Double strong copper strip production technology for automobile connector

An automotive connector and production process technology, applied in the field of double-strength copper strip production process, can solve problems such as difficulty in simultaneously satisfying tensile strength and elongation indicators

Active Publication Date: 2018-05-22
ANHUI CHUJIANG TECHCAL NEW MATERIAL CO LTD
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention aims to overcome the shortcomings of the brass products used in the production of automobile connectors in the prior art, such as the difficulty in meeting the tensile strength and elongation indicators at the same time, and provides a production process for double-strength copper strips used in automobile connectors , adopting the technical solution of the present invention can make brass products meet the dual requirements of the automotive connector industry on tensile strength and elongation indicators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of double-strength copper tape production process that is used for automobile connector of the present embodiment, its steps are as follows:

[0028] (1) Melting ingot; (2) Hot rolling; (3) Face milling; (4) Rough rolling, wherein the specified thickness of the coil after rough rolling is 2.5mm; (5) Primary annealing; (6) Primary cleaning (7) Medium rolling; (8) Second annealing and cleaning; (9) Finish rolling; (10) Three times annealing and cleaning; (11) Finish rolling; (12) Four cleanings; (13) Leveling; ( 14) Inspection delivery.

[0029] Step (1): After weighing the electrolytic copper plate and zinc ingot according to the composition standard of H65 brass, according to the melting points of the two materials, first add electrolytic copper into the copper water furnace for heating and melting, and then put the zinc ingot After adding and melting, after stirring and checking the slag composition, when the temperature of the molten copper water is adjusted t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a double strong copper strip production technology for an automobile connector, and belongs to the technical field of a copper strip production technology. The double strong copper strip production technology comprises the following steps of (1), smelting and ingot casting; (2), hot rolling; (3), milling; (4), rough rolling; (5), once annealing; (6), once cleaning; (7), medium rolling; (8),twice annealing and cleaning; (9), finish rolling; (10), three times annealing and cleaning; (11), finish rolling; (12), four times cleaning; (13), leveling; and (14), examining and delivering; and specified thickness of strip coil after rough rolling is 2.5 mm. According to the technical scheme, brass products can meet the double requirements of tensile strength and elongation index of automobile connector industry.

Description

technical field [0001] The invention relates to the technical field of copper strip production technology, in particular to a double-strength copper strip production technique for automotive connectors. Background technique [0002] The automotive wire harness connector products in automotive connectors have a complex shape in the stamping and forming part of the product, which requires extremely high plasticity of the copper strip material, and the male and female ends of the single-wire piece of the formed connector are engaged and separated (i.e. Insertion force) must meet the requirements of the domestic automotive industry standard "QC / T417-2011", and put forward higher requirements for the strength of copper strip materials. Therefore, for this type of product, the automotive connector industry has proposed "double strength The so-called "double-strength copper strip" is to ensure that the tensile strength of the copper strip material reaches the level of 500MPa, and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P15/00
CPCB23P15/00
Inventor 孙邈刘建新文志凌孙红刚胡兵
Owner ANHUI CHUJIANG TECHCAL NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com