Anti-aging natural rubber synthesis method

A natural rubber, anti-aging technology, applied in the field of synthetic anti-aging natural rubber, to achieve good aging performance, shorten the vulcanization time, and reduce the viscosity

Inactive Publication Date: 2018-05-29
SHENYANG SAIYA RUBBER PRODS
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The structure of the silane coupling agent is used for the pure purpose of improving the rubber/filler interaction. If other functional groups can be grafted on one end of the coupling agent, it can improve the rei

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An aging-resistant natural rubber composite material, prepared from the following raw materials in parts by weight: 135 parts of natural rubber, 45 parts of white carbon black VN3, 35 parts of carbon black N330, 6 parts of zinc oxide, 4 parts of stearic acid, anti-aging 3 parts of coupling agent, 8 parts of accelerator M and 3 parts of vulcanizing agent sulfur.

[0024] Preparation method, the steps are as follows:

[0025] (1) Synthesis of anti-aging silane coupling agent

[0026] Gamma-glycidyl ether oxypropyltrimethoxysilane and p-aminodiphenylamine are added in the reactor, and the mol ratio of the gamma-glycidyl etheroxypropyltrimethoxysilane and the p-aminodiphenylamine is 1: 1-2, feed nitrogen gas 0.2-0.6MPa, heating temperature 120-150°C, stirring speed 100-120r / min, stirring time 1-1.5h to prepare anti-aging silane coupling agent;

[0027] (2) In-situ modified filler

[0028] Weigh carbon black, white carbon black and anti-aging silane coupling agent into th...

Embodiment 2

[0036] An aging-resistant natural rubber composite material, prepared from the following raw materials in parts by weight: 130 parts of natural rubber, 44 parts of white carbon black VN3, 38 parts of carbon black N330, 7 parts of zinc oxide, 4 parts of stearic acid, anti-aging 3 parts of coupling agent, 7 parts of accelerator D and 3 parts of vulcanizing agent sulfur.

[0037] Preparation method, the steps are as follows:

[0038] (1) Synthesis of anti-aging silane coupling agent

[0039] Gamma-glycidyl ether oxypropyltrimethoxysilane and p-aminodiphenylamine are added in the reactor, and the mol ratio of the gamma-glycidyl etheroxypropyltrimethoxysilane and the p-aminodiphenylamine is 1: 1-2, feed nitrogen gas 0.2-0.6MPa, heating temperature 120-150°C, stirring speed 100-120r / min, stirring time 1-1.5h to prepare anti-aging silane coupling agent;

[0040] (2) In-situ modified filler

[0041] Weigh carbon black, white carbon black and anti-aging silane coupling agent into th...

Embodiment 3

[0049] An aging-resistant natural rubber composite material, prepared from the following raw materials in parts by weight: 140 parts of natural rubber, 48 parts of white carbon black VN3, 39 parts of carbon black N330, 8 parts of zinc oxide, 4 parts of stearic acid, anti-aging 3 parts of coupling agent, 8 parts of accelerator M and 4 parts of vulcanizing agent sulfur.

[0050] Preparation method, the steps are as follows:

[0051] (1) Synthesis of anti-aging silane coupling agent

[0052] Gamma-glycidyl ether oxypropyltrimethoxysilane and p-aminodiphenylamine are added in the reactor, and the mol ratio of the gamma-glycidyl etheroxypropyltrimethoxysilane and the p-aminodiphenylamine is 1: 1-2, feed nitrogen gas 0.2-0.6MPa, heating temperature 120-150°C, stirring speed 100-120r / min, stirring time 1-1.5h to prepare anti-aging silane coupling agent;

[0053] (2) In-situ modified filler

[0054] Weigh carbon black, white carbon black and anti-aging silane coupling agent into th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of rubber materials, and relates to an anti-aging natural rubber synthesis method, which comprises: (1) synthesizing an anti-aging silane coupling agent: adding gamma-glycidyl ether propyltrimethoxysilane and p-aminodiphenylamine to a reaction kettle, introducing 0.2-0.6 MPa nitrogen, heating to a temperature of 120-150 DEG C, and stirring for 1-1.5 h at a stirring rotation speed of 100-120 r/min to obtain anti-aging silane coupling agent; and (2) preparing an in-situ modified filler: weighing carbon black, white carbon black and an anti-aging silane coupling agent, placing into the reaction kettle, introducing 0.1-0.2 MPa N2 gas, carrying out heating to a temperature of 50-60 DEG C, and stirring for 1-1.5 h at a stirring rotation speed of 100-120 r/min to prepare the in-situ modified filler. According to the present invention, with the preparation method, the anti-aging natural rubber is prepared by adding the anti-aging coupling agent modified filler, such that the aging resistance of the rubber is improved, and the operation is simple; and the prepared anti-aging rubber has advantages of high strength, strong aging resistance and thelike.

Description

technical field [0001] The invention belongs to the technical field of rubber materials and relates to a method for synthesizing aging-resistant natural rubber. Background technique [0002] Natural rubber (NR) is the most widely used general-purpose rubber, but the excessive double bonds in its molecular structure cause the products to age easily. The application of anti-aging agent greatly prolongs the service life of rubber, but general anti-aging agent is easy to volatilize and migrate, which not only makes the performance of the product worse, but also pollutes the environment and endangers human health. The silane coupling agents used in the rubber industry are almost all sulfur-containing silane coupling agents, especially polysulfide silane coupling agents. The traditional coupling agent Si69 requires high mixing temperature during use, which is easy to cause scorching of the rubber material, and has the disadvantage of high porosity of the rubber material. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08K13/06C08K9/06C08K3/04C08K3/36C08K3/22C08K5/09
CPCC08K13/06C08K3/04C08K3/22C08K3/36C08K5/09C08K9/06C08K2003/2296C08L2201/08C08L7/00
Inventor 刘梦菲
Owner SHENYANG SAIYA RUBBER PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap