yarn for summer, the steps are as follows:

[0068] (1) Preparation of oiling agent for oiling: 2-hydroxymethyl-12-crown-4 and dodecyl phosphate potassium salt, trimethylolpropane laurate and sodium dodecyl sulfonate After mixing evenly at room temperature, add it to 9# mineral oil and stir evenly at 40°C for 1 hour to obtain an oil agent. The amount of each component added is as follows: 9# mineral oil is 2 parts; trimethylolpropane Lauric acid ester is 10 parts; 2-hydroxymethyl-12-crown-4 is 90 parts; dodecyl phosphate potassium salt is 8 parts; sodium dodecylsulfonate is 3 parts; the prepared oil The content of the crown ether is 79.6wt%, and the high temperature resistance of the oil is excellent, and the thermal weight loss is 14.5wt% after heat treatment at 200°C for 2 hours; the viscosity of the oil is low, and the kinematic viscosity 29.6mm 2 / s, the kinematic viscosity after the con...

Embodiment 2

[0074] A kind of preparation method of hot and humid comfortable polyester fiber DTY yarn for summer, the steps are as follows:

[0075] (1) Preparation of oiling agent for oiling: 15-crown ether-5 and isomeric tridecanol polyoxyethylene ether phosphate potassium salt, trimethylolpropane laurate and sodium pentadecylsulfonate in After mixing evenly at room temperature, add it to 10# mineral oil and stir evenly at 43°C for 1.5 hours to obtain the oil agent. In parts by weight, the addition amount of each component is as follows: 10# mineral oil is 2 parts; 15 parts of propane laurate; 70 parts of 15-crown-5; 10 parts of potassium isotridecyl polyoxyethylene ether phosphate; 7 parts of sodium pentadecyl sulfonate; prepared oil The content of crown ether in the agent is 67.30wt%. The high temperature resistance of the oil agent is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 13wt%. The viscosity of the oil agent is low. 28.1mm 2 / s, the kinem...

Embodiment 3

[0081] A kind of preparation method of hot and humid comfortable polyester fiber DTY yarn for summer, the steps are as follows:

[0082] (1) Preparation of oiling agent for oiling: mix 2-hydroxymethyl-15-crown-5 with potassium salt of tetradecyl phosphate, trimethylolpropane laurate and sodium pentadecylsulfonate After mixing evenly at room temperature, add it to 11# mineral oil and stir evenly at 48°C for 3 hours to obtain an oil agent. The addition amount of each component is as follows in parts by weight: 11# mineral oil is 8 parts; 10 parts of propane laurate; 85 parts of 2-hydroxymethyl-15-crown-5; 11 parts of potassium tetradecyl phosphate; 5 parts of sodium pentadecylsulfonate; The content of crown ether in the oil is 70.83wt%. The high temperature resistance of the oil is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 11wt%. The viscosity of the oil is low. Viscosity is 30.1mm 2 / s, the kinematic viscosity after the concentration is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Wicking heightaaaaaaaaaa
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to hot-wet comfortable polyester fiber DTY silk used in summer and a preparation method thereof. The method comprises the steps that spinning melt is measured, extruded through acomposite spinneret plate, cooled, oiled and wound to prepare POY silk, and the POY silk is guided through a silk guide pipe, meshed, heated, stretched, subjected to false twisting and hot shaping and wound to prepare the hot-wet comfortable polyester fiber DTY silk used in summer. The material is polyester dispersed with a matting agent, the core absorption height of prepared knitted fabric is larger than or equal to 160 millimeters, the evaporation rate is larger than or equal to 0.24 g / h, cross spinneret holes and circular spinneret holes are formed in the composite spinneret plate, the specific value of the micropore lengths of the cross spinneret holes and the circular spinneret holes is equal to the product of the proportion of equivalent diameters and the coefficient K, the value range of the coefficient K is between 0.97 and 1.03, an oiling agent which is used for oiling contains crown ether, and the content of crown ether is 67.30-85.58%. The preparation method is simple, andthe obtained fiber is excellent in hot-wet comfortable performance.

Description

technical field [0001] The invention belongs to the field of fiber preparation, and relates to a polyester fiber DTY filament for summer heat and humidity comfort and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, people's requirements for fabrics are getting higher and higher. While pursuing fashionable and elegant clothing, they also require clothing to be comfortable to wear. Comfort means that fabrics can meet people's physiological needs when they are in contact with people in the wearing environment. , Heart needs, the most important thing about fabric comfort is heat and humidity comfort, heat and humidity comfort refers to the fabric maintains a constant body temperature between the heat and moisture transfer between people and the environment, and creates good conditions for the normal physiological functions of the human body, so that The human body maintains a sense of comfort. The heat and humidity ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01D5/253D01D5/30D01D5/096D01F11/08
CPCD01D5/096D01D5/253D01D5/30D01F11/08
Inventor 沈建根魏德新杨超明
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More