High-chromium cast steel roller for rolling of hot rolled plate strip

A technology for high-chromium cast steel and hot-rolled sheet, applied in the direction of roll, metal rolling, metal rolling, etc., can solve the problems of long production cycle and complex production process, shorten the production cycle, improve mechanical strength and wear resistance. the effect of shortening the production cycle

Active Publication Date: 2018-05-22
SINOSTEEL XINGTAI MACHINERY & MILL ROLL
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the carbon content of high-chromium cast steel rolls is generally low and is affected by the alloy ratio, high-temperature quenching treatment is generally required to meet the requirements of the microstructure, which has the problems of complex production process and long production cycle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] In this example, the roll specification is ￠1200 / 1100×1550, the thickness of the working layer is 50mm, the hardness requirement is HSD72~78, and the composition design target of the working layer of the roll body is C1.60~1.80%, Si0.60~1.00%, Mn0.80~1.00%, Cr12.00~13.00%, Ni1.00~1.50%, Mo1.00~2.00%, V≥0.10%, S≤0.03%, P≤0.05%, the rest is Fe and unavoidable impurities . The manufacturing method is as follows:

[0035] A. Smelting: Ingredients are prepared according to the chemical composition of the working layer of the roll, and smelted in an induction furnace to obtain molten steel for the working layer of the roll. The smelting temperature is 1450°C; the core of the roll is made of pig iron and smelted in an induction furnace to obtain the core Molten steel, the smelting temperature is 1450℃;

[0036] B. Centrifugal casting: use a centrifuge to cast the working layer of the roller body, and the pouring temperature is 1350°C;

[0037] C. Pouring the core and roll n...

Embodiment 2

[0043]In this example, the roll specification is ￠1200 / 1100×1450, the thickness of the working layer is 50 mm, the hardness requirement is HSD80~85, and the composition design target of the working layer of the roll body is C1.80~2.00%, Si0.60~1.00%, Mn1.00~1.50%, Cr13.00~15.00%, Ni1.50~2.00%, Mo2.00~2.50%, V≥0.10%, S≤0.03%, P≤0.05%, the rest is Fe and unavoidable impurities . The manufacturing method is as follows:

[0044] A. Smelting: Ingredients are prepared according to the chemical composition of the working layer of the roll, and smelted in an induction furnace to obtain molten steel for the working layer of the roll. The smelting temperature is 1550°C; the core of the roll is made of pig iron and smelted in an induction furnace to obtain the roll core Molten steel, the smelting temperature is 1500℃;

[0045] B. Centrifugal casting: use a centrifuge to pour the working layer of the roller body into shape, and the pouring temperature is 1400°C;

[0046] C. Pouring the...

Embodiment 3

[0052] In this example, the roll specification is ￠1200 / 1100×1700, the thickness of the working layer is 50mm, the hardness requirement is HSD70~75, and the composition design target of the working layer of the roll body is: C1.60~1.80%, Si0.60~1.00% , Mn0.80~1.10%, Cr12.00~14.00%, Ni1.00~1.50%, Mo1.00~2.00%, V≥0.10%, S≤0.03%, P≤0.05%, the rest is Fe and unavoidable Impurities. The manufacturing method is as follows:

[0053] A. Smelting: Ingredients are prepared according to the chemical composition of the working layer of the roll, and smelted in an induction furnace to obtain molten steel for the working layer of the roll. The smelting temperature is 1500°C; the core of the roll is made of pig iron and smelted in an induction furnace to obtain the core Molten steel, the smelting temperature is 1480°C;

[0054] B. Centrifugal casting: use a centrifuge to pour the working layer of the roll body into shape, and the pouring temperature of the molten steel is 1380°C;

[0055]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-chromium cast steel roller for rolling of a hot rolled plate strip. The high-chromium cast steel roller comprises a roller core and a roller body working layer. The roller body working layer comprises, by mass, 1.60-2.00% of C, 0.60-1.00% of Si, 0.80-1.50% of Mn, 12.00-15.00% of Cr, 1.00-2.00% of Ni, 1.00-2.50% of Mo, greater than or equal to 0.10% of V, less than orequal to 0.03% of S, less than or equal to 0.05% of P and the balance Fe and inevitable impurities. By improving the chemical components of the roller body working layer and adjusting the heat treatment process, the carbon content is increased, generation of pearlite in a cast structure is suppressed, thus, the mechanical strength and abrasion resistance of the roller are improved, high temperature quenching does not need to be conducted in the rolling process, equipment can be saved, the production period is shortened, the production cost is reduced, and the roller performance stability is improved.

Description

technical field [0001] The invention relates to a roll, especially a high-chromium cast steel roll, which is used for rolling hot-rolled strips. Background technique [0002] High chromium cast steel has high mechanical strength and wear resistance, and has gradually replaced semi-steel and high chromium cast iron rolls. Finishing work rolls, small section steel and bar mill finishing rolls, etc. Since the carbon content of high-chromium cast steel rolls is generally low and is affected by the alloy ratio, high-temperature quenching treatment is generally required to meet the requirements of the microstructure, which has the problems of complex production process and long production cycle. Contents of the invention [0003] The technical problem to be solved in the present invention is to provide a high-chromium cast steel roll for hot-rolled strip rolling, which can increase the carbon content and suppress the formation of pearlite in the as-cast structure, and improve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/46C22C38/56C22C38/04C22C38/02C22C33/04B22D13/02C21D9/38B21B27/00
CPCB21B27/00B22D13/02C21D9/38C22C33/04C22C38/02C22C38/04C22C38/44C22C38/46C22C38/56
Inventor 刘娣杨昱东韩建宁杜旭景刘路军肖泽杨朱志磊陈立峰
Owner SINOSTEEL XINGTAI MACHINERY & MILL ROLL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com